Series of visible light responsive Ag/AgBr/(I/S) composites based on I/S were synthesized by deposition-precipitation method. Methyl orange (MO) and other organic dyes were used to evaluate the photoactivity of Ag/AgBr/(I/S) composites. The results showed that Ag/AgBr/(I/S) composites display a good photocatalytic activity for organic dyes degradation. As the content of Ag/AgBr was 25 wt%, Ag/AgBr/(I/S) composites exhibited the best the photocatalytic activity for organic dyes. The degradation rate of Rhodamine B (RhB) and MO were 90% and 92% after 20 min. Furthermore, cycling experiments revealed that the 25%Ag/AgBr/(I/S) composites had long-term recycling stability. The photocatalytic mechanism of Ag/AgBr/(I/S) composites to MO degradation was studied by free radical trapping experiments and electron paramagnetic resonance (EPR) test, which indicating that photogenerated · O 2 − is the dominant reactive specie. • Ag/AgBr-I/S composite based on I/S were synthesized by deposition-precipitation method. • Ag/AgBr can improve the light absorption ability and photocatalytic property. • The photodegradation to Methyl orange of 25%-Ag/AgBr-I/S can reach 90% after 20 min. • The 25%-Ag/AgBr-I/S has good photocatalytic activity and chemical stability. [ABSTRACT FROM AUTHOR]

Environmental pollution is becoming ever more serious, and photodegradation using sustainable energy-solar energy is of great importance. Studies have revealed that semiconductor compound photocatalysts have a wide range of promising applications in the treatment of environmental pollution. Based on the current view, we synthesized flower-like 3NiS/Zn 0.5 Cd 0.5 S composite catalyst for photodegradation reaction by a two-step method. We analyzed the growth mechanism of the catalysts in terms of reaction time and reaction temperature, and characterized the composites utilizing FSEM, XRD, UV–vis, and XPS. The results showed that the 3NiS/Zn 0.5 Cd 0.5 S composites synthesized under the optimal conditions we obtained experimentally had higher photocatalytic performance with 99.1% final conversion rate in 1h compared to the 97.7% final conversion efficiency of pure Zn 0.5 Cd 0.5 S in 1.5 h, which showed higher conversion efficiency and conversion rate, meanwhile, after 8 cycles of stability experiments, the stability of the composite remained good. Of course, the stability of the photocatalyst is also essential. Fig. 6(d) shows the cycle stability test of 3NiS/ZCS photodegradation. After eight cycles, the final conversion efficiency remains high at 95.4%, which shows good cycling stability. • Flower-like 3NiS/Zn 0.5 Cd 0.5 S were obtained by Simple and low-cost hydrothermal and solution impregnation methods. • Flower-like 3NiS/Zn 0.5 Cd 0.5 S has a higher visible light utilization efficiency than pure Zn 0.5 Cd 0.5 S. • The synthesis of our flower-like 3NiS/Zn 0.5 Cd 0.5 S with high photocatalytic properties and good cycling stability is promising for industrial applications. [ABSTRACT FROM AUTHOR]