Search

This research endeavours to study the growth of ultralong carbon nanotubes (UL-CNTs) from methane using diverse catalysts, namely FeCl3, bi-metallic Fe-Cu, Fe-Ni, and Fe-Co chlorides. Aqueous catalyst solutions were evenly dispersed on silica substrates and grown at 950 °C in the presence of hydrogen via a horizontal chemical vapour deposition (CVD) furnace. The samples underwent characterisation by Raman spectroscopy, scanning electron microscopy (SEM), and optical microscopy to identify the quality of CNTs and enumerate individual UL-CNTs. Our findings revealed that FeCl3, as a mono-metallic catalyst, generated the longest UL-CNTs, which measured 1.32 cm, followed by Fe-Cu (0.85 cm), Fe-Co (0.7 cm), and Fe-Ni (0.6 cm), respectively. The G/D ratio (graphene to defects) from the Raman spectroscopy was the highest with the FeCl3 catalyst (3.09), followed by Fe-Cu (2.79), Fe-Co catalyst (2.13), and Fe-Ni (2.52). It indicates that the mono-iron-based catalyst also produces the highest purity CNTs. Moreover, this study scrutinises the vapour-liquid-solid (VLS) model for CNT growth and the impact of carbide formation as a precursor to CNT growth. Our research findings indicate that forming iron carbide (Fe3C) is a crucial transition phase for amorphous carbon transformation to CNTs. Notably, the iron catalyst generated the longest and densest CNTs relative to other iron-based bi-metallic catalysts, which is consistent with the temperature of carbide formation in the mono-metallic system. From correlations made using the phase diagram with carbon, we conclude that CNT growth is favoured because of increased carbon solubility within the mono-metallic catalyst compared to the bi-metallic catalysts. [ABSTRACT FROM AUTHOR]

Carbon nanotubes (CNTs) have long been at the forefront of materials research, with applications ranging from composites for increased tensile strength in construction and sports equipment to transistor switches and solar cell electrodes in energy applications. There remains untapped potential still when it comes to energy and data transmission, with our group having previously demonstrated a working ethernet cable composed of CNT fibers. Material composition, electrical resistance, and electrical capacitance all play a strong role in the making of high-quality microphone and headphone cables, and the work herein describes the formation of a proof-of-concept CNT audio cable. Testing was done compared to commercial cables, with frequency response measurements performed for further objective testing. The results show performance is on par with commercial cables, and the CNTs being grown from waste plastics as a carbon source further adds to the value proposition, while also being environmentally friendly. [ABSTRACT FROM AUTHOR]

We report the effect of annealing, both electrical and by applied voltage, on the electrical conductivity of fibers spun from carbon nanotubes (CNTs). Commercial CNT fibers were used as part of a larger goal to better understand the factors that go into making a better electrical conductor from CNT fibers. A study of thermal annealing in a vacuum up to 800 °C was performed on smaller fiber sections along with a separate analysis of voltage annealing up to 7 VDC; both exhibited a sweet spot in the process as determined by a combination of a two-point probe measurement with a nanoprobe, resonant Raman spectroscopy, and X-ray photoelectron spectroscopy (XPS). Scaled-up tests were then performed in order to translate these results into bulk samples inside a tube furnace, with similar results that indicate the potential for an optimized method of achieving a better conductor sample made from CNT fibers. The results also help to determine the surface effects that need to be overcome in order to achieve this. [ABSTRACT FROM AUTHOR]

