Search

Transition metal catalysts are particularly effective in improving the kinetics of the reversible hydrogen storage reaction for light metal hydrides. Herein, K2MoO4 microrods were prepared using a simple evaporative crystallization method, and it was confirmed that the kinetic properties of magnesium hydride could be adjusted by doping cubic K2MoO4 into MgH2. Its unique cubic structure forms new species in the process of hydrogen absorption and desorption, which shows excellent catalytic activity in the process of hydrogen storage in MgH2. The dissociation and adsorption time of hydrogen is related to the amount of K2MoO4. Generally speaking, the more K2MoO4, the faster the kinetic performance and the shorter the time used. According to the experimental results, the initial dehydrogenation temperature of MgH2 + 10 wt% K2MoO4 composite is 250 °C, which is about 110 °C lower than that of As-received MgH2. At 320 °C, almost all dehydrogenation was completed within 11 min. In the temperature rise hydrogen absorption test, the composite system can start to absorb hydrogen at about 70 °C. At 200 °C and 3 MPa hydrogen pressure, 5.5 wt% H2 can be absorbed within 20 min. In addition, the activation energy of hydrogen absorption and dehydrogenation of the composite system decreased by 14.8 kJ/mol and 26.54 kJ/mol, respectively, compared to pure MgH2. In the cycle-stability test of the composite system, the hydrogen storage capacity of MgH2 can still reach more than 92% after the end of the 10th cycle, and the hydrogen storage capacity only decreases by about 0.49 wt%. The synergistic effect among the new species MgO, MgMo2O7, and KH generated in situ during the reaction may help to enhance the absorption and dissociation of H2 on the Mg/MgH2 surface and improve the kinetics of MgH2 for absorption and dehydrogenation. [ABSTRACT FROM AUTHOR]

Carbon materials play an important role in the development of solid hydrogen storage materials. The main purpose of this work is to study the low-cost synthesis of biomass carbon (BC) and its positive effect on the hydrogen storage behavior of magnesium hydride (MgH2). Herein, it is proven that when biomass carbon (BC) is used together with magnesium hydride (MgH2), biomass carbon can be used as an adsorption and desorption channel for hydrogen. The initial dehydrogenation temperature of MgH2 + 10 wt% BC composite is 250 °C, which is 110 °C lower than that of pure MgH2. In addition, the MgH2 + 10 wt% BC composite system can complete all dehydrogenation processes within 10 min at 350 °C. Meanwhile, 5.1 wt% H2 can also be dehydrogenated within 1 h at 300 °C. Under the same conditions, MgH2 hardly starts to release hydrogen. After complete dehydrogenation, the composite can start to absorb hydrogen at 110 °C. Under the conditions of 225 °C and 3 MPa, 6.13 wt% H2 can be absorbed within 1 h, basically reaching the theoretical dehydrogenation limit. Cycling experiments show that the MgH2 + 10 wt% BC composite has a good stability. After 10 cycles, the hydrogen storage capacity shows almost no obvious decline. It is believed that this study can help in the research and development of efficient carbon-based multifunctional catalysts. [ABSTRACT FROM AUTHOR]

Due to its high hydrogen storage efficiency and safety, Mg/MgH2 stands out from many solid hydrogen storage materials and is considered as one of the most promising solid hydrogen storage materials. However, thermodynamic/kinetic deficiencies of the performance of Mg/MgH2 limit its practical applications for which a series of improvements have been carried out by scholars. This paper summarizes, analyzes and organizes the current research status of the hydrogen storage performance of Mg/MgH2 and its improvement measures, discusses in detail the hot studies on improving the hydrogen storage performance of Mg/MgH2 (improvement measures, such as alloying treatment, nano-treatment and catalyst doping), and focuses on the discussion and in-depth analysis of the catalytic effects and mechanisms of various metal-based catalysts on the kinetic and cyclic performance of Mg/MgH2. Finally, the challenges and opportunities faced by Mg/MgH2 are discussed, and strategies to improve its hydrogen storage performance are proposed to provide ideas and help for the next research in Mg/MgH2 and the whole field of hydrogen storage. [ABSTRACT FROM AUTHOR]