Search

Objective: To investigate the ability of resin infiltration to protect demineralized enamel against acidic challenge. Materials and methods: Forty‐five extracted healthy premolars were selected for the study, each of which was sectioned vertically into 2 halves, giving 90 specimens. Specimens were then divided into three groups, where specimens of group A were not decalcified (control), while those of groups B and C were either subjected to decalcification only, or decalcification followed by Icon resin infiltration, respectively. Each group was further divided into three subgroups, according to the type of storage medium (water, Coca‐Cola, or Redbull). Evaluation parameters included color difference and surface roughness. Scanning electron microscope was used to evaluate enamel surface topography. Statistical analysis was performed by ANOVA followed by least significant difference test. Results: Although Coca‐Cola caused the highest color change and surface roughness among the studied specimens, yet, the resin‐infiltrated enamel was more resistant to surface changes than the nonresin infiltrated enamel, even under acid attack. Conclusion: Resin infiltration has the ability to provide and maintain protection to the demineralized enamel against acidic attack. Clinical significance: Resin infiltration may be considered as a promising solution to restore esthetic of demineralized enamel following orthodontic treatment and to protect it against acidic beverages. [ABSTRACT FROM AUTHOR]

In the present study, Zingiber officinale is used for the synthesis of Zingiber officinale capped silver nanoparticles (ZOE-AgNPs) and compares the antimicrobial efficacy and compressive strength of conventional glass ionomer cement (GIC) combined with ZOE-AgNPs, lyophilized miswak, and chlorhexidine diacetate (CHX) against oral microbes. Five groups of the disc-shaped GIC specimens were prepared. Group A: lyophilized miswak and GIC combination, Group B: ZOE-AgNPs and GIC combinations, Group C: CHX and GIC combination, Group D: ZOE-AgNPs + CHX + GIC; Group E: Conventional GIC. Results confirmed the successful formation of ZOE-AgNPs that was monitored by UV-Vis sharp absorption spectra at 415 nm. The X-ray diffractometer (XRD) and transmission electron microscope (TEM) results revealed the formation of ZOE-AgNPs with a mean size 10.5–14.12 nm. The peaks of the Fourier transform infrared spectroscopy (FTIR) were appearing the involvement of ZOE components onto the surface of ZOE-AgNPs which played as bioreducing, and stabilizing agents. At a 24-h, one-week and three-week intervals, Group D showed the significantly highest mean inhibitory zones compared to Group A, Group B, and Group C. At microbe-level comparison, Streptococcus mutans and Staphylococcus aureus were inhibited significantly by all the specimens tested except group E when compared to Candida albicans. Group D specimens showed slightly higher (45.8 ± 5.4) mean compressive strength in comparison with other groups. The combination of GIC with ZOE-AgNPs and chlorhexidine together enhanced its antimicrobial efficacy and compressive strength compared to GIC with ZOE-AgNPs or lyophilized miswak or chlorhexidine combination alone. The present study revealed that The combination of GIC with active components of ZOE-AgNPs and chlorhexidine paves the way to lead its effective nano-dental materials applications. [ABSTRACT FROM AUTHOR]