Search

Abstract: One of the major barriers that hinder the application of forward osmosis (FO) processes is the lack of optimized membranes that possess high water flux, low salt leakage and good anti-internal concentration polarization (ICP) and anti-fouling/anti-scaling properties during practical FO operations. In this study, novel composite FO hollow fiber membranes with an RO-like selective skin and an NF-like secondary selective skin were successfully developed for the first time. The fabrication procedures involved making ultrafiltration hollow fiber substrate using poly(amide–imide) (PAI) polymer material via phase inversion method, followed by interfacial polymerization (IP) and chemical modification to yield a polyamide RO-like inner skin and a positively charged NF-like outer skin, respectively. It was found that the sequence of conducting IP on the substrate inner surface prior to the chemical modification of the outer skin was preferred in order to achieve better performance for the resultant double-skinned hollow fibers. The newly developed FO hollow fibers exhibited high water permeability of 2.05L/m2 hbar and 85% rejection to NaCl at 1bar pressure as well as superior FO water flux of 41.3L/m2 h and low ratio of salt flux over water flux of 0.126g/L when using DI water and 2.0M NaCl as feed and draw solutions, respectively, in the active layer facing draw solution (AL-DS) orientation. Furthermore, the experimental results showed that the composite FO hollow fiber membrane was able to outperform single-skinned membrane when the feed contains divalent ions or the feed exhibits high scaling tendency to membrane. This suggested that the integration of RO- and NF-like two selective skins in FO membrane is an effective way to minimize the ICP effect, mitigate the membrane scaling and thus enhance the feasibility of FO processes for practical applications. [Copyright &y& Elsevier]

Abstract: Composite nanofiltration (NF) hollow fiber membranes desirable for water softening under low operating pressure (<2bar) were successfully developed in the current study. The thin-film selective layer of the composite hollow fiber was formed through interfacial polymerization on the inner surface of a polyethersulfone (PES) ultrafiltration (UF) membrane substrate with branched polyethyleneimine (PEI) and trymesoyl chloride (TMC) employed as the monomers in aqueous and organic phases, respectively. It is found that a proper molecular weight of PEI and the presence of sodium dodecyl sulfate (SDS) in the aqueous phase are important for a successful interfacial polymerization reaction. The resulting membrane prepared with optimized preparation parameters possesses a positively charged thin-film selective layer with pure water permeability (PWP) of about 17l/m2 hbar and a molecular weight cut-off (MWCO) of around 500Da, which translates into the effective pore diameter of about 1.29nm. With combined separation mechanisms of Donnan exclusion and steric hindrance, it was possible to achieve MgCl2 and MgSO4 rejection of 96.7% and 80.6%, respectively, when tested for 1000ppm feed solutions at 2bar operating pressure. In addition, for a 3000ppm TDS feed stream containing salt mixtures, the membrane rejections for Mg2+ and Ca2+ ions were found to be around 90% while the water flux was about 20l/m2 h at 2bar pressure, suggesting the potential of the newly developed composite hollow fibers for effective water softening application. [Copyright &y& Elsevier]