Abstract: The plasma treatment of rapid heating was introduced for increasing fracture strength of free-standing diamond films. The effects of plasma high temperature annealing treatment on surface morphology, internal stress, vacancy defects, impurities and fracture strength of free-standing diamond films were investigated by scanning electron microscopy (SEM), Raman, positron annihilation technique (PAT) and mechanical property testing. It showed that the fracture strength of the diamond films increases up to 70% for lower fracture diamond films with treating temperature (1500–1600°C). The graphitization in surface and interior of diamond films would be produced by high temperature treatment more than 1700°C. Fracture strengths of diamond films could be enhanced after high temperature treatment and the main factor of that was compressive stress state in diamond films induced by graphitization. The impurity of N was segregated and integrated with vacancy cluster to become [N–V]0 and [N–V]−. [Copyright &y& Elsevier]

Abstract: Highly c-axis oriented ZnO film is often deposited on diamond substrates by RF magnetron sputtering and widely used for high frequency surface acoustic wave (SAW) devices. Deposition temperature is a key factor affecting the quality of the ZnO film. Different quality polished free-standing diamond films prepared by DC Arc Plasma Jet were used as the substrates to deposit ZnO films at different temperatures. Effect of the deposition temperature and the quality of the diamond films on the properties of the ZnO films were investigated by means of scanning electron microscopy (SEM) and X-ray diffraction (XRD). The results show that highly c-axis oriented ZnO films can be much easier deposited on the optical-grade diamond films with <111> preferred orientation than the tool-grade diamond films with <220> preferred orientation. The optimal deposition temperature is 200°C for highly c-axis oriented and lower roughness ZnO films. Acoustic phase velocity of more than 10,000m/s for the SAW devices based on the ZnO/optical-grade free-standing diamond films was obtained. [Copyright &y& Elsevier]

Abstract: A destroyable Ti interlayer on graphite substrate was used for fabrication of crack-free free-standing diamond films by high-power DC Arc Plasma Jet. Ti interlayer was arc ion plated on the polycrystalline graphite substrate. The thickness, morphology and composite phase of the Ti interlayer were examined by scanning electron microscopy (SEM) and X-ray diffraction (XRD). Titanium carbide (TiC) was detected in both sides of the interlayer, which played an important role with respect to reasonable adhesion and diamond nucleation. Semi-translucent and crack-free diamond films were obtained and characterized by SEM and Raman spectroscopy. It is shown that the diamond films so obtained have excellent Raman signature. The overall results suggest that plating Ti interlayer on graphite substrate is an effective way to obtain potentially crack-free free-standing diamond films. [Copyright &y& Elsevier]

A piece of diamond film (Ø 125 mm) was polished based on prefabricated stress. The diamond film was glued to a metal workpiece at high temperatures. The difference in the thermal expansion coefficients between the diamond film and the workpiece was exploited to prefabricate stress in the middle of the two materials. This prefabricated stress had a compressive effect on the diamond film, offset the stress generated in the grinding and polishing process, and prevented the diamond film from cracking. The feasibility of the prestressing method was verified by a combination of experiments and finite element simulations. The prestressing method was used to bond the diamond film to a 10 mm-thick brass fixture at 20, 50, 70, and 90 °C. It was found that when the temperature of the bonded diamond film reached 90 °C, the increase in the prefabricated stress was −410.71 MPa. The finite element simulation results were found to be consistent with the experimental data. The diamond film was cooled down to room temperature after bonding at high temperatures to simulate the prefabricated stress generation process. The diamond film with the prefabricated stress was again heated to the bonding temperature to simulate the stress change caused by the frictional heat generated during the polishing process. The stress of the bonded sample increased when it was cooled down to room temperature. The stress on the diamond surface became smaller during the polishing process, and the stress almost disappeared with the rise in bonding temperature, verifying the viability of the prestressing method. [Display omitted] • Prestressing method to polish a large-sized diamond film was proposed. • Diamond film was bonded to the metal fixture at high temperature and cooled. • The prefabricate stress was measured and simulated. • A Ø125 mm diamond film was successfully polished using this idea. [ABSTRACT FROM AUTHOR]

