Search

Composite tubes have an asymmetry deformation and loading distribution under transverse bending. This work investigated the effect of the stacking sequence on the critical damage to a hybrid tube with 45° and 60° braided layers. In-situ infrared thermal imaging was adopted to observe the initiation and development of internal damage. As the outermost reinforcing material in the stacking structure, the 60° braided layer with high contact strength inhibited damage to the contact area at the top and improved the bending strength of the specimen at the initial stage of loading. As the inner reinforcing material in the stacking structure, the 45° braided layer with high bending toughness maintained the high stability of the load-carrying capacity during bending and restrained the tensile failure at the bottom of the tube. However, the interlaminar interface of braided layers with different braiding angles reduced the interlaminar fracture toughness. The interlaminar delamination failure developed rapidly as the bending at the bottom of the tube increased. This delamination damage determines the peak load-carrying capacity of the laminated structure. • The mechanical behavior of the stacking structure braided tube with the outer 60° braid and the inner 45° braid be studied. • Infrared thermography is applied to detect and analyze damage distribution degree in the loading process. • The load and damage distribution of stacking structure braided tubes are analyzed. [ABSTRACT FROM AUTHOR]

In this study, damage behavior and failure mode of braided composite tube subjected to repeated transverse low-velocity impact were investigated by combining experimental and numerical methods. The effects of impact energy (2.0 J, 5.6 J and 10.5 J) and impact position (identical, adjacent and opposite positions) on impact responses were evaluated. A finite element (FE) model with high computational efficiency was also established to predict the effect of single impact on the repeated impact response by varying boundary conditions. When subjected to single impact, the braided tube presented delamination-dominated damage behaviors caused by obvious structural deformation. The top part sunken and both lateral sides bulged, were found to have correlation with the mechanical response of tube with respect to initial scope and peak load, respectively. The delamination area increased at higher impact energies due to increasing shear stress caused by adjacent braided layers. Delamination induced by the first impact had different role on repeated impact responses. At identical position, it caused larger sinking deformation at top part of the tube and thus a lower initial scope. At adjacent position with impact energy of 5.6/10.5 J, the delamination damage caused a reduced resistance to bulging deformation at one lateral side of the tube, leading to a lower peak load. At opposite position, it had no obvious influence on repeated impact response. • The damage behavior of braided tube subjected to single transverse impact with different impact energy was investigated. • Mechanical response of repeated impact depended on delamination position caused by single impact. • The proposed numerical model can provide accuracy results for repeated impact scenario. [ABSTRACT FROM AUTHOR]