Search

Non-sustainable single-use plastics used for food packaging needs to be phased out. Films made from cellulose nanofibrils (CNFs) are suitable candidates for biodegradable and recyclable packaging materials as they exhibit good mechanical properties, excellent oxygen barrier properties and high transparency. Yet, their poor water vapour barrier properties have been a major hindrance in their commercialisation. Here, we describe the preparation of 25 μm thick CNF films with significantly improved water vapour barrier properties after deposition of ultrathin polymeric and metallic coatings, parylene C and aluminium, respectively. When first adding a 40 nm aluminium layer followed by an 80 nm parylene layer, i.e. with a combined thickness of less than one percent of the CNF film, a water vapour transmission rate of 2.8 g m−2 d−1 was achieved at 38 °C and 90 % RH, surpassing a 25 μm polypropylene film (4–12 g m−2 d−1). This is an improvement of more than 700 times compared to uncoated CNF films, under some of the harshest possible conditions a packaging material will need to endure in commercial use. The layers showed a good and even coverage, as assessed by atomic force microscopy, and the parylene-coated surfaces were hydrophobic with a contact angle of 110°, providing good water repellency. [Display omitted] [ABSTRACT FROM AUTHOR]

EDC-mediated coupling has frequently been utilized to poly(ethylene glycol) functionalize (PEGylate) cellulose-based materials, but no work has previously been reported on the direct N -(3-dimethylaminopropyl)- N -ethylcarbodiimide (EDC)-mediated PEGylation of cellulose nanofibrils (CNF). Herein, we report the first study where CNF has been directly sterically stabilized with amine-terminated PEG employing N -hydroxysuccinimide (NHS)-assisted EDC-coupling. This work has shown that this coupling reaction is highly sensitive to the reaction conditions and purification procedures, and hence an optimized coupling protocol was developed in order to achieve a reaction yield. Elemental analysis of the nitrogen content also showed the successful PEGylation. It was also shown that a surprisingly low PEGylation (1%) is sufficient to significantly improve the colloidal stability of the PEGylated samples, which reached dispersion-arrested-state-transitions at higher concentrations than neat CNF. The colloidal stability was preserved with increasing ionic strength, when comparably long polymer chains were grafted, targeting only 1% PEGylation. [ABSTRACT FROM AUTHOR]

Nanoscale infrared (IR) spectroscopy and microscopy, enabling the acquisition of IR spectra and images with a lateral resolution of 20 nm, is employed to chemically characterize individual cellulose nanocrystals (CNCs) and cellulose nanofibrils (CNFs) to elucidate if the CNCs and CNFs consist of alternating crystalline and amorphous domains along the CNF/CNC. The high lateral resolution enables studies of the nanoscale morphology at different domains of the CNFs/CNCs: flat segments, kinks, twisted areas, and end points. The types of nanocellulose investigated are CNFs from tunicate, CNCs from cotton, and anionic and cationic wood-derived CNFs. All nano-FTIR spectra acquired from the different samples and different domains of the individual nanocellulose particles resemble a spectrum of crystalline cellulose, suggesting that the non-crystalline cellulose signal observed in macroscopic measurements of nanocellulose most likely originate from cellulose chains present at the surface of the nanocellulose particles. [Display omitted] [ABSTRACT FROM AUTHOR]

The structure and dynamics of networks formed by rod-shaped particles can be indirectly investigated by measuring the diffusion of spherical tracer particles. This method was used to characterize cellulose nanofibril (CNF) networks in both dispersed and arrested states, the results of which were compared with coarse-grained Brownian dynamics simulations. At a CNF concentration of 0.2 wt% a transition was observed where, below this concentration tracer diffusion is governed by the increasing macroscopic viscosity of the dispersion. Above 0.2 wt%, the diffusion of small particles (20–40 nm) remains viscosity controlled, while particles (100–500 nm) become trapped in the CNF network. Sedimentation of silica microparticles (1–5 μm) in CNF dispersions was also determined, showing that sedimentation of larger particles is significantly affected by the presence of CNF. At concentrations of 0.2 wt%, the sedimentation velocity of 5 μm particles was reduced by 99 % compared to pure water. [Display omitted] [ABSTRACT FROM AUTHOR]