Deposition of a consistent diamond coating on intricate surfaces has historically posed a difficulty. This article presents the advancement in research on depositing a uniform diamond coating on three-dimensional (3D) silicon spheres, utilizing a faraday cage within a microwave plasma chemical vapor deposition (MPCVD) reactor. A self-consistent three-dimensional multi-physics field model has been established for simulating the microwave electric field and plasma inside a reactor with or without a faraday cage. Results indicate the cage effectively reduces the discharge at the top of the silicon sphere and improves uniformity of the distribution of the microwave electric field and plasma electron density on the sphere's surface. MPCVD trials have demonstrated that a powerful discharge takes place at the apex of the silicon sphere resulting in an excessive thermal gradient if the cage is not added. The apex of the silicon sphere is covered with a blend of diamond and graphite phases. Due to the excessive internal stress of the coating, approximately 50 % of the samples experience coating detachment. After the addition of the cage, the strong discharge is transferred to the top of the cage, effectively suppressing the microwave electric field and plasma inside the cage. Improved quality, reduced internal stress, and enhanced uniformity of the polycrystalline diamond coating are achievable on the silicon spheres within the cage. Moreover, this technique offers a novel approach to coat diamond on complex 3D geometries. [Display omitted] • Three-dimensional multi-physics modeling verifies that faraday cage suppresses microwave electric field and plasma. • The Faraday cage improves the uniformity of the distribution of microwave electric fields and plasma in the internal space. • Uniform, high crystal quality, low stress diamond coating. [ABSTRACT FROM AUTHOR]

The direct-current arc plasma jet method is advantageous for the rapid deposition of large-area self-supporting diamond films. However, dark defects tend to be generated during the growth process, significantly affecting the performance of the diamond. In this study, we use the direct-current arc plasma jet method to prepare transparent and translucent samples. Subsequently, we compare their optical, thermal, and mechanical properties and analyze the differences in their performances via microstructure and defect analyses. The results indicate that the transparent diamond samples exhibit excellent optical and thermal properties, with a transmittance of 68.4 % at a wavelength of 10.6 μm and a thermal conductivity similar to that of type-IIa single crystal diamond (i.e. 2002 W/(m·K)). Meanwhile, the translucent diamond exhibits outstanding mechanical properties, with a fracture strength of 984 MPa. Characterization results based on electron backscatter diffraction and X-ray computed tomography suggest that a preferred orientation along the (220) planes is conducive to the densification growth of the samples, thereby enhancing their optical and thermal properties. However, the generation of numerous twins results in interlocking between grains, which improves sample's mechanical properties but introduces porosity and impurities, thus deteriorating its optical and thermal performance. [Display omitted] • Optical and thermal diamond films were deposited by DC-arc plasma jet CVD with growth rates >6 μm/h. • Strong (220) texture and numerous twins can improve optical transmittance and fracture strength, respectively. • X-ray CT was used to reveal defects distribution and content within diamond samples. [ABSTRACT FROM AUTHOR]

Diamond is a highly attractive material for many applications in material science, engineering, chemistry, and biology because of its favorable properties. The preparation of large-area freestanding diamond plate can greatly reduce the production cost of diamond and promote the industrialization of diamond. In this study, the dual-magnetic field mode was introduced to optimize the magnetic field distribution in direct current arc plasma jet chemical vapor deposition (DC Jet CVD) system, and the arc plasma was effectively controlled under the coupling of electric field and magnetic field. The uniformity of the plasma distribution above the substrate surface is significantly improved, resulting in long-term stable and uniform growth of the 8-inch freestanding diamond plate. The influence of dual-magnetic field mode on magnetic field generation, arc feature, and reactive group distribution was studied. 8-inch freestanding diamond plates with an average thickness of 2.8 mm were prepared by dual-magnetic controlled DC Jet CVD. The results showed that the 8-inch diamond plate preferred a high (220) orientation, and the deviation of thickness of which was around 10 % of the averaged values. Raman spectroscopy of diamond revealed a 6.6 cm−1 of full width at half maximum (FWHM) and calculated 1.20 GPa compressive stress in the 8-inch diamond plate. By means of mechanical and thermal property measurements, the large area diamond plate shows a robust structure with the average values of three-point bending fracture strength of 987.2 MPa, and extremely high thermal conductivity of 1797.8 W/(m·k) as well. The deviation of three-point bending fracture strength and the thermal conductivity over the 8-inch diamond plate was around 7.9 % and 12.6 % of the respective averaged values. [Display omitted] • A uniform and robust 8-inch diamond plate was prepared using a dual-field DC arc CVD system. • The average three-point bending fracture strength of the 8-inch diamond plate was 987.23 MPa, and the average thermal conductivity was 1797.80 W/(m•K). • The effect of dual magnetic field mode on the distribution of arc morphology and arc plasma groups was analyzed using a high-speed camera and filter. [ABSTRACT FROM AUTHOR]

