Anodisation with electrochemical cathodic deposition method was employed to modify the surface of Ti implants with a bilayer coating made of Sr- doped titania (Sr-TiO2) and hydroxyapatite doped with magnesium (Mg-HAp). The Mg-HAp/Sr-TiO2 bilayer coating was compared with pure TiO2 and Sr-TiO2 single-layer coating. The Sr incorporation into TiO2 and Mg substitution into HAp strengthened their bioactive properties. The tensile test indicated increase in the mechanical strength of the bilayer coated substrate compared to pure TiO2 substrate. Moreover, the study indicated that the Sr and Mg ions were uniformly incorporated into the Mg-HAp/Sr-TiO2 bilayer coating with significantly higher roughness and hydrophilicity compared to the control. In vitro studies with osteoblasts cells had a superior response to the Mg-HAp/Sr-TiO2 bilayer surface. It was found that a bilayer Mg-HAp/Sr-TiO2 coating on Ti implants promotes bioactivity and has superior adhesion strength necessary for osseointegration and bone healing. [ABSTRACT FROM AUTHOR]

A Ti3C2 MXene/Ti composite powder was developed through surface modification and powder coating for producing a high-performance titanium matrix composites (TMCs) by laser power bed fusion. Introducing MXene rarely changed the original sphericity and flowability of Ti powder while it slightly enhanced the laser absorption capacity of Ti powder. The printing conditions in turn affected the morphology and distribution of MXene in as-printed composites. At optimised printing parameters, majority of MXene with high structural integrity and uniform distribution remained along the grain boundaries of as-printed composites, and a combination of high surface quality, geometrical accuracy and densification was obtained. The remaining MXene played the synergy of pulling-out effect and load transfer role, which increased the yield strength from 530 to 710 MPa, while retaining good ductility (elongation of 19.8%). Compared with ASTM standard cast Ti64 alloy, our MXene/Ti composites also exhibited superior comprehensive tensile properties and excellent strength-ductility synergy. [ABSTRACT FROM AUTHOR]