Abstract: Optical properties of PbS quantum dots (QDs) precipitated inside the oxide glass matrix were investigated. Photoluminescence (PL) from the PbS QDs showed peak wavelengths located at 1170–1680nm with widths of 150–550nm. Radii of QDs in glasses were 2.3–4.7nm depending upon the thermal treatment. Peak wavelengths of PL bands shifted as much as 70nm as the temperatures and excitation irradiances increased. Calculated effective local temperatures indicated that these shifts of PL spectra were associated with local heating induced by the temperatures and laser beam. [Copyright &y& Elsevier]

• Adjusting optical performance of PbS QDs embedded glass to cover the whole telecommunication bands. • Revealing the absorption cross sections of PbS QDs at 1040 nm are 4–13 × 10−16 cm2, the bi- and tri-excitons lifetime is ∼60 and ∼10 ps. • Obtaining the broadband net gain in 1500–1620 nm in single PbS QDs embedded glass with a threshold of < N >=4.1. • Achieving a maximum gain time of ∼20 ps and gain coefficient of >120 cm−1 for PbS QDs embedded glass. Lead sulfide quantum dots (PbS QDs) have a unique performance in the near-infrared (NIR) range. In-situ precipitation of PbS QDs in glass not only improves the stability, but also is easy to be fabricated fiber compatible with silicon photonics. In this work, we reveal that absorption cross sections of PbS QDs at 1040 nm are 4–13 × 10−16 cm2, the bi- and tri-excitons lifetime are∼60 and ∼10 ps due to the trap-assisted Auger recombination using transient absorption (TA). Furthermore, we demonstrate the broadband net gain in 1500–1600 nm in single PbS QDs embedded glass with a gain threshold of < N >= 4.1 (averaged number of excitons), and achieve the maximum gain time of ∼20 ps and gain coefficient of >120 cm−1. These results illustrate the existing obstacles to achieve the net gain in PbS QDs embedded glass, which is important for applications on fiber amplifiers, NIR laser and high-capacity telecommunication. [ABSTRACT FROM AUTHOR]

Abstract: The size and spatial distribution of PbS QDs in glasses need to be controlled in order to achieve desired optical characteristics. This paper reports on the use of several rare-earth oxides such as Ho2O3, Er2O3, and La2O3 to control the size of PbS QDs in silicate glasses. Additions of rare-earth oxides result in blue shifts of the absorption bands from 1344nm to 930nm, and the wavelengths of PL bands can be controlled between 1421nm and 1035nm. Additions of up to 0.8mol% of Ho2O3 decreased the diameters of PbS QDs from 4.82nm to 3.02nm. The same tendencies were found for both Er2O3 and La2O3 additions, although the size of PbS QDs increased as the ionic radius of rare-earth ions increased. It is proposed that clusters of RE–O bonds act as nucleating agents for the precipitation of PbS QDs. [Copyright &y& Elsevier]