Search

Abstract  In this study, Scots pine sapwood (Pinus sylvestris L.) and Douglas fir heartwood (Pseudotsuga menziesii Franco) specimens were exposed in double layer field trials at four different exposure sites and under different exposure conditions (in total ten test sets). The material climate of wood in terms of wood moisture content (MC) and wood temperature was automatically monitored over a period of 6 years and compared with the progress of decay. The aim of this study was to highlight the interrelationship between microclimate, material climate, and decay as a basis for the establishment of dose-response functions to be used for service life prediction of wood and wood-based products. Differences in resulting decay dynamics between the test sites as well as between the different types of exposure were quantified and discussed with respect to corresponding microclimatic and material climatic conditions. The time between the beginning of exposure and the first occurrence of visible decay varied between the sites and influenced the total decay development. The fundamental importance of direct decay factors, such as MC and wood temperature, were underlined and basic requirements for establishing dose-response-functions to be used in service life prediction models were derived. [ABSTRACT FROM AUTHOR]

Abstract  Scots pine sapwood (Pinus sylvestris L.) and Douglas fir heartwood (Pseudotsuga menziesii Franco) specimens were exposed in double layer field trials at 23 different European test sites under different exposure conditions (in total 27 test sets). The material climate in terms of wood moisture content (MC) and wood temperature was automatically monitored over a period of up to 7 years and compared with the progress of decay. The overall aim of this study was to establish dose–response relationships between climate factors and decay as a basis for the service life prediction of wood. The “Scheffer Climate Index” based on weather data collected at official meteorological stations at the different test sites poorly correlated with the corresponding decay progress and was therefore not a suitable tool for estimating site-specific decay potential. In contrast, the use of the combined material climatic parameters MC and wood temperature led to a feasible dose–response function and turned out to be a useful basis for service life prediction of wood. [ABSTRACT FROM AUTHOR]

The suitability of a previously described high-energy multiple impact (HEMI) test for the detection of early fungal decay was examined. The HEMI test characterises the treatment severity of thermally modified wood by stressing the treated material by thousands of impacts of pounding steel balls. This method differentiates between heat treatment intensities, which are manifest as structural changes in the wood. Similar changes in wood structure are known for wood decayed by fungi. Pine (Pinus sylvestris L.) decayed by brown rot and beech (Fagus sylvatica L.) decayed by white rot were tested. Mass loss caused by fungal decay and resistance to impact milling (RIM) determined in HEMI tests were found to be highly correlated. Testing of non-degraded pine, beech, and ash (Fraxinus exelsior L.) showed only marginal effects of wood density on RIM. Furthermore, annual ring angles and RIM of spruce (Picea abies Karst.) were not correlated. Accordingly, the detection of RIM reduction in decayed wood is not masked by variations in density and orientation of the annual rings. Previous results showed no adverse effects of weathering on RIM. Thus, the detection of fungal decay with HEMI tests is feasible not only for laboratory purposes, but also for wood in outdoor applications that has already undergone weathering. [ABSTRACT FROM AUTHOR]

Thermal modification processes improve the durability and dimensional stability of wood, but strength properties, especially dynamic ones, are compromised. Results from standard dynamic strength testing, such as impact bending tests, suffer from high variability and therefore require a high number of replicates. To overcome this, a new test method named high-energy multiple impact (HEMI) was developed by investigating heat-treated Picea abies Karst., Abies alba Mill. and untreated Robinia pseudoacacia L. The method is based on crushing small specimens by thousands of impacts from pounding steel balls in a heavy vibratory mill. The level of destruction was determined by sieving and analyzing the size distribution of the fragments. We calculated the resistance to impact milling (RIM) based on the mass of the size fractions. RIM shows a linear correlation with the intensity of the thermal treatment. The HEMI test method has the following advantages: small number of specimens, short time for specimen preparation, small variances, and high reproducibility of results. [ABSTRACT FROM AUTHOR]

AbstractThere is increasing awareness of the durability, dimensional stability, and strength properties of thermally modified timber products. Appropriate standards and test methods for industrial-scale quality control are needed. The aim of this study was to investigate the suitability of CIE L*a*b* color measurements for implementation in industrial quality control. Good linear correlation was found between a cumulated measure of L* and b* data and the heat treatment intensity for spruce (Picea abiesKarst.), pine (Pinus sylvestrisL.), and beech (Fagus sylvaticaL.). Wood samples homogenized by milling revealed less variation in color values compared to wood surface measurements. Thus, measurements on milled wood are recommendable to obtain results with high statistical significance. Color measurements are rapid, precise, and highly reproducible. Based on the strong correlation between color data and heat-treatment intensities, color measurements could easily be implemented for quality control of thermally modified timber. [ABSTRACT FROM AUTHOR]

AbstractThe occurrence of fungal species on pine sapwood samples obtained from an above-ground field test study was analysed by terminal restriction fragment length polymorphism (T-RFLP), cloning, and sequencing. Samples were taken from eight double-layer set-ups that were exposed to the environment at six different locations in south-west Germany. The occurrence of fungal species was correlated with decay intensity and rot types on one hand, and characteristics of the test sites, such as precipitation, average temperature and height above sea level on the other hand. In total, 62 different fungal species were found based on T-RFLP, cloning and sequencing. Of the 39 species that were found four or more times, 30 were ascomycetes, five were basidiomycetes, and four could not be classified. The most common fungus found in this study was Coniochaeta ligniaria((Grev.) Cooke), a soft rot fungus that occurred in 87 of 152 samples (57%). No single factor at the test sites seemed to be decisive for the abundance of fungal species or decay intensity. Within the first years of this study, soft rot fungi was found more frequently in pine sapwood specimens than basidiomycetes. [ABSTRACT FROM AUTHOR]

AbstractGamma irradiation, which is an easy, fast and effective method for wood sterilisation, changes molecular structures not only in pest cells, but also in wood cell walls. Radiation-induced depolymerisation causes significant changes in some properties of wood crucial for restoration and for laboratory testing of wood-preservative effectiveness, as demonstrated by experimental data. The influence of gamma radiation on maximum swelling (αMAX), resistance to impact milling (RIM), and the total amount of water-soluble carbohydrates (TSC) was investigated. Cobalt (60Co) was used as a gamma source and Scots pine wood (Pinus sylvestrisL.) was irradiated at doses of 30, 90 and 150 kGy. A strong linear correlation was found between TSC and radiation dosage. Leached irradiated specimens showed significantly greater TSC content than non-irradiated controls. RIM decreased significantly and linearly with increasing radiation dosage. After leaching, the linearity between these parameters improved. Gamma radiation had no significant effect on αMAXand the time elapsed after irradiation did not influence αMAX, RIM or TSC. [ABSTRACT FROM AUTHOR]