Search

A detailed study of the magnetic characterizations of the top structure MgO/CoFeB/Mo is presented. The samples show strong perpendicular magnetic anisotropy (PMA) when the thickness of CoFeB is 0.9 nm and 1.1 nm. The saturation magnetic moment and interface anisotropy constant are 1566 emu/cm3 and 3.75 erg/cm2, respectively. The magnetic dead layer (MDL) is about 0.23 nm in this system. Furthermore, strong capping layer thickness dependence is also observed. The strong PMA of 1.1 nm CoFeB only exists in a Mo cap layer thickness window of 1.2–2 nm. To maintain PMA, the metal layer could not be too thin or thick in these multilayers. The oxidation and diffusion of the metal capping layer should be respectively responsibility for the degradation of PMA in these thin or thick metal capping layer samples. [ABSTRACT FROM AUTHOR]

Pure tungsten (W) and chromium doped W (W-5%Cr) are prepared by powder metallurgy. The microstructure, blistering and helium retention are investigated by x-ray diffraction, scanning electron microscopy, transmission electron microscopy and thermal desorption spectroscopy (TDS). These results show that the average size and density of helium blisters on the surface of pure W are much larger than those on the W-5%Cr alloy. Vacancy-impurity pairs can reduce the migration coefficients of vacancy and vacancy-helium complexes, and Cr may play a role of such an impurity. Moreover, the TDS result shows that the highest desorption peak moves to higher temperature, which is attributed to the HemCrkVn complexes in the W-Cr alloy. In addition, the helium retention is found to be higher in W than in W-5%Cr. [ABSTRACT FROM AUTHOR]

Tungsten has been chosen as one of the most promising candidates as the plasma-facing material in future fusion reactors. Although tungsten has numerous advantages compared with other materials, issues including dust are rather difficult to deal with. Dust is produced in fusion devices by energetic plasma-surface interaction. The re-deposition of dust particles could cause the retention of fuel atoms. In this work, tungsten is deposited with deuterium plasma by hollow cathode discharge to simulate the dust production in a tokamak. The morphology of the deposited tungsten can be described as a film with spherical particles on it. Thermal desorption spectra of the deposited tungsten show extremely high desorption of the peak positions. It is also found that there is a maximum retention of deuterium in the deposited tungsten samples due to the dynamic equilibrium of the deposition and sputtering process on the substrates. [ABSTRACT FROM AUTHOR]

The dependence of perpendicular magnetic anisotropy (PMA) on the barrier layer MgO thickness in MgO/CoFeB/Ta multilayers is investigated. The results show that the strongest PMA occurs in a small window of about 2–4 nm with the increase of MgO thickness from 1–10 nm. The crystalline degree of MgO and the change of interatomic distance along the out-of-plane direction may be the main reasons for the change of PMA in these multilayers. Moreover, the roughnesses of 2- and 4-nm-thick MgO samples are 3.163 and 1.8 nm, respectively, and both the samples show PMA. These results could be used to tune the magnetic characteristic of the ultra thin CoFeB film for future applications in perpendicular magnetic devices. [ABSTRACT FROM AUTHOR]