Search

Transition metal catalysts are particularly effective in improving the kinetics of the reversible hydrogen storage reaction for light metal hydrides. Herein, K2MoO4 microrods were prepared using a simple evaporative crystallization method, and it was confirmed that the kinetic properties of magnesium hydride could be adjusted by doping cubic K2MoO4 into MgH2. Its unique cubic structure forms new species in the process of hydrogen absorption and desorption, which shows excellent catalytic activity in the process of hydrogen storage in MgH2. The dissociation and adsorption time of hydrogen is related to the amount of K2MoO4. Generally speaking, the more K2MoO4, the faster the kinetic performance and the shorter the time used. According to the experimental results, the initial dehydrogenation temperature of MgH2 + 10 wt% K2MoO4 composite is 250 °C, which is about 110 °C lower than that of As-received MgH2. At 320 °C, almost all dehydrogenation was completed within 11 min. In the temperature rise hydrogen absorption test, the composite system can start to absorb hydrogen at about 70 °C. At 200 °C and 3 MPa hydrogen pressure, 5.5 wt% H2 can be absorbed within 20 min. In addition, the activation energy of hydrogen absorption and dehydrogenation of the composite system decreased by 14.8 kJ/mol and 26.54 kJ/mol, respectively, compared to pure MgH2. In the cycle-stability test of the composite system, the hydrogen storage capacity of MgH2 can still reach more than 92% after the end of the 10th cycle, and the hydrogen storage capacity only decreases by about 0.49 wt%. The synergistic effect among the new species MgO, MgMo2O7, and KH generated in situ during the reaction may help to enhance the absorption and dissociation of H2 on the Mg/MgH2 surface and improve the kinetics of MgH2 for absorption and dehydrogenation. [ABSTRACT FROM AUTHOR]

Carbon materials play an important role in the development of solid hydrogen storage materials. The main purpose of this work is to study the low-cost synthesis of biomass carbon (BC) and its positive effect on the hydrogen storage behavior of magnesium hydride (MgH2). Herein, it is proven that when biomass carbon (BC) is used together with magnesium hydride (MgH2), biomass carbon can be used as an adsorption and desorption channel for hydrogen. The initial dehydrogenation temperature of MgH2 + 10 wt% BC composite is 250 °C, which is 110 °C lower than that of pure MgH2. In addition, the MgH2 + 10 wt% BC composite system can complete all dehydrogenation processes within 10 min at 350 °C. Meanwhile, 5.1 wt% H2 can also be dehydrogenated within 1 h at 300 °C. Under the same conditions, MgH2 hardly starts to release hydrogen. After complete dehydrogenation, the composite can start to absorb hydrogen at 110 °C. Under the conditions of 225 °C and 3 MPa, 6.13 wt% H2 can be absorbed within 1 h, basically reaching the theoretical dehydrogenation limit. Cycling experiments show that the MgH2 + 10 wt% BC composite has a good stability. After 10 cycles, the hydrogen storage capacity shows almost no obvious decline. It is believed that this study can help in the research and development of efficient carbon-based multifunctional catalysts. [ABSTRACT FROM AUTHOR]

