Search

Abstract: Delamination-free ultrafiltration (UF) dual layer hollow fibers have been successfully fabricated by dry jet-wet spinning technique. Two different polymers of poly(amide-imide) (PAI) and polyethersulfone (PES) were utilized as the selective layer on the outer side and the porous support layer on the inner side, respectively. The dual layer substrates were subsequently modified to develop a nanofiltration (NF)-like skin on the outer layer by polyethyleneimine (PEI) cross-linking followed by multilayer polyelectrolyte depositions. These membranes were characterized by a series of standard protocols in terms of membrane structure, permeability and salt rejection, and were applied in FO process. Experiments reveal that the dual-layer NF hollow fiber modified by polyelectrolyte cross-linking and depositions can achieve pure water permeability of 4.1l/m2.h.bar and a high rejection to MgCl2 up to 97%. In FO process, the dual-layer hollow fibers exhibited a water flux of 39 and 21lm−2 h−1 in the orientations of active layer facing draw solution and feed water, respectively, by using 0.5M MgCl2 as draw solution and de-ionized (DI) water as feed at room temperature. It suggests that the combined treatment of polyelectrolyte cross-linking and deposition is an effective way to form a NF-like selective layer for FO dual-layer hollow fiber membranes. [Copyright &y& Elsevier]

Abstract: There has been a resurgence of interest in forward osmosis (FO) as a potential means of desalination, dewatering and in pressure retarded osmosis, which Sidney Loeb was advocating over 3decades ago. This paper describes the characteristics and potential applications of a newly developed FO hollow fiber membrane, which was fabricated by interfacial polymerization on the inner surface of a polyethersulfone (PES) hollow fiber. This FO membrane presents excellent intrinsic separation properties, with a water flux of 42.6L/m2 h using 0.5M NaCl as the draw solution and DI water as the feed with the active layer facing the draw solution orientation at 23°C. The corresponding ratio of salt flux to water flux was only 0.094g/L, which is superior to all other FO membranes reported in the open literature. To evaluate different application scenarios, various NaCl solutions (500ppm (8.6mM), 1wt.% (0.17M) and 3.5wt.% (0.59M)) were used as the feed water to test the performance of the FO membrane. The membrane can achieve a water flux of 12.4L/m2 h with 3.5wt.% NaCl solution as the feed and 2M NaCl as the draw solution, suggesting it has good potential for seawater desalination. [ABSTRACT FROM AUTHOR]

The emerging technology of pressure retarded osmosis (PRO) has been intensely studied over the past decades due to its potential in harvesting salinity gradient energy, but membrane fouling can deteriorate the PRO performance. To mitigate membrane fouling, the outer surface of the inner-selective thin-film composite (TFC) polyetherimide (PEI) hollow fiber membrane was modified by depositing poly-(allylamine hydrochloride) (PAH) and poly acrylic acid (PAA) polyelectrolytes. The results show that the outer surface of the modified membrane had less pores exposed and was more negatively charged, which was beneficial for preventing the entrance and adsorption of the negatively charged foulants into the membrane substrate. It was further proved that the modified membrane was effective in reducing PRO fouling by organic macromolecules such as alginate and bovine serum albumin, while maintaining the mechanical properties and intrinsic separation properties well. Interestingly, after 200 ppm alginate was introduced to the feed water, the power density of the modified membrane could be maintained constant at 16.2 W·m − 2 at 15 bar while that of the non-modified membrane reduced around 17% at the end of a 300-min testing period. The results suggest that the polyelectrolytes deposition is a feasible strategy for adding anti-fouling property to PRO membranes. [ABSTRACT FROM AUTHOR]

This study investigated the fouling behavior and chemical cleaning of forward osmosis (FO) membranes for treating produced/process water (PPW) from a real gas field using thin-film composite FO hollow fiber membranes. Experiments revealed that membrane fouling occurred during the PPW treatment, which hindered the water and solute transport through the membrane. The water permeability and FO reference water flux of the membrane decreased by 22.9% and 24.8%, respectively, after fouling. Membrane surface characterization was carried out, and the results indicated the deposition and entrapment of organic species on the membrane after the PPW treatment. The efficiencies of various cleaning agents, including sodium dodecyl sulfate (SDS), ethylenediaminetetraacetic (EDTA) and NaOH, were evaluated. It was found that cleaning with SDS for 15 min is the most effective method for restoring water flux, and very stable FO performance can be obtained during batch treatment of PPW. The FO membrane can reduce the PPW volume by 50% at a relatively high average water flux of 15.6 L·m − 2 ·h − 1 in the active layer facing feed solution orientation using 1 M NaCl as draw solution (equivalent to the draw solution available in the field). This study demonstrates the great potential of FO technology for produced/process water treatment. [ABSTRACT FROM AUTHOR]

Thin-film composite (TFC) membranes are generally preferred over integrally skinned asymmetric (ISA) membranes in pressure retarded osmosis (PRO) process due to their much higher water permeability, but they cannot operate in the active layer facing feed solution (AL-FS) orientation because of potential delamination of the rejection layer under the high applied pressure. However, operating under AL-FS orientation is preferred as a strategy for better fouling control. Hence, in this study, three ISA hollow fiber membranes were fabricated using a dry-jet wet-spinning method, followed by chemical cross-linking to obtain membranes for PRO application. The best-performing membrane was subjected to fouling test in two orientations. Our results demonstrate that the AL-FS orientation is better for a sustainable long-term PRO operation, given the stable performance throughout the two-day testing. Also, the current use of power density per membrane area as a performance benchmark may not be practical for large-scale PRO operation, and the volumetric power density per module is more relevant. In terms of volumetric power density for a hypothetical 5-in. module, our best-performing membrane is predicted to generate a 3.6 to 10 times better power density than commercial modules, rendering our ISA hollow fiber membranes promising for scaling-up to bigger modules. [Display omitted] • Operating under AL-FS orientation is preferred as a strategy for better fouling control. • Integrally skinned asymmetric hollow fiber membranes were developed for AL-FS orientation in PRO. • The membranes achieved sustainable power production when wastewater was employed. • The volumetric power density was predicted to yield promising solution for practical application. [ABSTRACT FROM AUTHOR]

Thin-film composite (TFC) membranes are generally preferred over integrally skinned asymmetric (ISA) membranes in pressure retarded osmosis (PRO) process due to their much higher water permeability, but they cannot operate in the active layer facing feed solution (AL-FS) orientation because of potential delamination of the rejection layer under the high applied pressure. However, operating under AL-FS orientation is preferred as a strategy for better fouling control. Hence, in this study, three ISA hollow fiber membranes were fabricated using a dry-jet wet-spinning method, followed by chemical cross-linking to obtain membranes for PRO application. The best-performing membrane was subjected to fouling test in two orientations. Our results demonstrate that the AL-FS orientation is better for a sustainable long-term PRO operation, given the stable performance throughout the two-day testing. Also, the current use of power density per membrane area as a performance benchmark may not be practical for large-scale PRO operation, and the volumetric power density per module is more relevant. In terms of volumetric power density for a hypothetical 5-in. module, our best-performing membrane is predicted to generate a 3.6 to 10 times better power density than commercial modules, rendering our ISA hollow fiber membranes promising for scaling-up to bigger modules. [Display omitted] • Operating under AL-FS orientation is preferred as a strategy for better fouling control. • Integrally skinned asymmetric hollow fiber membranes were developed for AL-FS orientation in PRO. • The membranes achieved sustainable power production when wastewater was employed. • The volumetric power density was predicted to yield promising solution for practical application. [ABSTRACT FROM AUTHOR]