Slightly graphitization might be incurred on CVD diamond films when suffering instantaneous high temperature thermal shock. In this paper, phase transitions of CVD free-standing diamond films have been studied experimentally at the temperature range of 1500–1800 °C through a plasma rapid heating process. Raman spectra and X-ray photoelectron spectra (XPS) are compared and discussed for the purpose of measuring the percentage of graphitic carbon component in CVD diamond films after heat treatment at different temperatures. An obvious optical degradation took place in both visible and infrared bands with the increased treating temperature. The result indicates that graphitization is dominated along grain boundaries rather than in internal grains. In addition, the nitrogen related absorption peaks were not covered by the enhanced optical absorption background, which was caused by the opaque graphitic carbon formed at high temperature. Nitrogen concentrations have also been evaluated for these graphitized diamond films and there is no evidence to show the movement or aggregation of nitrogen atoms. [ABSTRACT FROM AUTHOR]

The growth process of carbon film on the surface of hydrocooling copper substrate in high-density direct current (DC) arc plasma was studied. Scanning electron microscopy, Fourier transform infrared spectroscopy, X-ray diffraction, nuclear magnetic resonance spectroscopy, and UV confocal Raman spectroscopy were used to analyze the structural constituents of the intermediate products generated at different growth periods. Results show that despite the remarkable heating effect of DC arc plasma to the copper substrate, one layer of cauliflower saturated carbon and double carbon bond as main component loose matter are first formed because of water-cooled copper substrate. With the increase in thickness of carbon film, the surface temperature gradually increases, the etching ability of the atomic hydrogen is enhanced and high concentration reactive units are maintained on the surface of carbon film. The cauliflower structure may effectively reduce the diamond nucleation barrier and promote the generation of nano-diamond. The diamond grains gradually grow up to the micron scale by the continuing influence of carbon-based active group and plasma. The growth pattern of carbon film on the hydrocooling copper substrate in high-density DC arc plasma may provide a new way to prepare large crack-free diamond films. [ABSTRACT FROM AUTHOR]

The addition of titanium (Ti) interlayer was verified to reduce the residual stress of diamond films. The evolution of interfacial stress during the cooling process is critical for the fabrication of large-area crack-free diamond films, so it is very worthy of further study. Variable-temperature X-ray diffraction (XRD) tests and finite element simulation were performed to evaluate the stress evolution of a diamond film. The film (with diameter of 150 mm) was prepared on a graphite substrate with Ti interlayer using DC arc plasma jet. Residual compressive stress in the diamond film is gradually increased during the cooling process. Moreover, the value and growth rate of the residual stress from the XRD tests are significantly lower than the finite element simulation results. All XRD peaks of diamond, graphite, and titanium carbide (TiC) generated on both sides of the Ti interlayer shift to a larger angle. By contrast, several XRD peaks of Ti deviate to a low angle. Elastic deformation of the Ti layer may offset the lattice contraction caused by the cooling effect. Elasticity modulus of TiC is significantly greater than that of Ti, which is more inclined to release the stress of the diamond film by self-fracturing. After the variable-temperature tests, residual compressive stress of the diamond film at room temperature is 1.1 GPa, whereas that before the tests is 1.4 GPa. These values are significantly lower than the finite element simulation results (3.05 GPa). [ABSTRACT FROM AUTHOR]

