Search

• The reduced TiO 2 coatings were fabricated by MAO and further H-PIII. • After H-PIII, the coatings had more Ti-OH bonds and O V. • The formation of Ti-OH bonds promoted cell osteogenic differentiation. • The O V endowed the coatings with enhanced bacteriostatic effects. Titanium implants fabricated by micro-arc oxidation (MAO) are widely used in orthopedic therapies. However, TiO 2 is a bio-inert material and lacks antibacterial properties. Therefore, it is crucial to enhance the biological activity and antibacterial properties of MAO implants. In this work, TiO 2 coatings were fabricated by MAO and further hydrogen plasma immersion ion implantation (H-PIII). The formation of Ti-OH bonds promoted cell proliferation and osteogenic differentiation. The presence of Ti3+ and oxygen vacancies narrowed the forbidden band of TiO 2 and showed bacteriostatic effect to E. coli and S. aureus. [ABSTRACT FROM AUTHOR]

As a promising implantable material, poly ether ether ketone (PEEK) possesses similar elastic modulus to that of cortical bones yet suffers from bio-inertness and poor osteogenic properties, which limits its application as orthopedic implants. In this work, calcium is introduced onto PEEK surface using calcium plasma immersion ion implantation (Ca-PIII). The results obtained from scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS) confirm the modified layer with varying contents of calcium are formed on PEEK surfaces. Water contact angle measurements reveal the increasing hydrophobicity of both Ca-PIII treated surfaces. In vitro cell adhesion, viability assay, alkaline phosphatase activity and collagen secretion analyses disclose improved the adhesion, proliferation, and osteo-differentiation of rat bone mesenchymal stem cells (bMSCs) on Ca-PIII treated surfaces. The obtained results indicate that PEEK surface with enhanced osteogenic activity can be produced by calcium incorporation. [ABSTRACT FROM AUTHOR]

Si-incorporated TiO 2 nanopores films were prepared by anodization and silicon plasma immersion ion implantation. The microstructure and phase composition of the films were investigated by scanning electron microscopy, X-ray diffraction and X-ray photoelectron spectroscopy. The hydrophilicity of the films was evaluated using water contact angle measurement and MG63 cells were cultured on the films to investigate the cytocompatibility. The results showed that the concentration and depth of silicon on the Si-incorporated TiO 2 nanopores films increased with the duration time of implantation. Both the as-annealed and Si-incorporated nanopores films exhibited good hydrophilicity and cytocompatibility, while the TiO 2 nanopores films implanted silicon for 1.0 h showed higher proliferation rate and vitality of MG63 cells than others, indicating a great potential application for titanium implants. [ABSTRACT FROM AUTHOR]

Silicon incorporated titania (Si–TiO2) films were prepared on titanium substrates by plasma immersion ion implantation and deposition (PIII&D) using filtered Ti and Si cathodic arc sources in oxygen atmosphere. The as-deposited films were further annealed at 400°C, 600°C and 800°C for 2h in air. The microstructure and phase composition of the films were investigated by field emission scanning electron microscopy, atomic force microscopy, X-ray diffraction, X-ray photoelectron spectroscopy and Raman spectroscopy. The hydrophilicity of the film was illustrated using water contact angle measurement and the in vitro bioactivity was evaluated by simulated body fluid immersion test. Pure titania (TiO2) film was also parallelly studied for comparison. The results show that the grain size of TiO2 and Si–TiO2 films increases and their hydrophilicity is enhanced with the increase of annealing temperature, while the Si–TiO2 film exhibits smaller grain and better hydrophilicity than TiO2 film. The bioactivity of the Si–TiO2 film is also better than that of TiO2 film. Moreover, the 600°C-annealed Si–TiO2 film possesses best bioactivity, which is thought to result from the existence of anatase phase and nanoscale grains. [ABSTRACT FROM AUTHOR]

