The absorption spectra, emission under 940 nm excitation by laser diode, and fluorescence lifetimes of as-grown and annealed Cr,Yb:YAG crystal have been investigated at room temperature. The increase of absorption coefficients at 941 and 1030 nm and the quenching of Yb3+ emission intensity and fluorescence lifetime after annealing are due to the increase of the concentration of Cr4+ ions. The data of thermal expansion and specific heat of the crystal have been measured. The thermal expansion coefficient is α=8.71×10−6 /K. The specific heat is 89.9 cal/mol K at 320.5 K. [Copyright &y& Elsevier]

Abstract: Gd2SiO5 (GSO) single crystal codoped with Yb3+ and Er3+ (Abbr. as Er:Yb:GSO) was successfully grown by the Czochralski (CZ) method for the first time and the spectral characteristics were investigated. The absorption and fluorescence spectra were measured. The emission lifetime of the 4I13/2–Er-level was measured to be 5.84ms and the emission cross-section at 1529nm was calculated to be 1.03×10−20 cm2. The results indicate that Er:Yb:GSO is a potential laser material at ∼1.55μm wavelength region. [Copyright &y& Elsevier]

High-quality Dy:PbWO 4 crystal has been successfully grown by the Bridgman method. Fluorescence properties of the grown crystal at the yellow-light region were discussed. The absorption cross-section of Dy3+ ions at 454 nm was calculated to be 0.142 × 10−20 cm2, which corresponded to the transition from 6H 15/2 to 4I 15/2 level. Based on Judd-Ofelt theory, the J-O intensity parameters Ω t and the emission cross-section were calculated. The fluorescence lifetime of 4F 9/2 level was measured to be 193 μs. • Dy: PbWO 4 crystal was grown successfully by the Bridgman method. • Judd-Ofelt theory was used to analyze the spectral properties of Dy: PbWO 4 for the first time. • Dy: PbWO 4 crystal is a potential laser medium for yellow laser operation. [ABSTRACT FROM AUTHOR]

The high optical quality Er:Lu 2 O 3 and Er,Pr:Lu 2 O 3 crystals were grown by Floating zone method. The spectral properties of Er:Lu 2 O 3 and Er,Pr:Lu 2 O 3 crystals were investigated. After co-doping small concentration of Pr3+, the depopulated influence of Pr3+ to the NIR emission was much stronger than the MIR emission. The near-infrared and up-conversion fluorescence were significantly quenched. Moreover, the fluorescence lifetime of 4I 13/2 abviously decreases from 4.02 ms to 1.71 ms in 7% Er, 0.05% Pr: Lu 2 O 3 crystal, and the lifetime ratio is 1.63 with large fluorescence lifetime of 4I 11/2 which is desirable lifetime ratio in these crystals. Thus, the spectral performance was significantly improved by co-doping 0.05 at.% of Pr3+. The high laser performance at 2.7 μm of 7% Er, 0.05% Pr: Lu 2 O 3 crystal is expectable. • The high optical quality Er:Lu 2 O 3 and Er,Pr:Lu 2 O 3 crystals were firstly grown by Floating zone method. • The spectral properties of Er:Lu 2 O 3 and Er,Pr:Lu 2 O 3 crystals were firstly investigated. • After co-doping low concentration of Pr3+, the near-infrared, ESA and up-conversion fluorescence were significantly quenched. • The spectral performance of Er:Lu 2 O 3 crystal was significantly improved at 2.7 μm by co-doping 0.05 at.% of Pr3+. [ABSTRACT FROM AUTHOR]