Search

• A simple liquid Ga assisted-alloying/dealloying strategy to fabricate nanoporous Ag. • The thickness of alloy layer/nanoporous Ag varies with the mass loading of Ga. • The bimodal wire-like and unimodal bulk-like nanoporous Ag is obtained. • The substrate-supported nanoporous Ag exhibits excellent mechanical properties. The substrate-supported nanoporous Ag with controllable thickness and different morphologies (bulk-like and wire-like) is fabricated via the liquid Ga-assisted alloying/dealloying strategy. [Display omitted] Nanoporous metals show great potentials in various applications including catalysis, sensing, actuation and supercapacitors. The liquid Ga-assisted alloying/dealloying strategy is a feasible and scalable way to fabricate substrate-supported nanoporous metals. However, the influence of intrinsic alloying mode and mechanism on the formation and modulation of nanoporous structure has not been thoroughly explored before. In this work, after painting liquid Ga on Ag foil, both the bulk-like Ag 3 Ga (in the Ag-rich zone) and wire-like Ag 3 Ga (in the liquid Ga-rich zone) form owing to the interdiffusion of Ag and Ga atoms. Correspondingly, the bimodal wire-like and unimodal bulk-like nanoporous Ag is obtained because of the structure inheritance during dealloying. In addition, the thickness of alloy layer (nanoporous layer) versus mass loading of liquid Ga follows a good linear relationship. The in-situ X-ray diffraction of dealloying from Ag 3 Ga to nanoporous Ag illustrates no other intermetallic phase appears and the dealloying process can be described by the dissolution-surface diffusion model. More importantly, the substrate-supported nanoporous Ag exhibits excellent mechanical properties which are of great importance to the future applications of nanoporous metals. [ABSTRACT FROM AUTHOR]

Metallic actuators have received a wide range of attention in the past two decades because of their larger strains than piezoelectric ceramics and higher strength relative to conducting polymers. However, the metallic actuators composed of noble metals are limited to the high material cost for further development and practical applications. Here, nanoporous CuMnNi (np‐CMN) alloys are fabricated from a ternary Mn70Cu20Ni10 precursor through an electrochemical dealloying method, and their microstructures/compositions are further regulated through different electrochemical processes (multi‐step and two‐step). The np‐CMN alloys show good electrochemical actuation properties in 1 m NaOH solution, and the sample obtained from two‐step dealloying exhibits much better actuation performance than that from multi‐step dealloying. The maximum strain amplitude of np‐CMN could reach up to 0.46%, which is comparable to or even better than that of noble metal‐based actuators. Our work indicates that the low‐cost np‐CMN alloy could be a competitive material among electrochemical metallic actuators. [ABSTRACT FROM AUTHOR]

Ag-Zn alloys are identified as highly active and selective electrocatalysts for CO2 reduction reaction (CO2RR), while how the phase composition of the alloy affects the catalytic performances has not been systematically studied yet. In this study, we fabricated a series of Ag-Zn alloy catalysts by magnetron co-sputtering and further explored their activity and selectivity towards CO2 electroreduction in an aqueous KHCO3 electrolyte. The different Ag-Zn alloys involve one or more phases of Ag, AgZn, Ag5Zn8, AgZn3, and Zn. For all the catalysts, CO is the main product, likely due to the weak CO binding energy on the catalyst surface. The Ag5Zn8 and AgZn3 catalysts show a higher CO selectivity than that of pure Zn due to the synergistic effect of Ag and Zn, while the pure Ag catalyst exhibits the highest CO selectivity. Zn alloying improves the catalytic activity and reaction kinetics of CO2RR, and the AgZn3 catalyst shows the highest apparent electrocatalytic activity. This work found that the activity and selectivity of CO2RR are highly dependent on the element concentrations and phase compositions, which is inspiring to explore Ag-Zn alloy catalysts with promising CO2RR properties. [ABSTRACT FROM AUTHOR]

A class of ruthenium-nickel alloy catalysts featured with nanoporous nanowires (NPNWs) were synthesized by a strategy combining rapid solidification with two-step dealloying. RuNi NPNWs exhibit excellent electrocatalytic activity and stability for oxygen evolution reaction (OER) and hydrogen evolution reaction (HER) in which the RuNi-2500 NPNWs catalyst shows an OER overpotential of 327 mV to deliver a current density of 10 mA cm−2 and the RuNi-0 NPNWs catalyst requires the overpotential of 69 mV at 10 mA cm−2 showing the best HER activity in alkaline media. Moreover, the RuNi-1500 NPNWs catalyst was used as the bifunctional electrocatalyst in a two-electrode alkaline electrolyzer for water splitting, which exhibits a low cell voltage of 1.553 V and a long-term stability of 24 h at 10 mA cm−2, demonstrating that the RuNi NPNWs catalysts can be considered as promising bifunctional alkaline electrocatalysts. A class of ruthenium-nickel alloy catalysts featured with nanoporous nanowires (NPNWs) was synthesized by a strategy combined rapid solidification with two-step dealloying, in which the total cell voltage of RuNi-1500 NPNWs electrolyzer for water splitting is 1.553 V to deliver a current density of 10 mA cm−2. [Display omitted] • A two-step dealloying strategy was used to prepare RuNi catalysts. • RuNi catalysts exhibit a unique nanoporous nanowires (NPNWs) morphology. • RuNi NPNWs catalysts show excellent electrocatalytic performance for OER and HER. • RuNi NPNWs catalysts can be used as bifunctional catalysts for water splitting. [ABSTRACT FROM AUTHOR]

