Search

Abstract: Recently membrane distillation (MD) has received intensive interests for a range of applications such as desalinations of seawater and brine. One of the major obstacles for MD application is the lack of an optimized MD membrane that can produce a high and stable flux in long-term operation. Two types of superhydrophobic PVDF nanofiber membranes, integrally-modified and surface-modified PVDF membranes, have been successfully fabricated by electro-spinning followed by surface modification, which includes dopamine surface activation, silver nanoparticle deposition and hydrophobic treatment. The modification is convenient because of mild reactions and wide applicability. These novel composite nanofiber membranes have been characterized by a series of measurements and benchmarked against commercial PVDF flat sheet membrane for MD application. The characterizations reveal that the modifications have altered the membrane surface morphology and topology and made the membrane superhydrophobic due to their hierarchical structures. Compared with unmodified membrane, the integrally-modified membrane (I-PVDF) can achieve a high and stable MD water flux of 31.6Lm−2 h−1 using a 3.5wt% NaCl as the feed solution while the feed and permeate temperatures were fixed at 333K and 293K, respectively. To the best of our knowledge, this result is superior to all other PVDF flat-sheet membranes tested under the same or similar conditions, which is believed to be attributed to the open-surface pore structure and thin thickness of the PVDF nanofiber membrane with the aid of electro-spinning. The superhydrophobic nature of the membrane surface brought by the integral modification on all nanofibers renders the membrane anti-wetting property while remaining high water flux. [Copyright &y& Elsevier]

Abstract: The main challenges for membranes used in membrane distillation (MD) are well-designed porous structure and hydrophobic surface property. Hydrophobic nanofiber membranes possess high hydrophobicity, high surface porosity and adjustable pore sizes and membrane thickness, which make them an attractive candidate as MD membrane. The current study aims to fabricate and optimize polyvinylidene fluoride (PVDF) nanofiber membranes for MD application. Scanning electron microscopy (SEM), capillary flow porometer, geniometer, a homemade setup for liquid entry pressure (LEP) measurement and direct contact MD (DCMD) setup were used to characterize the resultant nanofiber PVDF membranes. Polymer dope compositions, spinning parameters such as sprayer moving speed and chamber moisture were optimized to examine their effects on pore size distribution of the membranes. Inorganic additives were also added into the dope to improve the electro-spinability of diluted polymer dopes in order to further decrease membrane pore size. Meanwhile, a heat-press post-treatment was considered as a necessary step to improve fresh nanofiber membrane integrity, enhance water permeation flux and help prevent membrane pores from wetting in DCMD operation. The experiment confirmed that all the electrospun membranes exhibit a rough surface with high hydrophobicity (>135° water contact angle). The post-treated PVDF nanofiber membranes were able to present a steady water permeation flux of about 21kgm−2 h−1 throughout the entire testing period of 15h, using a 3.5wt% NaCl solution as the feed under the feed and permeate inlet temperatures of 323K and 293K, respectively. This result was better than these of commercial PVDF membranes and the nanofiber PVDF-clay membrane reported in literature, suggesting the competency of PVDF nanofiber membranes for DCMD applications. [Copyright &y& Elsevier]