To understand the interface effects between human gingival fibroblasts (HGFs) and the titanium substrate for soft tissue sealing, zinc (Zn) was incorporated into titanium by plasma immersion ion implantation (PIII) in the work, and the durations of 30, 60 and 90 min were adopted for serials of Zn content on titanium to identify the possible dose-effect relationship. Results showed that the implanted Zn formed metallic Zn and zinc oxide on the surface, and the Zn content increased with the extension of implantation time. The release of Zn ions occurred in the saline solution, but the amounts of released ions were inconsistent with the Zn content of implanted samples and their corrosion behaviors, indicating the different reaction activities among the sample surfaces. Moreover, in vitro studies disclosed that the incorporated samples were beneficial to the adhesion, proliferation, and migration of HGFs with appropriate dose of released Zn ions as well as the surface activities, as the fact it was not a directly proportional dose-effect relationship between released Zn ions and the behaviors of cells. It was suggested that Zn-PIII provided an approach to improve the soft tissue sealing of titanium through interfacial activities of implanted samples to regulate the behaviors of HGFs and the usage of Zn ions followed a synergistic manner. The interface effects of Zn-PIII titanium on the behaviors of human gingival fibroblasts relied on the implanted time. Unlabelled Image • Zn implanted titanium regulated the behaviors of HGFs through interface effects. • The surface activities of Zn-PIII samples were affected by the implantation time. • HGFs behaviors were not in a proportional dose-effect relation with released ions. [ABSTRACT FROM AUTHOR]

Abstract: Zinc (Zn) and silver (Ag) are co-implanted into titanium by plasma immersion ion implantation. A Zn containing film with Ag nanoparticles (Ag NPs) possessing a wide size distribution is formed on the surface and the corrosion resistance is improved due to the micro-galvanic couples formed by the implanted Zn and Ag. Not only are the initial adhesion, spreading, proliferation and osteogenic differentiation of rBMSCs observed from the Zn/Ag implanted Ti in vitro, but also bacteria killing is achieved both in vitro and in vivo. Electrochemical polarization and ion release measurements suggest that the excellent osteogenic activity and antibacterial ability of the Zn/Ag co-implanted titanium are related to the synergistic effect resulting from the long-range interactions of the released Zn ions and short-range interactions of the embedded Ag NPs. The Zn/Ag co-implanted titanium offers both excellent osteogenic activity and antibacterial ability and has large potential in orthopedic and dental implants. [Copyright &y& Elsevier]