1. Composition, microstructure and mechanical properties of cBN-based composites sintered with AlN- Al- Ni binder.
- Author
-
Li, Liqiang, Zhao, Yabo, Sun, Kun, Ji, Huanli, Feng, Dandan, and Li, Zhihong
- Subjects
- *
ALUMINUM nitride , *METAL microstructure , *MECHANICAL properties of metals , *BORON nitride , *COMPOSITE materials , *SINTERING , *BINDING agents - Abstract
Cubic boron nitride (cBN)-based composites were fabricated using AlN-Al-Ni binders at high pressure and high temperature (HPHT). Effects of binder content and temperature on phase composition, microstructure and mechanical properties of cBN-based composites were investigated. Abrasive ratio was measured using a new method. Almost all Al reacted with cBN during sintering, resulting in AlN as well as AlB 2 phases, while remaining Al and Ni formed intermetallic compounds. At 1500 °C, the reaction reached its maximum. Excellent relative density, flexural strength and fracture toughness of composites, sintered with 17 wt% binder, were 99.6%, 661 MPa and 7.19 MPa m 1/2 , respectively. However, the optimum value of hardness and abrasive ratio of composites at binder content of 13 wt% were 47.92 GPa and 2.99, respectively. [ABSTRACT FROM AUTHOR]
- Published
- 2018
- Full Text
- View/download PDF