Search

Abstract: Delamination-free ultrafiltration (UF) dual layer hollow fibers have been successfully fabricated by dry jet-wet spinning technique. Two different polymers of poly(amide-imide) (PAI) and polyethersulfone (PES) were utilized as the selective layer on the outer side and the porous support layer on the inner side, respectively. The dual layer substrates were subsequently modified to develop a nanofiltration (NF)-like skin on the outer layer by polyethyleneimine (PEI) cross-linking followed by multilayer polyelectrolyte depositions. These membranes were characterized by a series of standard protocols in terms of membrane structure, permeability and salt rejection, and were applied in FO process. Experiments reveal that the dual-layer NF hollow fiber modified by polyelectrolyte cross-linking and depositions can achieve pure water permeability of 4.1l/m2.h.bar and a high rejection to MgCl2 up to 97%. In FO process, the dual-layer hollow fibers exhibited a water flux of 39 and 21lm−2 h−1 in the orientations of active layer facing draw solution and feed water, respectively, by using 0.5M MgCl2 as draw solution and de-ionized (DI) water as feed at room temperature. It suggests that the combined treatment of polyelectrolyte cross-linking and deposition is an effective way to form a NF-like selective layer for FO dual-layer hollow fiber membranes. [Copyright &y& Elsevier]

Abstract: A new type of forward osmosis (FO) hollow fiber membranes with an antifouling nanofiltration (NF)-like selective layer has been developed in this work. The fabrication involves a step of porous poly(amide-imide) (PAI) ultrafiltration (UF) hollow fiber spinning via phase inversion, followed by simple polyelectrolyte post-treatments using positively charged polyethyleneimine (PEI) for cross-linking and negatively charged polystyrene sulfonate sodium salt (PSS) for deposition. The membranes are subsequently characterized by a series of standard protocols and evaluated in FO process. The PAI FO membranes possess a pure water permeability of 3.7–4.3Lm−2 h−1 bar−1 and Na2SO4 rejections up to 85% at 1bar. In the FO process, the membranes can achieve water flux of 17 and 12Lm−2 h−1 for active layer facing draw solution (AL-facing-DS) and active layer facing feed water (AL-facing-FW) configurations, respectively, using a 2000ppm Na2SO4 aqueous solution as the feed and 0.5M Na2SO4 as the draw solution. When the feed contained 1000ppm bovine serum albumin (BSA) and 2000ppm Na2SO4, a steady water flux of 11Lm−2 h−1 can be maintained using 0.5M Na2SO4 as the draw solution at ambient temperature of 23°C. The approach of making FO membranes developed in the present study offers the advantages of simple fabrication process, tailorable selective layer and promising membrane performance for protein-contained wastewater treatment by FO process. [Copyright &y& Elsevier]

Abstract: Hollow fiber membranes with a positively charged nanofiltration (NF)-like selective layer have been successfully fabricated by utilizing asymmetric microporous hollow fibers made of Torlon® polyamide–imide (PAI) material as the porous substrate followed by polyelectrolyte post-treatment using polyethyleneimine (PEI), which has not been reported previously. The reaction between PAI and PEI has been confirmed by experiments. The membrane structure and surface property are carefully tailored by adjusting polymer dope composition, spinning conditions and the post-treatment parameters. These membranes are, subsequently, characterized by a series of standard protocols in terms of membrane morphology, structure, permeability and salt rejection, and are applied in forward osmosis (FO) processes. The newly developed PAI hollow fiber membranes show a pure water permeability of 2.19–2.25L/m2 hbar and reasonable NaCl and MgCl2 rejections of 49% and 94% at 1bar, respectively. It is also found that in FO processes, when using 0.5M MgCl2 as a draw solution and DI water as the feed in the active layer facing feed water (AL-facing-FW) configuration at 23°C, the water fluxes of two PAI FO hollow fiber membranes are 8.36 and 9.74L/m2 h, respectively, and the J S /J V of the two membranes is smaller than 0.4g/L, which is lower than the data of 0.85g/L for commercial FO membrane from Hydration Technologies Inc. (HTI). Different from a neutral membrane, the positively charged FO membrane provides double electric repulsions to the salt transfer through the membrane in the AL-facing-FW configuration, leading to a reduction of salt penetration, while in the active layer facing draw solution (AL-facing-DS) configuration, the positive charges facilitate salt transportation. This study provides a simple and effective approach to make hollow fibers suitable for FO applications. [Copyright &y& Elsevier]

The layer-by-layer (LBL) polyelectrolyte deposited membranes have drawn increasing attention in various applications due to the ease of selective layer formation and their stability and versatility. In this study, the LBL deposition was performed at the inner surface of the polyethersulfone (PES) hollow fiber substrate to form composite nanofiltration (NF) membrane. The semi-dynamic deposition procedure was adopted with the aid of syringes. The newly developed inner deposited (id-LBL) membranes were then tested in NF and forward osmosis (FO) applications and the performance were compared with outer surface deposition as well as some literature data. The id-LBL membranes could not only withstand higher operating pressure but also possess superior hardness rejection especially in high concentration mixed salt solutions (more than 95% rejection to Mg 2+ and Ca 2+ in a 5000 ppm total dissolved salt (TDS) mixture under 4.8 bar). As for the FO process, with only two layer deposition, the id-LBL membranes also demonstrated significant performance improvement with increased water flux (up to 70 L/m 2 h using 0.5 M MgCl 2 as draw solution in active layer facing draw solution configuration) and reduced salt leakage (around 0.5 g/m 2 h using 1 M MgCl 2 draw solution in active layer facing feed water configuration). This study suggests that for hollow fiber substrate, the inner surface is more suitable for the formation of the selective layer via LBL deposition than the outer surface. [ABSTRACT FROM AUTHOR]