The CVD diamond films at different growth stages were prepared on the same substrate by DC arc plasma jet CVD. The surface morphologies and residual stress of diamond films were characterized by scanning electron microscope and Raman spectroscopy. The intrinsic stress of diamond films were obtained by subtracting thermal stress from residual stress. The results showed that the intrinsic compress stress was 0.42 GPa for the precoalescence stage due to the sp 2 carbon inclusions in diamond islands. With the diamond islands growing up and even snapping together to form grain boundary at the coalescence stage the intrinsic compress stress was 0.06 GPa. Eventually, the diamond islands coalesced into a continuous polycrystalline film, the intrinsic compress stress vanished and converted to tensile stress, the intrinsic tensile stress reached 1.41 GPa due to the number of grain boundaries increasing. The evolution of intrinsic stress during diamond film initial growth was mainly attributed to the surface free energy of diamond islands changed to the free energy of grain boundaries which was consistent with the Nix-Clemens model. [ABSTRACT FROM AUTHOR]

Polycrystalline CVD free-standing diamond films have been heat treated through a rapid heating process using a direct current (DC) arc plasma jet system within the temperature range of 1500–2000 °C. The optical transmission of the diamond film decreases when the treatment temperature exceeds 1500 °C. When the diamond film was annealed to 1800 °C for just 1 min, the infrared (IR) transmittance at λ = 10.6 μm of the film was significantly decreased from 60.5% to 4.0%, due to the transformation from diamond to graphite. Further increase of the temperature to 2000 °C leads to complete loss of optical transmittance in only 30 s, due to the detrimental occurrence of graphitization. XRD patterns indicate that graphite ultimately grows preferentially along the (0002) plane by forming disordered or turbostratic graphite as intermediate product. Raman spectra and SEM images verify that at 1500–1850 °C graphitic carbon transforms from the diamond surface in the form of protruding submicron crystallites, which were still containing a number of sp 3 C C bonds. In addition to graphitization on the external surface, the diamond-graphite phase transition also occurs along the grain boundaries and the calculated activation energy of the grain boundary graphitization process is 276 kJ·mol − 1 for the CVD diamond. [ABSTRACT FROM AUTHOR]

Diamond radiation detector is an ideal choice for the next-generation radiation detection in harsh environments, due to its small size, high irradiation resistance and fast response. However, high-purity single crystal diamond is hard to be prepared at the high growth rate due to the inevitable impurity incorporation. In this paper, based on the high-quality high-temperature/high-pressure (HPHT) single crystal diamond substrate, detector-grade single crystal diamonds material with high purity and low defect density were epitaxially grown at growth rate of about 4 μm/h by using plasma environment purification technology. It showed that the full width at half maximum of X-ray rocking curve of high-quality single crystal diamond could reach 0.007°, there was no nitrogen related impurity in PL spectrum, and the substitutional nitrogen content estimated by UV absorption spectrum was less than 10 ppb. After metallization and packaging process, the diamond detectors were prepared and the detector response under irradiation with 241Am α-particles was realized. For the sample with fewer dislocations, the charge collection efficiency and energy resolution of this detector were 86.8 % and 7.85 % for electrons, and 96.7 % and 2.48 % for holes. The product of mobility and lifetime of electrons and holes were 1.7 × 10−4 cm2V−1 and 3.7 × 10−4 cm2V−1, respectively. The high performances of the detector indicate that the current diamond detector can meet the application requirements of commercial diamond detectors. [Display omitted] • Detector-grade diamond was prepared by plasma environment purification technology. • The high-purity single crystal diamond was grown at growth rate of about 4 μm/h. • The diamond detector with charge collection efficiency of 96.7 % was realized. • The products of mobility and lifetime of electrons and holes were 1.7 × 10−4 and 3.7 × 10−4 cm2V−1. [ABSTRACT FROM AUTHOR]

Lift-off is a promising method to prepare thin, high-finish, and freestanding large-area single crystal and polycrystalline diamonds. However, accurate control of the damage layer characteristic to achieve both stress release and lift-off process is difficult. In this work, high-energy C+ was implanted in single crystal diamond and polycrystalline diamond to create subsurface damage. The defect behavior and structural transformation of the ion implantation and annealing process were investigated. The homoepitaxial growth was subsequently carried out and the epitaxial layer was lifted off from the substrate by selectively etching the damaged layer. The results show that the cap layer and the substrate (below the damage layer) keep the sp3 carbon structure before and after annealing, which is confirmed by the atomic-scale electron energy loss spectroscopy (EELS). The high-resolution transmission electron microscopy (HRTEM) images show that after annealing at 1000 °C for 1 h, the damaged layer was transformed from amorphous carbon to a mixture of graphite and amorphous carbon, providing the damaged layer that could be removed by electrochemical solution. Meanwhile, the distorted diamond area was changed to a sharp interface, which ensures the low roughness of the substrate surface after the lift-off process. After etching for 30 h, a freestanding polycrystalline diamond film with a thickness of 100 μm and a surface roughness of 1.68 nm was obtained. The roughness of the lift-off substrate surface is 1.10 nm, indicating the epitaxial growth can be repeated directly without polishing. [Display omitted] • The defect behavior and structural transformation of the high-energy C+ implanted diamonds were investigated. • The stress state of the diamonds before and after ion implantation and after lift-off process were evaluated. • A 100 μm-thick freestanding polycrystalline diamond film with a surface roughness of 1.68 nm was successful obtained. [ABSTRACT FROM AUTHOR]