The inherent value and use of hydrocarbons from waste plastics and solvents can be extended through open-loop chemical recycling, as this process converts plastic to a range of non-plastic materials. This process is enhanced by first creating plastic–solvent combinations from multiple sources, which then are streamlined through a single process stream. We report on the relevant mechanics for streamlining industrially relevant polymers such as polystyrene (PS), polypropylene (PP), high-density polyethylene (HDPE), and acrylonitrile butadiene styrene (ABS) into chemical slurries mixed with various organic solvents such as toluene, xylene, and cyclohexane. The miscibility of the polymer feedstock within the solvent was evaluated using the Relative Energy Difference method, and the dissolution process was evaluated using the "Molecular theories in a continuum framework" model. These models were used to design a batch process yielding 1 tonne/h slurry by setting appropriate assumptions including constant viscosity of solvents, disentanglement-controlled dissolution mechanism, and linear increase in the dissolved polymer's mass fraction over time. Solvent selection was found to be the most critical parameter for the dissolution process. The characteristics of the ideal solvent are high affinity to the desired polymer and low viscosity. This work serves as a universal technical guideline for the open-loop chemical recycling of plastics, avoiding the growth of waste plastic by utilising them as a carbon feedstock towards a circular economy framework. [ABSTRACT FROM AUTHOR]

For every three people on the planet, there are approximately two Tonnes (Te) of plastic waste. We show that carbon recovery from polystyrene (PS) plastic is enhanced by the coaddition of solvents to grow carbon nanotubes (CNTs) by liquid injection chemical vapour deposition. Polystyrene was loaded up to 4 wt% in toluene and heated to 780 °C in the presence of a ferrocene catalyst and a hydrogen/argon carrier gas at a 1:19 ratio. High resolution transmission electron microscopy (HRTEM), scanning electron microscopy (SEM), thermogravimetric analysis (TGA) and Raman spectroscopy were used to identify multiwalled carbon nanotubes (MWCNTs). The PS addition in the range from 0 to 4 wt% showed improved quality and CNT homogeneity; Raman "Graphitic/Defective" (G/D) values increased from 1.9 to 2.3; mean CNT diameters increased from 43.0 to 49.2 nm; and maximum CNT yield increased from 11.37% to 14.31%. Since both the CNT diameters and the percentage yield increased following the addition of polystyrene, we conclude that carbon from PS contributes to the carbon within the MWCNTs. The electrical contact resistance of acid-washed Bucky papers produced from each loading ranged from 2.2 to 4.4 Ohm, with no direct correlation to PS loading. Due to this narrow range, materials with different loadings were mixed to create the six wires of an Ethernet cable and tested using iPerf3; the cable achieved up- and down- link speeds of ~99.5 Mbps, i.e., comparable to Cu wire with the same dimensions (~99.5 Mbps). The lifecycle assessment (LCA) of CNT wire production was compared to copper wire production for a use case in a Boeing 747-400 over the lifespan of the aircraft. Due to their lightweight nature, the CNT wires decreased the CO2 footprint by 21 kTonnes (kTe) over the aircraft's lifespan. [ABSTRACT FROM AUTHOR]

Carbon nanotubes (CNTs) can be spun into fibers as potential lightweight replacements for copper in electrical current transmission since lightweight CNT fibers weigh <1/6th that of an equivalently dimensioned copper wire. Experimentally, it has been shown that the electrical resistance of CNT fibers increases with longitudinal strain; however, although fibers may be under radial strain when they are compressed during crimping at contacts for use in electrical current transport, there has been no study of this relationship. Herein, we apply radial stress at the contact to a CNT fiber on both the nano- and macro-scale and measure the changes in fiber and contact resistance. We observed an increase in resistance with increasing pressure on the nanoscale as well as initially on the macro scale, which we attribute to the decreasing of axial CNT...CNT contacts. On the macro scale, the resistance then decreases with increased pressure, which we attribute to improved radial contact due to the closing of voids within the fiber bundle. X-ray photoelectron spectroscopy (XPS) and UV photoelectron spectroscopy (UPS) show that applied pressure on the fiber can damage the π–π bonding, which could also contribute to the increased resistance. As such, care must be taken when applying radial strain on CNT fibers in applications, including crimping for electrical contacts, lest they operate in an unfavorable regime with worse electrical performance. [ABSTRACT FROM AUTHOR]