Search

Deposition of a consistent diamond coating on intricate surfaces has historically posed a difficulty. This article presents the advancement in research on depositing a uniform diamond coating on three-dimensional (3D) silicon spheres, utilizing a faraday cage within a microwave plasma chemical vapor deposition (MPCVD) reactor. A self-consistent three-dimensional multi-physics field model has been established for simulating the microwave electric field and plasma inside a reactor with or without a faraday cage. Results indicate the cage effectively reduces the discharge at the top of the silicon sphere and improves uniformity of the distribution of the microwave electric field and plasma electron density on the sphere's surface. MPCVD trials have demonstrated that a powerful discharge takes place at the apex of the silicon sphere resulting in an excessive thermal gradient if the cage is not added. The apex of the silicon sphere is covered with a blend of diamond and graphite phases. Due to the excessive internal stress of the coating, approximately 50 % of the samples experience coating detachment. After the addition of the cage, the strong discharge is transferred to the top of the cage, effectively suppressing the microwave electric field and plasma inside the cage. Improved quality, reduced internal stress, and enhanced uniformity of the polycrystalline diamond coating are achievable on the silicon spheres within the cage. Moreover, this technique offers a novel approach to coat diamond on complex 3D geometries. [Display omitted] • Three-dimensional multi-physics modeling verifies that faraday cage suppresses microwave electric field and plasma. • The Faraday cage improves the uniformity of the distribution of microwave electric fields and plasma in the internal space. • Uniform, high crystal quality, low stress diamond coating. [ABSTRACT FROM AUTHOR]

Diamond is a highly attractive material for many applications in material science, engineering, chemistry, and biology because of its favorable properties. The preparation of large-area freestanding diamond plate can greatly reduce the production cost of diamond and promote the industrialization of diamond. In this study, the dual-magnetic field mode was introduced to optimize the magnetic field distribution in direct current arc plasma jet chemical vapor deposition (DC Jet CVD) system, and the arc plasma was effectively controlled under the coupling of electric field and magnetic field. The uniformity of the plasma distribution above the substrate surface is significantly improved, resulting in long-term stable and uniform growth of the 8-inch freestanding diamond plate. The influence of dual-magnetic field mode on magnetic field generation, arc feature, and reactive group distribution was studied. 8-inch freestanding diamond plates with an average thickness of 2.8 mm were prepared by dual-magnetic controlled DC Jet CVD. The results showed that the 8-inch diamond plate preferred a high (220) orientation, and the deviation of thickness of which was around 10 % of the averaged values. Raman spectroscopy of diamond revealed a 6.6 cm−1 of full width at half maximum (FWHM) and calculated 1.20 GPa compressive stress in the 8-inch diamond plate. By means of mechanical and thermal property measurements, the large area diamond plate shows a robust structure with the average values of three-point bending fracture strength of 987.2 MPa, and extremely high thermal conductivity of 1797.8 W/(m·k) as well. The deviation of three-point bending fracture strength and the thermal conductivity over the 8-inch diamond plate was around 7.9 % and 12.6 % of the respective averaged values. [Display omitted] • A uniform and robust 8-inch diamond plate was prepared using a dual-field DC arc CVD system. • The average three-point bending fracture strength of the 8-inch diamond plate was 987.23 MPa, and the average thermal conductivity was 1797.80 W/(m•K). • The effect of dual magnetic field mode on the distribution of arc morphology and arc plasma groups was analyzed using a high-speed camera and filter. [ABSTRACT FROM AUTHOR]