Diamond has attracted increasing attention because it has high thermal conductive. Here, a freestanding diamond thermal conductive film with a diameter of about 7 in. and an average thickness of 1.54 mm was prepared by DC arc plasma jet CVD with multi-stage magnetic fields. Specifically, the thickness uniformity was ensured by adding the magnetic field during the deposition of the freestanding diamond film. The morphology, structure and thermal conductivity of the diamond film were studied. The results showed that the expansion area of the DC arc plasma approached the surface of the substrate increasing duo to add the bottom magnetic field. Structural characterization revealed that the grain of the diamond film in the arc main were coarse, affected by the shape of DC arc plasma, while in the arc center and edge were fine. The main orientation of polycrystalline structure of the diamond film was the crystalline plane of (220). The Raman peaks of diamond film in different areas moved to a higher wavelength, indicating the existence of compressive stress inside the diamond film. The coarse columnar grain and a few grain boundaries were in the arc main. Therefore, the average value of the thermal conductivity (k ⊥) of diamond film measured in the arc main was 1728.9 ± 4.9 W/(m·k). Meanwhile, the thermal conductivity of the arc center and edge area was lower than that of the arc main. [Display omitted] • A freestanding diamond thermal conductive film with a diameter of about 7 in. was prepared. • DC arc plasma jet CVD with multi-stage magnetic fields was adopted. • The average value of the thermal conductivity (k ⊥) of diamond film measured in the arc main was 1728.9 ± 4.9 W/(m·k). [ABSTRACT FROM AUTHOR]

A plasma arc generator was used to heat treat the free-standing CVD diamond films at 1450–1900 °C. An Arrhenius curve was fit according to trends in the measured Raman peak intensity ratio of diamond to graphite as a function of heat treatment temperature, and the curve was extrapolated linearly. It was found that the extrapolation lines intersected at the Debye temperature, Θ D = 2021 K. By comparing the activation energies of diamond graphitization in literature and from different measurement modes in our study, it was found that the graphitization mechanisms were different on both sides of Debye temperature due to differences in the excited lattice vibration modes. When the heat treatment temperature was just below the Debye temperature, the graphitization process was promoted by generating vacancies or the breaking of single C C bonds, and the apparent activation energy was 366 ± 60 kJ·mol−1. When the heat treatment temperature was above the Debye temperature, the graphitization process was promoted by the simultaneous breaking of multiple C C bonds, and the apparent activation energy was 887 ± 141 kJ·mol−1. In combination with the morphology changes on the surface of the CVD diamond film after high temperature heat treatment, the mechanism of the micro-cyclic phase transition on the surface of the diamond film at temperatures lower than Debye temperature was summarized as follows. First, C C bonds on the diamond surface were activated and broken at high temperatures, and some diamond carbon atoms dissociated from solid phase sites to the gas phase by forming hydrocarbon free radicals. Then, the carbon atoms from these hydrocarbons entered the graphite lattice step by step to complete the spontaneous deposition of sp2 clusters. [Display omitted] • The morphological changes of diamond surface dependent on temperature and hydrogen plasma environment were observed. • Taking the Debye temperature as a critical point, the graphitization activation energy exhibits a significant difference. • The graphitization mechanism of CVD diamond surface was proposed based on the kinetics analysis. [ABSTRACT FROM AUTHOR]