Polyetheretherketone (PEEK) possesses a similar elastic modulus as bones but yet suffers from bio-inertness and poor osteogenesis. In this work, tantalum ions are implanted energetically into PEEK by plasma immersion ion implantation (PIII) to form Ta 2 O 5 nanoparticles in the near surface. Nanoindentation reveals that the surface elastic modulus of the Ta ion implanted PEEK is closer to that of human cortical bones. In vitro cell adhesion, alkaline phosphatase activity, collagen secretion, extracellular matrix mineralization, and real-time PCR analyses disclose enhanced adhesion, proliferation, and osteogenic differentiation of rat bone mesenchymal stem cells (bMSCs) on the Ta-PIII modified PEEK. In vivo evaluation of the cortico-cancellous rat femur model by means of micro-CT, sequential fluorescent labeling, and histological analysis after 8 weeks confirms significantly improved osteointegration. The bone-like elastic modulus and modified surface topography of the Ta-PIII modified PEEK synergistically induce osteogenic differentiation of bMSCs and the surface-modified materials have large potential in dental and orthopedic implants. [ABSTRACT FROM AUTHOR]

Abstract: As an implantable material, carbon-fiber-reinforced polyetheretherketone (CFRPEEK) possesses an adjustable elastic modulus similar to that of cortical bone and is a prime candidate to replace metallic surgical implants. However, the bioinertness and poor osteogenic properties of CFRPEEK limit its clinical application as orthopedic implants. In this work, titanium ions are introduced energetically into CFRPEEK by plasma immersion ion implantation (PIII). Scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS) reveal the formation of nanopores with the side wall and bottom embedded with ∼20 nm TiO2 nanoparticles on the CFRPEEK surface. Nanoindentation measurements confirm the stability and improved elastic resistance of the structured surfaces. In vitro cell adhesion, viability assay, and real-time PCR analyses disclose enhanced adhesion, proliferation, and osteo-differentiation of rat bone mesenchymal stem cells (bMSCs). The multilevel structures on CFRPEEK also exhibit partial antibacterial activity to Staphylococcus aureus and Escherichia coli. Our results indicate that a surface with multifunctional biological properties can be produced by multilevel surface engineering and application of CFRPEEK to orthopedic and dental implants can be broadened and expedited based on this scheme. [Copyright &y& Elsevier]

To understand the interface effects between human gingival fibroblasts (HGFs) and the titanium substrate for soft tissue sealing, zinc (Zn) was incorporated into titanium by plasma immersion ion implantation (PIII) in the work, and the durations of 30, 60 and 90 min were adopted for serials of Zn content on titanium to identify the possible dose-effect relationship. Results showed that the implanted Zn formed metallic Zn and zinc oxide on the surface, and the Zn content increased with the extension of implantation time. The release of Zn ions occurred in the saline solution, but the amounts of released ions were inconsistent with the Zn content of implanted samples and their corrosion behaviors, indicating the different reaction activities among the sample surfaces. Moreover, in vitro studies disclosed that the incorporated samples were beneficial to the adhesion, proliferation, and migration of HGFs with appropriate dose of released Zn ions as well as the surface activities, as the fact it was not a directly proportional dose-effect relationship between released Zn ions and the behaviors of cells. It was suggested that Zn-PIII provided an approach to improve the soft tissue sealing of titanium through interfacial activities of implanted samples to regulate the behaviors of HGFs and the usage of Zn ions followed a synergistic manner. The interface effects of Zn-PIII titanium on the behaviors of human gingival fibroblasts relied on the implanted time. Unlabelled Image • Zn implanted titanium regulated the behaviors of HGFs through interface effects. • The surface activities of Zn-PIII samples were affected by the implantation time. • HGFs behaviors were not in a proportional dose-effect relation with released ions. [ABSTRACT FROM AUTHOR]

Abstract: Zinc (Zn) and silver (Ag) are co-implanted into titanium by plasma immersion ion implantation. A Zn containing film with Ag nanoparticles (Ag NPs) possessing a wide size distribution is formed on the surface and the corrosion resistance is improved due to the micro-galvanic couples formed by the implanted Zn and Ag. Not only are the initial adhesion, spreading, proliferation and osteogenic differentiation of rBMSCs observed from the Zn/Ag implanted Ti in vitro, but also bacteria killing is achieved both in vitro and in vivo. Electrochemical polarization and ion release measurements suggest that the excellent osteogenic activity and antibacterial ability of the Zn/Ag co-implanted titanium are related to the synergistic effect resulting from the long-range interactions of the released Zn ions and short-range interactions of the embedded Ag NPs. The Zn/Ag co-implanted titanium offers both excellent osteogenic activity and antibacterial ability and has large potential in orthopedic and dental implants. [Copyright &y& Elsevier]