Cold-mixed epoxy asphalt (CEA) has attracted extensive attention in overloaded and steel bridge pavement and maintenance engineering because of its room temperature construction and low energy consumption. However, the compatibility of epoxy resin and asphalt in CEA is still a challenge, limiting its application to some extent. This study aims to enhance the compatibility of CEA with low amounts of plant oil-based compatibilizers and suggest appropriate methods for assessing the compatibility of CEA. GO-grafted epoxidized soybean oil (GOESO) and GO-grafted soybean oil (GOSO) were synthesized and used to modify CEA. The GO and ESO (or SO) solutions were prepared at concentrations of 0.5 mg/mL and 5 mg/mL, respectively. The pH of the solution was adjusted to 5∼6 before heating. The results showed that 0.2 wt% of GO-modified oil-based compatibilizers had similar effects as 30 wt% of oil-based compatibilizers and did not significantly alter the crystal and chemical structures of the CEAs. GOESO is the preferred recommended GO-modified compatibilizer because of the enhanced compatibilizing ability of the epoxy groups in ESO. The compatibilization mechanism involved the effects of the oils on the chemical structures, curing reaction rate, and microstructures of CEAs. The proportion of asphalt particles larger than 20 μm and the reaction rate had strong correlations with the mechanical properties of the cured CEAs. Molecular dynamics simulations revealed that GOSO reduced the solubility parameter (δ) and Flory-Huggins parameter (χ) difference between components A and B by 39.4% and 65.8%, respectively, while GOESO increased the δ and χ difference between components A and B by 10.4% and 15.8%, respectively. • 0.2 wt% graphene oxide modified oil compatibilizers achieved comparable effects to 30 wt% oil-based compatibilizers. • GOESO and GOSO enhance compatibility by changing the curing reaction rate and the microstructures. • The oil with epoxy groups possibly had a strong capability of compatibility enhancement. [ABSTRACT FROM AUTHOR]

High temperature and oxidation are two of the most critical factors that cause epoxy asphalt aging. This paper aims to clarify the variation of mechanical performance and structure of effect of cold-mixed epoxy asphalt (CEA) after thermal-oxidative (TO) aging. The mechanical properties of CEA were studied by tensile tests and dynamic mechanical analysis. The microstructure of CEA was studied by Fourier transform infrared spectrum, X-ray photoelectron spectroscopy, SEM, and fluorescence microscopy. The results indicated that the tensile strength of CEA increased to 5.16 MPa, the elongation at break decreased to 50.3%, and the T g decreased significantly after TO aging. TO aging made the epoxy resin in CEA post-cure, oxidate, degrade and the cross-linked network break. Furthermore, the asphalt particles in CEA agglomerated and oxidized. [Display omitted] • ER underwent a post-curing reaction and degradation. • Asphalt underwent volatilization of the light components and an oxidation reaction. • Thermal-oxidative aging destroyed the original phase structure of the CEA. [ABSTRACT FROM AUTHOR]