Search

GaN microwires were shown to possess promising characteristics as building blocks for radiation resistant particle detectors. They were grown by metal organic vapour phase epitaxy with diameters between 1 and 2 μm and lengths around 20 μm. Devices were fabricated by depositing gold contacts at the extremities of the wires using photolithography. The response of these single wire radiation sensors was then studied under irradiation with 2 MeV protons. Severe degradation of the majority of devices only sets in for fluences above protons cm−2 revealing good radiation resistance. During proton irradiation, a clear albeit small current gain was observed with a corresponding decay time below 1 s. Photoconductivity measurements upon irradiation with UV light were carried out before and after the proton irradiation. Despite a relatively low gain, attributed to significant dark currents caused by a high dopant concentration, fast response times of a few seconds were achieved comparable to state-of-the-art GaN nanowire photodetectors. Irradiation and subsequent annealing resulted in an overall improvement of the devices regarding their response to UV radiation. The photocurrent gain increased compared to the values that were obtained prior to the irradiation, without compromising the decay times. The results indicate the possibility of using GaN microwires not only as UV detectors, but also as particle detectors. [ABSTRACT FROM AUTHOR]

Single nitride nanowire core/shell n-p photodetectors are fabricated and analyzed. Nanowires consisting of an n-doped GaN stem, a radial InGaN/GaN multiple quantum well system and a p-doped GaN external shell were grown by catalyst-free metal–organic vapour phase epitaxy on sapphire substrates. Single nanowires were dispersed and the core and the shell regions were contacted with a metal and an ITO deposition, respectively, defined using electron beam lithography. The single wire photodiodes present a response in the visible to UV spectral range under zero external bias. The detector operation speed has been analyzed under different bias conditions. Under zero bias, the  −3 dB cut-off frequency is ~200 Hz for small light modulations. The current generation was modeled using non-equilibrium Green function formalism, which evidenced the importance of phonon scattering for carrier extraction from the quantum wells. [ABSTRACT FROM AUTHOR]

We report a highly flexible strain sensor which exploits the piezoelectric properties of ultra-long gallium nitride (GaN) wires. Langmuir–Blodgett assembled wires are encapsulated in a dielectric material (parylene-C), which is sandwiched between two planar electrodes in a capacitor-like configuration. Through FEM simulations we show that encapsulating densely aligned conical wires in a properly designed dielectric layer can maximize the amplitude of the generated piezoelectric output potential. According to these considerations we designed and fabricated macroscopic flexible strain sensors (active area: 1.5 cm2). The sensor was actuated in three point configuration inducing curvature radii of less than 10 cm and has a typical force sensitivity of 30 mV N−1. [ABSTRACT FROM AUTHOR]

A catalyst-free method for growing self-assembled GaN wires on c-plane sapphire substrates by metal-organic vapour phase epitaxy is developed. This approach, based on in situ deposition of a thin SiNx layer ([?]2 nm), enables epitaxial growth of c-oriented wires with 200-1500 nm diameters and a large length/diameter ratio (>100) on c-plane sapphire substrate. Detailed study of the growth mechanisms shows that a combination of key parameters is necessary to obtain vertical growth. In particular, the duration of the SiNx deposition prior to the wire growth is critical for controlling the epitaxy with the substrate. The GaN seed nucleation time determines the mean size diameter and structural quality, and a high Si-dopant concentration promotes vertical growth. Such GaN wires exhibit UV-light emission centred at [?]350 nm and a weak yellow band ([?]550 nm) at low temperature. [ABSTRACT FROM AUTHOR]