Search

The failure mode is a dominant factor of mechanical performance of braided composite tube subjected to axial compression. The failure mode was modified by tailoring stack-up sequence of composite tubes hybridized by bi/tri-axial braided laminate. The thermal photographing and micro-CT scanning methods were employed to monitor the in-situ damage progression and post-mortem specimen, respectively. The results show that the delamination was easy to be induced at the interface nearby tri-axial braided laminate. It attributes to the combination between the crack caused by local buckling of the axial yarns and the crack caused by shear deformation of braiding yarns. By the illumination of this behavior, delamination is controlled to occur at the different position along thickness direction of braided tube by adjusting the stacking sequence of braided laminates. When delamination position transfer from the inner/outer sides to the middle of tube wall, the failure mode transfer from the progressive folding to splaying, which increase the specific energy absorption by 45.77%. [ABSTRACT FROM AUTHOR]

In this study, the performance of braided composite tubes under low-velocity transverse impact loading at mid-span was investigated using both numerical and experimental methods. Three types of braided composite tubes with different braiding angles (30°, 45°, and 60°) were manufactured. The transverse punch behavior of the tubes was examined on a low-velocity imspact test bench. A meso-level finite element model of the composite tube was also established for identifying the damage initiation and development. The numerical results showed a good correlation with the experimental data. The mechanical response including force–time histories, force–displacement histories, and fracture morphologies was compared between three types of composite tubes for analyzing the influence of braiding angle on the impact response and failure mode. Although suffering from the low bending stiffness depends on fiber volume fraction at initial impact stage, the braided tube with 30° angle engaged more portion to resist impact loading in subsequent process and thus presented higher peak loading than the one with large angle. In addition, there are distinct different failure modes between composite tubes with various braiding angles. Shear yarn breakage underneath the punch was prone to occur in 30° sample because the braiding yarn was closer to the axial direction of tube. In contrast, the resin was deboned severely from the braiding yarn and then the braiding yarn exhibits plastic deformation in 60° sample due to the stress concentration caused by the large braiding angle. [ABSTRACT FROM AUTHOR]

• The effect of ply number on the impact response was identified. • The effect of impact damage on the residual axial compression behavior was analyzed. • The proposed two-step FE model predicted accurately the damage behaviors of braided tube. In this study, transverse low-velocity impact response and residual axial compression behavior of braided composite tube with different ply number was investigated by experimental and numerical methods. The transverse low-velocity impact tests with 5.6 J energy were conducted on the composite tubes. The quasi-static axial compression performance of intact and pre-impacted tubes was compared to evaluate the effect of impact damage. A two-step finite element (FE) model was also established to reveal damage mechanisms of braided tube under impact loading and following axial compression. It was found that the wall thickness had a significant influence on the impact response. Obvious structural deformation occurred in 2-ply tube when subjected to impact loading, resulting in a large projected delamination area. In following axial compression process, the delamination failure significantly reduced the local compression stiffness and caused a structural instability, which led to a buckling failure mode. In contrast, increasing bending stiffness of 3 or 4-ply tube suppressed its structural deformation during impact, leading to a confined projected delamination area and therefore the buckling of tube wall was prevented effectively when subjected to axial compression. For all impacted tubes, the transition of failure mode from progressive folding mode in intact tube led to a lower energy absorption capacity per composite ply, especially for 2-ply tube. [ABSTRACT FROM AUTHOR]

[Display omitted] • Integral braiding and near-net forming of CFRP and CFRP/Al hybrid composite tubes. • In-situ and real-time failure mode analysis of CFRP and CFRP/Al composite tube under transverse impact. • Comprehensive effect of braiding angle, locailzed temperature rise, and ductile aluminum on the damage mechanism. High-speed infrared thermography, micro-CT characterization and full-scale mesostructural simulation were jointly applied to reveal the impact deformation and damage mechanism of composite tubes. Two different failure modes, namely the Impact Side Dominated (ISD) and Impact-/Non-impact Side (INIS), were found to have relation with the braiding angle and localized temperature rise. The hybrid effect can not only prevent resin fragmentation in the triangle region at the lateral side and the diamond region at the non-impact side, but also inhibit the CFRP damage development at the lateral and non-impact side. In small-angle braided tube, the impact-side rebound trend of CFRP layer leads to mismatch at the CFRP-Al interface, which results in opening delamination. In large-angle braided tube, the non-impact-side damage plays an important role in further load-bearing capacity. Apart from the structure effect, temperature rise has an effect on composite damage mode by degrading the localized matrix stiffness. [ABSTRACT FROM AUTHOR]