Search

Purpose: This study evaluated the effect of an aromatic silane compound and acidic functional monomer on the bond strength of fused quartz. Materials and Methods: A total of 264 disk specimens were fabricated from fused quartz for shear bond testing. Two silane compounds were used: 3-(trimethoxysilyl)propyl methacrylate (3-TMSPMA) and 3-(4-methacryloyloxyphenyl)propyltrimethoxysilane (3-MPPTS). As acidic functional monomers, 4-methacryloyloxyethyl trimellitate (4-MET) and 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) were used. The disks were primed with one of each silane compound with or without the acidic functional monomer of the same molarity. The specimens were bonded with a tri-n-butylborane (TBB) initiated luting material. The shear bond strength was determined before and after 10,000 thermocycles. Bond strength was statistically evaluated with Kruskal-Wallis, Mann-Whitney U-, and Steel-Dwass tests. To test dye penetration, the specimens were immersed in 0.5 wt% fuchsin solution for 24 h after priming with each condition, bonding, and 10,000 thermocycles. The dye penetration area was determined by observing the backside of the bonded specimen with an optical microscope. The relationship between the shear bond strength and dye penetration ratio was analyzed with Spearman's rank correlation test. Results: The highest post-thermocycling bond strengths in the 1 mol% and 2 mol% groups were 3-TMSPMA + 10-MDP and 3-MPPTS + 10-MDP. Spearman's rank correlation coefficient between shear bond strength and dye penetration area was γ = -0.7519, indicating a strong negative correlation. Conclusion: The surface treatments of 3-TMSPMA and 3-MPPTS combined with 10-MDP yielded higher bond strength after 10,000 thermocycles than those combined with 4-MET, despite the similarity in molarity. The shear bond strength was negatively correlated with the dye penetration area. [ABSTRACT FROM AUTHOR]

This study assessed the effect of a primer containing 10-methacryloyloxydecyl-(2-thiohydantoin-4-yl)propionate (MDTHP) on the bonding of noble metal alloys to an acrylic resin. Three noble metal alloys were selected as adherends, and V-Primer containing 6-(4-vinylbenzyl-n-propyl)amino-1,3,5-triazine-2,4-dithione was used as a comparative control. The disk specimens of each noble metal alloy were wet-ground and divided into three conditions: specimens primed with MDTHP primer or V-Primer, and specimens without priming. An acrylic resin was bonded to each specimen, and the specimens were performed the shear bond test. The MDTHP primer showed higher shear bond strength than the V-Primer for all specimens. X-ray photoelectron spectroscopic analysis showed that MDTHP was adsorbed on the Au-Pt-Pd alloy surface even after acetone cleaning. MDTHP binds not only with Cu but also with Au and Ag, promoting the bond strength of noble metal alloys. The effectiveness of MDTHP on dental noble metal alloys was suggested. [ABSTRACT FROM AUTHOR]

This study assessed the gloss and surface roughness of computer-aided design/computer-aided manufacturing (CAD/CAM) resin composites corroded with acidulated phosphate fluoride (APF) application. One ceramic block, ten CAD/CAM resin composites for premolars, and four CAD/CAM resin composites for molars were assessed. The surface topography of the materials before and after APF application was observed using an electron microscope. The results were analyzed by Wilcoxon signed-rank test and Dunnett's many to one test (p<0.05). Gloss after APF application was significantly lower for all CAD/CAM resin composites except Artesano. Ra after APF application was significantly higher for all CAD/CAM resin composites except Artesano, Dentcraft HR Block, and Estelite P Block, and Sa was significantly higher for all CAD/CAM resin composites. Irregular surface topography was observed after APF application and the surface features differed among the materials. Therefore, APF application may be detrimental to the surface properties of CAD/CAM resin composites. [ABSTRACT FROM AUTHOR]

