Search

In this study, damage behavior and failure mode of braided composite tube subjected to repeated transverse low-velocity impact were investigated by combining experimental and numerical methods. The effects of impact energy (2.0 J, 5.6 J and 10.5 J) and impact position (identical, adjacent and opposite positions) on impact responses were evaluated. A finite element (FE) model with high computational efficiency was also established to predict the effect of single impact on the repeated impact response by varying boundary conditions. When subjected to single impact, the braided tube presented delamination-dominated damage behaviors caused by obvious structural deformation. The top part sunken and both lateral sides bulged, were found to have correlation with the mechanical response of tube with respect to initial scope and peak load, respectively. The delamination area increased at higher impact energies due to increasing shear stress caused by adjacent braided layers. Delamination induced by the first impact had different role on repeated impact responses. At identical position, it caused larger sinking deformation at top part of the tube and thus a lower initial scope. At adjacent position with impact energy of 5.6/10.5 J, the delamination damage caused a reduced resistance to bulging deformation at one lateral side of the tube, leading to a lower peak load. At opposite position, it had no obvious influence on repeated impact response. • The damage behavior of braided tube subjected to single transverse impact with different impact energy was investigated. • Mechanical response of repeated impact depended on delamination position caused by single impact. • The proposed numerical model can provide accuracy results for repeated impact scenario. [ABSTRACT FROM AUTHOR]

The study aims to understand the effect of stacking sequence on the impact response and residual flexure characteristics of braided composite tube by combination of low-velocity impact, fracture observation and acoustic emission monitoring. Two stacking sequence configurations of braided tube in terms of [I60/O40] and [I40/O60] were designed and their low-velocity impact response and damage behavior were examined. Uniform structures namely [I40/O40] and [I60/O60] were also employed as reference specimens. The quasi-static bending performances of intact and impacted tubes were further compared to evaluate the influence of impact damage on residual performance. The results show that failure mode of impacted tubes strongly depends on braided structure of outer ply, of which large braiding angle(60°) leads to the formation of bottom delamination and degradation of structural integrity. The comparative experiments indicate that [I60/O40] tube improves flexure after impact performance with respect to specific energy absorption by 45.98% over [I40/O60] counterpart because of absence of bottom delamination. Thus, structure design of braided composite consisting of intra-ply structure and stacking sequence would be an economically feasible method to improve the transverse mechanical performance. • The braided structure of outer ply has a decisive role on the failure mode of composite tube under transverse impact. • There was a sharp load dropping when a bottom delamination occurred in intact braided tube under quasi-static bending. • Bottom delamination induced by impact significantly reduced residual bending performance of braided tube. [ABSTRACT FROM AUTHOR]