The development of high-efficiency carbon-based multifunctional catalysts is of great significance for improving solid-state hydrogen storage materials. Herein, it was confirmed that CoMoO 4 sheet-like nanocatalysts uniformly supported on the surface of reduced graphene oxide (CoMoO 4 /rGO) were successfully prepared by a simple hydrothermal reaction. The novel CoMoO 4 /rGO catalyst was subsequently doped into MgH 2 to improve its hydrogen storage performance. MgH 2 –10 wt% CoMoO 4 /rGO starts to release hydrogen at around 204 °C, which is about 36 °C and 156 °C lower than that of MgH 2 −10 wt%CoMoO 4 and pure MgH 2 , respectively. In addition, 6.25 wt% H 2 can be released within 10 min at 300 °C. After complete dehydrogenation, H 2 can be absorbed below 80 °C. Meanwhile, it can absorb 4.2 wt% H 2 in 20 min under the condition of 150 °C and 3 MPa. Moreover, the activation energy of hydrogen absorption and dehydrogenation of MgH 2 –10 wt%CoMoO 4 /rGO composites are reduced by 31.44 kJ mol−1 and 33.78 kJ mol−1, respectively, compared with pure MgH 2. Cycling experiment shows that the MgH 2 –10 wt%CoMoO 4 /rGO composite system can still maintain about 98% of the hydrogen storage capacity after 10 cycles. Furthermore, studies on the catalytic mechanism show that the synergistic effect between the in-situ generated MgO, Co 7 Mo 6 and Mo may help to promote the diffusion of H 2 , thereby improving the MgH 2 Hydrogen storage properties. • MgH 2 –10 wt%CoMoO 4 /rGO composite system was reported for the first time. • MgH 2 –10 wt%CoMoO 4 /rGO composite material starts dehydrogenation at about 204 °C. • MgH 2 –CoMoO 4 /rGO composites showed promising kinetic properties. • MgH 2 –CoMoO 4 /rGO composites showed good cyclic stability. • MgO, Mo and Co 7 Mo 6 were formed in situ during the reaction. [ABSTRACT FROM AUTHOR]

Due to its high hydrogen storage efficiency and safety, Mg/MgH2 stands out from many solid hydrogen storage materials and is considered as one of the most promising solid hydrogen storage materials. However, thermodynamic/kinetic deficiencies of the performance of Mg/MgH2 limit its practical applications for which a series of improvements have been carried out by scholars. This paper summarizes, analyzes and organizes the current research status of the hydrogen storage performance of Mg/MgH2 and its improvement measures, discusses in detail the hot studies on improving the hydrogen storage performance of Mg/MgH2 (improvement measures, such as alloying treatment, nano-treatment and catalyst doping), and focuses on the discussion and in-depth analysis of the catalytic effects and mechanisms of various metal-based catalysts on the kinetic and cyclic performance of Mg/MgH2. Finally, the challenges and opportunities faced by Mg/MgH2 are discussed, and strategies to improve its hydrogen storage performance are proposed to provide ideas and help for the next research in Mg/MgH2 and the whole field of hydrogen storage. [ABSTRACT FROM AUTHOR]

• Nano NiO/C catalysts were prepared by ultrasonic oscillation and calcination. • Hydrogen could be released at 195 °C and absorbed at 50 °C for the composite. • De/hydrogenation activation energy of the composite were significantly reduced. • The composite material had good cyclic reversibility. • Ab initio calculations showed that NiO and Mg 2 Ni could improve the diffusivity of H atoms. Magnesium based solid hydrogen storage material (MgH 2) has the advantages of good safety and high hydrogen storage capacity in the shipping field. However, the high hydrogen absorption and desorption temperature have not been well solved. Herein, this work proves that it is very effective to improve the hydrogen storage performance of MgH 2 by doping nano NiO/C catalyst. Specifically, experimental results showed that MgH 2 + 9 wt% NiO/C composite could dehydrogenate at 195 °C, which was 155 °C lower than pure MgH 2. In addition, 6.21 wt% H 2 could be released rapidly at 300 °C for 10 min. After complete dehydrogenation, the absorption rate of hydrogen is 50 °C, which is 80 °C lower than that of pure MgH 2. Moreover, 5.13 wt% H 2 could be absorbed within 1 h at 125 °C and 3 MPa hydrogen pressure. In addition, dehydrogenation and hydrogen absorption apparent activation energies of MgH 2 + 9 wt% NiO/C composite are 70.26 kJ/mol and 25.55 kJ/mol lower than those of pure MgH 2 , respectively. The cycle experiment showed that MgH 2 + 9 wt% NiO/C had excellent cycle stability and could maintain 98.8% hydrogen storage capacity after 20 cycles. Furthermore, the study of the catalytic mechanism indicated that NiO/C catalyst is evenly distributed on the surface of MgH 2. More importantly, Mg 2 Ni/Mg 2 NiH 4 is generated in situ, which acts as a "hydrogen pump" and speeds up hydrogen diffusion during the hydrogen absorption and desorption cycle. [ABSTRACT FROM AUTHOR]