Abstract: Due to the unique properties of amphiphilic Pluronic block copolymers, they have been blended with other polymers such as PVDF to prepare membranes. Considering the stability issue, the strong pore-forming ability of Pluronic F127, and the mechanical strength of the resultant membranes, Pluronic/LiCl mixed additive consisting of a very low concentration of Pluronic has been used in this study. The effects of spinning conditions on PVDF hollow fiber fabrication have also been studied. It is found that the use of merely 0.2wt% of Pluronic is sufficient to impose significant impacts on the morphology, filtration performance, and mechanical properties of the resultant fibers. Hollow fibers spun using higher coagulant temperature, higher take-up speed, and water as the bore fluid exhibit better mechanical properties and filtration performance. PVDF hollow fiber membranes with PWP of 1180L/m2 hMPa and MWCO of 5kDa were obtained when spun with optimized spinning conditions and using 3wt% of LiCl and 0.2wt% of Pluronic as the mixed additive. The fibers can withstand a pressure of 0.55MPa from the lumen. [Copyright &y& Elsevier]

The use of nanotechnology in water separation membranes is a promising approach to alleviate the global water crisis. Graphene oxide (GO) with its unique water transport property has exhibited high potential for application in the water treatment processes. In this study, we have designed and fabricated a novel nanofiltration (NF)-like GO surface deposited poly(amide-imide)–polyethyleneimine (PAI–PEI) hollow fiber membrane. The PAI hollow fiber substrate was prepared by phase inversion and modified with PEI to obtain a positively charged membrane surface. The negatively charged GO nanosheets were then electrostatically immobilized onto the membrane surface via an instant dip-coating to form the NF-like selective layer. Our results have shown that the GO nanosheets serve as effective selective barriers and can achieve higher water permeability up to 86% without compromising membrane selectivity when used to substitute part of the PEI cross-linked selective layer. This is attributed to the smaller hydrodynamic resistance of GO nanosheets and their ability to effectively narrow the pore size distribution. Moreover, shortening of the membrane modification time and better mechanical properties of the GO modified membrane can be attained by avoiding excessive PEI cross-linking. The GO deposition also exhibits good stability when subjected to a backwashing pressure of 100,000 Pa and a cross-flow rate of 600 mL/min, which corresponds to a velocity of 14 cm/s and a Reynolds number of ~870. These results have demonstrated a high potential of using this GO modified hollow fiber membrane for large scale water softening applications. [ABSTRACT FROM AUTHOR]