The synthesis of cost-effective and high-performance electrocatalysts for water splitting is the main challenge in electrochemical hydrogen production. In this study, we adopted a high throughput method to prepare bi-metallic catalysts for oxygen/hydrogen evolution reactions (OER/HER). A series of Ni–Mo alloy electrocatalysts with tunable compositions were prepared by a simple co-sputtering method. Due to the synergistic effect between Ni and Mo, the intrinsic electrocatalytic activity of the Ni–Mo alloy electrocatalysts is improved, resulting in excellent HER and OER performances. The Ni 90 Mo 10 electrocatalyst shows the best HER performance, with an extremely low overpotential of 58 mV at 10 mA cm−2, while the Ni 40 Mo 60 electrocatalyst shows an overpotential of 258 mV at 10 mA cm−2 in OER. More significantly, the assembled Ni 40 Mo 60 //Ni 90 Mo 10 electrolyzer only needs a cell voltage of 1.57 V to reach 10 mA cm−2 for overall water splitting. [Display omitted] • A high throughput method was used to prepare Ni–Mo alloy catalysts. • Ni–Mo alloy catalysts exhibit remarkable activity and stability for HER and OER. • The Ni–Mo alloy acts as a bifunctional catalyst for overall water splitting. • The synergistic effect between Ni and Mo leads to the excellent performances. [ABSTRACT FROM AUTHOR]

Alloying Ni with Pd lowers the overpotential of benzaldehyde hydrogenation and obtains a reaction rate 20 times higher than that of Ni at 0.1 V vs. RHE, which is ascribed to the lower binding energy of benzaldehyde on the metal surface revealed by the in-situ IR study. [Display omitted] • Nanoporous nanowire NiPd alloys were synthesized using a dealloying method. • Alloying Ni and Pd lowers the overpotential of ECH of benzaldehyde. • The activity of NiPd alloy is comparable with Pd. • In-situ IR study reveals that Pd tunes the binding strength of adsorbed benzaldehyde. Ni is one of the most promising catalysts in aldehydes hydrogenation, although the high overpotential and low Faradaic efficiency limit its electrocatalytic performances. Here we introduce an effective and facile alloying strategy to tune the electronic structure of Ni. We demonstrate that alloying Pd to Ni can significantly boost the electrocatalytic performances of benzaldehyde hydrogenation and lower the overpotential to the level of pure Pd. Pd introduction enhances the electrocatalytic hydrogenation process over hydrogen evolution reaction (HER), and results in an increased Faradaic efficiency. The npnw-Ni 82 Pd 18 catalyst shows the optimal atomic ratio of Ni and Pd among the explored catalysts, and achieved a turnover frequency (TOF) value of 1387 mol mol metal -1h-1 at -0.1 V vs. reversible hydrogen electrode (RHE), higher than that of npnw-Ni (60 mol mol metal -1h-1) and comparable to np-Pd (1306 mol mol metal -1h-1) under the same reaction conditions. In-situ surface-enhanced infrared absorption spectroscopy study reveals that the electronic interactions between Ni and Pd would activate the adsorbed benzaldehyde, and therefore result in an enhanced activity in benzaldehyde hydrogenation. [ABSTRACT FROM AUTHOR]

A room-temperature Ag 3 Ga-mediated liquid EGaSn anode with improved wettability for advanced Mg ion batteries. [Display omitted] • The room-temperature Ag 3 Ga-mediated liquid EGaSn anode was simply prepared for MIBs. • Ag 3 Ga can improve the wettability of EGaSn on the substrate and provide capacity. • ssm-Ag 3 Ga-EGaSn shows superior electrochemical performance in half and full cells. • Reaction mechanism of the Ag 3 Ga-mediated liquid EGaSn anode was unveiled. Liquid metals with a self-healing property can address the passivation issue of Mg metal and the huge volume variation problem of solid alloy-type anodes in rechargeable magnesium ion batteries (MIBs). Liquid Ga-based anodes show great potentials in MIBs, however, being operated at room temperature is a great challenge. Herein, a novel strategy is proposed to enhance the room-temperature Mg storage performance of liquid eutectic GaSn (EGaSn) alloy through constructing a bifunctional intermetallic compound (Ag 3 Ga) layer on the current collector. This Ag 3 Ga layer could greatly improve the wettability of EGaSn on the substrate in the electrolyte environment. Moreover, operando X-ray diffraction confirms that Ag 3 Ga could participate the reversible alloying/dealloying reactions during the discharge/charge processes and thus provide an extra capacity. Eventually, the Ag 3 Ga-mediated EGaSn anode exhibits outstanding electrochemical performance towards Mg storage in both half and full cells at room temperature (∼24 and 21 °C), as benchmarked with state-of-the-art anodes in MIBs. Specially, the MIBs could be stably cycled up to 600 cycles in the half cell configuration, and 100 cycles in the full cell assembly. This work provides useful information on the development of advanced anodes for MIBs. [ABSTRACT FROM AUTHOR]