In order to realize the practical use of diamond as a semiconductor material, large-area single-crystal diamond wafers with uniform quality are required. Mosaic growth is an effective method to produce inch-grade single-crystal diamonds. However, the quality of the wafer is limited by the junction interface seriously, because cracking occurs easily due to the high internal stress. In this paper, the repetition growth method was adopted to grow mosaic splicing single-crystal diamond without polycrystalline diamond interface. The high-quality single crystal diamond slices were reduplicated by microwave plasma chemical vapor deposition (MPCVD). The substrates were obtained by cutting a piece of CVD diamond along a plane perpendicular to 〈001〉 (with a (100)-oriented surface). The evolution of the growth characteristics around the junction of the substrates at different stages was studied. The results show that the surface of the epitaxial layers gradually evolves from blurry terraces to a regular well-ordered step flow. When the substrates have the same deviation direction and the off-direction angles are within 3°, the junction of the substrates can connect smoothly. Raman mapping shows that there is a mixture of tensile stress and compressive stress near the junction. As the thickness of the epitaxial layer increases from 280 μm to 560 μm, the range of tensile stress near the joint area expands from 85 μm to 150 μm, the maximum tensile stress increases from 0.08 GPa to 0.16 GPa. In addition, the value of FWHM in the X-ray rocking curve is less than 2.80 cm−1 around the junction, which indicates good crystal quality. [Display omitted] • The evolution of growth characteristics around the junction in the mosaic diamond was studied. • The mosaic boundary evolved from blurry terraces to a well-ordered step flow and finally connected. • The lowest value of tensile stress near the joint area was reported as the film thickness increased. • The larger FWHM of Raman peak around the junction is caused by the increased tensile stress. • The "inherit" effect of NV content of the epitaxial layer was observed for the corresponding substrate. [ABSTRACT FROM AUTHOR]

In-situ micro-area analysis of precisely polished polycrystalline diamond (PCD) film by high-speed three-dimensional dynamic friction polishing (3DM-DFP) is carried out in this work, continuing from the previous works focusing on the subsurface cleavage and polishing mechanism. Multi-orientational grains with variable hardness anisotropy are generally considered the reason for the surface irregularity of PCD after smoothing. The unreached surface ultra-smoothness in local region after polishing is mainly resulted from the height difference at grain boundary (GB) area (e.g. , a selected GB micro-region is of around Ra roughness of 5.7 nm and altitude intercept of 6.6 nm). However, different individual grains nearby showing (100), (110), (111) orientations are all of roughness <0.5 nm, demonstrating these places are contiguously polished. The observed local roughening at GBs region after mechanical sliding accompanying with friction heat is the major factor to cause the surface irregularity, which is affected by the inhomogeneity of crystal thermal expansion and contraction associated with the defects in multi-orientational crystals generated by mechanical process. Among multi-crystals the low-position (110) region has a Ra roughness of 0.1 nm but with great tensile stress and relatively weak distortion compared with other orientational areas. An insight of the inhomogeneous volume change associated with thermal expansion and contraction affected by defects condition was proposed to straightforwardly illuminate the rationale of GB effects on the ultra-smoothing of PCD by 3DM-DFP. [Display omitted] • A phenomenon deteriorating ultra-smoothing of PCD by high-speed 3DM-DFP was found. • In-situ micro-area analysis of PCD before and after 3DM-DFP was carried out. • The height difference at GBs is resulted from the CTE inhomogeneity associated with defects. [ABSTRACT FROM AUTHOR]

Polycrystalline CVD diamond films were subjected to transient heat treatment at the temperature range of 1500–1900 °C in the Ar/H 2 plasma arc environment. The structural changes of the diamond grain boundaries (GB) were indirectly investigated by employing IR optical absorption, Raman spectroscopy, X-ray diffraction (XRD), and fractographic scanning electron microscopy (SEM). The graphitization difference between near-nucleation side and near-growth side is mainly due to the difference in the GBs' content. It is proposed that the bonded‑hydrogen atoms, of which a large amount remained in the diamond GBs, play an active role in the process of graphitization. We recognized the intensity evolution of a peak in Raman spectra located at 1470 cm−1, which was attributed to the trans -polyacetylene at diamond GBs. This result suggests the likelihood that the long-chain hydrocarbon precursor is involved in a mechanism for the sp3-to-sp2 transformation. As the propagation of the graphitization from diamond GB to grain interior, sp2 carbon with compressed state forms in its place due to the limited space for expansion. The graphite along GBs affects the fracture mode of the diamond films, which causes partial GBs to tear, while transgranular fracture occurs instead of directly intergranular fracture. [Display omitted] • A transient heat treatment method was employed to effectively keep the GB graphitization at an early stage. • The Graphitization model demonstrated the long-chain hydrocarbon precursor was involved in the sp3-to-sp2 transformation. • The fracture of annealed diamond was completed between transgranular and intergranular crack propagation. [ABSTRACT FROM AUTHOR]

