Search

• Difference of damage modes caused by the boundary conditions of primary load-bearing yarns. • Straightening effect of braided yarns with undulations under low-velocity impact. • Variation of off-axial angles leading to the transition of failure modes. The sensitivity of off-axial angle on impact response was investigated by experimental and numerical methods in this work. Three types of braided laminates with different on/off-axial angles in terms of OA00, OA225 and OA45 were prepared and low-velocity impact tests with various energy levels were performed. Meso-level finite element model (FEM) was also developed to reveal impact damage initiation and development. We discovered that the boundary condition of primary load-bearing yarns depending on the off-axial angles caused the difference of structural deformation and stress distribution of braiding yarns during impact process. Due to the restriction of the pressurized tips, the straightening effect of primary load-bearing yarns with heavy waviness caused its out-of-plane movement and related main cracks in OA00 specimen. In addition, the matrix resin cracks were found at the edge of the specimen because of in-plane shear movement of braiding yarns. As for OA45 specimen, more evident bending deformation was observed, resulting in elevated tensile stress of braiding yarns on non-impact side. The variation of off-axial angle from 0 to 45 degree led to the failure mode transforming from the extensive matrix damage on specimen edge to the severe fiber breakage on non-impact side. As a medium off-axial angle, OA225 specimen exhibited a mixture failure mode to resist impact and achieved excellent performance with respect to higher peak force and delayed load dropping. [Display omitted] [ABSTRACT FROM AUTHOR]

In this work, the synergistic effect of 3D orthogonal woven structure and asymmetric carbon/glass hybridization on impact response was studied by experimental and numerical methods. The hybrid 3D orthogonal woven (H3DOW) composite plates were manufactured on a home-made 3D weaving machine. Impacts with various energies 42.9, 54.9, 66.9 and 78.9 J were applied to carbon (CG) and glass (GC) sides. The impact response was examined using fracture morphology observation and mechanical curves. Yarn-level finite element models including failure criteria and progressive damage law were established in ABAQUS/Explicit to compare the structural deformation and damage behavior. The impact side significantly influences the failure modes of H3DOW materials. GC specimen failed through delamination between carbon layers at non-impact side and subsequent fiber tensile breakage, whereas the crushing damage in the carbon yarn located in the impact-side and large area debonding between yarn and matrix resin in superficial layers was the dominant failure mode in CG specimen. This caused the CG configuration to exhibit better impact resistance with respect to the perforation threshold energy. [ABSTRACT FROM AUTHOR]

• The structural hybridization effect on low-velocity impact response of braided/unidirectional (UD) laminates was investigates. • Continuum shell finite element models based on the anisotropic constitutive relationship of braided and UD plies were established to reveal the damage onset and propagation. • The extensive delamination formed rapidly when impacted on the fabric side. • The damage characterized by severe fiber breakage occurs at the impact site when impacted on UD ply side. This work investigated the structural hybridization effect on the low-velocity impact response of braided/unidirectional(UD) laminate. Two groups of hybridization laminates, namely interleaving and clustering groups, were manufactured. The impact performance of the specimens was characterized by combining dropping testbench, optical camera and ultra-sound detector. A continuum shell finite element model was established to reveal the progressive damage behavior of hybridization laminate. The specimen in the interleaving group presented overwhelming performance than that in the clustering group. The impact side effect on failure modes was discussed in detail. When impacted on the braided fabric side, extensive delamination formed on the edge of the specimen due to bending deformation. It further resulted in-plane crushing failure of UD sub-laminate. In contrast, severe fiber breakage occurs at the impact site due to combination stress of tensile and shear when impacted on UD side. Therefore, the fabric-impacted specimen exhibits better impact resistance than that impacted on UD side with respect to higher peak load and lower absorbed energy. [Display omitted] [ABSTRACT FROM AUTHOR]