The purpose of this study is to investigate the combined effect of two-liquid silane-phosphate primer and single-liquid sodium sulfite primer on bonding between self-polymerizing resins and feldspathic ceramics, and to promote the polymerization behavior of self-polymerizing resins at the bonding interface. The silane-phosphate primer (Super-Bond PZ Primer; PZ) and the sodium sulfite primer (Teeth Primer; TP) were used as the surface treatment agents for bonding the feldspathic ceramics and the self-polymerizing resins (MMA-TBB resin and 4-META/MMA-TBB resin). Combined PZ and TP showed high shear bond strengths. The peak of the differential scanning calorimetry curve was shown to occur early through the addition of TP. These results indicated that additional TP promoted the conversion in the initial polymerization of resin, and the firmly bond was obtained at the interface. PZ+TP treatment can be regarded as an effective treatment for a temporary splint used in teeth restoration. [ABSTRACT FROM AUTHOR]

The purpose of the current study was to evaluate the effect of etching with potassium hydrogen difluoride (KHF2) and ammonium hydrogen difluoride (NH4HF2) on the bond strength of a self-polymerizing methyl methacrylate resin (MMA-TBB) bonded to zirconia. Zirconia disks were prepared using the following surface treatment: no treatment, alumina blasting, and etching with KHF2 or NH4HF2. The specimens were bonded with the MMA-TBB. The shear bond (Ø=5 mm) strength was measured. The surface free energies of the specimens were determined by measuring contact angles. The KHF2 and NH4HF2 groups exhibited higher shear bond strength and surface free energy than did the alumina blasting and no treatment groups. Compared with alumina blasting, etching with KHF2 and NH4HF2 exhibited superior bonding ability of mechanical retention to zirconia. [ABSTRACT FROM AUTHOR]

This study aimed to investigate how different compositions of experimental silane-based primers in a methyl methacrylate solution containing 3-(trimethoxysilyl)propyl methacrylate (3-TMSPMA) or 3-(4-methacryloyloxyphenyl)propyl trimethoxysilane (3-MPPTS) might act as silicon dioxide bonding agents. With or without post-silanization heat treatment, primer-treated quartz discs were bonded using the MMA-TBB resin and their bond strengths were evaluated. The disks were primed with one of the following materials: 1 mol% 3-TMSPMA, 2 mol% 3-TMSPMA, 1 mol% 3-MPPTS, and 2 mol% 3-MPPTS. Shear bond strength was determined both before and after thermocycling. Statistical analyses were performed with non-parametric procedure (Kruskal-Wallis, Mann-Whitney U, and Steel-Dwass tests). Both primers were effective with heat treatment to enhance bonding between quartz and the MMA-TBB, and the bonding durability of the 1 and 2 mol% 3-MPPTS (16.8 and 24.9 MPa) with heat groups was significantly higher than in the 1 and 2 mol% 3-TMSPMA (5.4 and 9.8 MPa) with heat groups. [ABSTRACT FROM AUTHOR]

This study aimed to evaluate the effect of surface preparation on bond strength of a tri-n-butylborane initiated resin (MMA-TBB) bonded to zirconia. Zirconia disks were either airborne-particle abraded with alumina or silica-coated. The disks were thereafter primed with one of the following materials: phosphate-silane (Clearfil Ceramic Primer), phosphate (Alloy Primer), or silane (ESPE Sil). The specimens were bonded with the MMA-TBB. Shear bond strength was determined both before and after thermocycling. Bond strength of unprimed zirconia (control) was not affected by the surface roughness of each adherend. Priming with phosphate was effective for bonding alumina-blasted zirconia. Priming with silane was effective for bonding silica-coated zirconia. Priming effect of the phosphate-silane was superior to that of silane alone for bonding silica-coated zirconia. Bond strength to zirconia of the MMATBB is significantly influenced by a combination of the specific functional monomer and the surface modification performed rather than the material surface roughness. [ABSTRACT FROM AUTHOR]