The surface conductivity on the H-terminated diamond is still an interesting topic in the field of diamond electronics. Until now, the carrier mobility in the conductive channel has been limited to below 200cm2/Vs due to the various surface scattering mechanisms. In this paper, a high mobility conductive channel on the H-terminated diamond surface was reported. Firstly, the high quality diamond films were deposited on the commercial CVD diamond substrates. After polishing, the H-termination was obtained by hydrogen plasma treatment. The surface morphology of the H-terminated diamond was observed by atomic force microscope (AFM) and scanning electron microscope (SEM). The crystal quality on the diamond surface was characterized by Raman spectroscopy. The impurities in the crystals were tested by photoluminescence spectroscopy. The surface conductivity of H-terminated diamond was monitored comprehensively by Hall test. It can be found that the sheet resistance decreases much and the carrier mobility increases dramatically after the hydrogen plasma treatment and mechanical cleaning. The maximum mobility value is up to 365cm2/Vs with carrier density of 2.9 × 1012 cm−2, which is the highest value reported. Raman spectra of diamond surface show that a peak appears at 1121.4 cm−2 after the hydrogen plasma treatment, which corresponds to the nanocrystal diamond or carbon clusters of sp3 bonded material. The corresponding mobility enhancement mechanism on the H-terminated diamond surface was proposed. Unlabelled Image • The carrier mobility enhancement on the H-terminated diamond surface was found. • A thin carbon film on the diamond surface was observed with Raman peak at 1121 cm−1. • The H-terminated diamond surface showed high carrier mobility of 365cm2/Vs. • The corresponding mobility enhancement mechanism was proposed. [ABSTRACT FROM AUTHOR]

To unfold the promise of diamond as an advanced technical material, single-crystal diamonds (SCDs) and polycrystalline diamonds (PCDs) were smoothed by high-precision three-dimensional movement dynamic friction polishing (3DM-DFP) to achieve the ultra-smooth surface with roughness <5 nm (even 1 nm) more effectively. However, this inevitably leads to subsurface damage growth, i.e., subsurface defects evolved from nearly damage free to partial defects, and to cleavage faults beneath the SCD surface, resulting from mechanical fatigue and/or the rate of energy input by increasing the linear polishing velocity (from 12 m s−1 to 60 m s−1). In this study it was elucidated, for the first time, the subsurface uniform tile-roof-like cleavage faults and its formation mechanism of diamond after 3DM-DFP at the superhigh speed of linear sliding velocity of 60 m s−1. And the generated subsurface damage would be extended to about 10 μm in depth of the (100) SCD and manifested as micro-cleavage fault region, transition area and compressive zone. Meanwhile, two Raman peaks of 1425 cm−1 (first-order) and 2200 cm−1 (second-order) are assigned to the subsurface damage, which is the amorphous carbon (quasi sp 3 + sp 2) resulting from the cleavage along (111) crystal planes, based on the fine analysis of Raman spectroscopy and the study of subsurface defect evolution in different types of diamonds. Moreover, the assignment of concomitant peaks of 1750 cm−1 (localized defects) and 2100 cm−1 (sp 1 chains) were revealed. Unlabelled Image • SCDs and PCDs with roughness <5 nm (even 1 nm) were smoothed by 3DM-DFP. • Uniform subsurface cleavage was generated in SCD after 3DM-DFP at linear velocity of 60 m s−1. • Mechanical damage beneath the SCD (100) surface would be extended to 10 μm in depth. • Heavy subsurface damage comprises cleavage, transition and compressive regions. • Subsurface a -C consisting of quasi sp 3 + sp 2, sp 1 and C V was revealed after 3DM-DFP. [ABSTRACT FROM AUTHOR]