Search

The feasibility of using Corning's edge strength measurement system (ESMS) for ultra‐thin LCD panels has been demonstrated. Panels were used to validate the load‐to‐stress correlation: digital image correlation, finite element analysis and mirror radius measurement all showed good agreement, supporting the robustness of the strength measurement. The edge strength of panels was measured by both static and dynamic ESMS. Test results revealed that dynamic ESMS is advantaged over static in better capturing the relevant flaw population owing to its larger test area. Accurate edge strength measurement via ESMS coupled with selective fracture analysis on the weakest flaws will assist in improving the edge strength of ultra‐thin LCD panels [ABSTRACT FROM AUTHOR]

Transparent brittle ceramics such as soda-lime glass pose unique challenges for performing full-field optical measurement of deformations and stresses to characterize fracture and failure behaviors. Low fracture toughness coupled with high stiffness and elastic wave speeds are among the factors responsible for some of these challenges as deformations tend to be small and confined to an extremely small region near the stress concentrators. Need for strong birefringence, elaborate optics, or lack of sufficient measurement sensitivity are some of the factors against legacy techniques such as photoelasticity, optical interferometry, and speckle methods, respectively, to study soda-lime glass. Motivated by these factors, the feasibility of Digital Gradient Sensing ( DGS) method to measure crack-tip and contact-induced deformations in soda-lime glass under quasi-static loading is demonstrated. This first of a two parts paper demonstrates the applicability of DGS for the problem under quasi-static loading condition. The optical measurements are used to evaluate the relevant parameters and compare with the analytical solutions. The second part of this study is focused on measuring contact-point and crack-tip deformations during impact-induced stress wave loading. [ABSTRACT FROM AUTHOR]

Transparent brittle ceramics such as soda-lime glass pose unique challenges for performing full-field optical measurement of deformations and stresses to characterize fracture and failure behaviors. Low fracture toughness coupled with high stiffness and elastic wave speeds are among the factors responsible for some of these challenges as deformations tend to be confined to an extremely small region near an almost mathematically sharp growing crack. Need for strong birefringence, elaborate optics, or lack of sufficient measurement sensitivity are some of the factors against legacy techniques such as photoelasticity, optical interferometry, and speckle methods, respectively, to study soda-lime glass. Motivated by these factors, the feasibility of digital gradient sensing ( DGS) method to measure impact induced deformations near a contact-point and a dynamically growing crack-tip in soda-lime glass are demonstrated in this work. This second of a two-part paper demonstrates the applicability of DGS for the problems under stress wave loading conditions. Ultrahigh-speed photography (1 million frames per sec) in conjunction with DGS and a Hopkinson pressure bar to load soda-lime glass specimens are employed. The optical measurements are postprocessed to obtain relevant engineering parameters and stress field [ABSTRACT FROM AUTHOR]