Search

Activation is commonly used to improve the surface and porosity of different kinds of carbon nanomaterials: activated carbon, carbon nanotubes, graphene, and carbon black. In this study, both physical and chemical activations are applied to graphene oxide by using CO2 and KOH-based approaches, respectively. The structural and the chemical properties of the prepared activated graphene are deeply characterized by means of scanning electron microscopy, Raman spectroscopy, Fourier transform infrared spectroscopy, X-ray photoelectron spectrometry and nitrogen adsorption. Temperature activation is shown to be a key parameter leading to enhanced CO2 adsorption capacity of the graphene oxide-based materials. The specific surface area is increased from 219.3 m2 g−1 for starting graphene oxide to 762.5 and 1060.5 m2 g−1 after physical and chemical activation, respectively. The performance of CO2 adsorption is gradually enhanced with the activation temperature for both approaches: for the best performances of a factor of 6.5 and 9 for physical and chemical activation, respectively. The measured CO2 capacities are of 27.2 mg g−1 and 38.9 mg g−1 for the physically and chemically activated graphene, respectively, at 25 °C and 1 bar.

Volumetric properties such as density and isobaric thermal expansivity, and surface tension are of paramount importance for nanofluids to evaluate their ability to be used as efficient heat transfer fluids. In this work, the nanofluids are prepared by dispersing few-layer graphene in a commercial heat transfer fluid Tyfocor® LS (40:60 wt.% propylene-glycol/water) with the aid of three different nonionic surfactants: Triton X-100, Pluronic® P-123 and Gum Arabic. The density, isobaric thermal expansivity and surface tension of each of the base fluids and nanofluids are evaluated between 283.15 and 323.15 K. The influence of the mass content in few-layer graphene from 0.05 to 0.5% on these nanofluid properties was studied. The density behavior of the different proposed nanofluids is slightly affected by the presence of graphene, and its evolution is well predicted by the weight-average equation depending on the density of each component of the nanofluids. For all the analyzed samples, the isobaric thermal expansivity increases with temperature which can be explained by a weaker degree of cohesion within the fluids. The surface tension evolution of the graphene-based nanofluids is found to be sensitive to the used surfactant, its content and the few-layer graphene concentration.

High-quality graphene is an especially promising carbon nanomaterial for developing nanofluids for enhancing heat transfer in fluid circulation systems. We report a complete study on few layer graphene (FLG) based nanofluids, including FLG synthesis, FLG-based nanofluid preparation, and their thermal conductivity. The FLG sample is synthesized by an original mechanical exfoliation method. The morphological and structural characterization are investigated by both scanning and transmission electron microscopy and Raman spectroscopy. The chosen two-step method involves the use of thee nonionic surfactants (Triton X-100, Pluronic® P123, and Gum Arabic), a commercial mixture of water and propylene glycol and a mass content in FLG from 0.05 to 0.5%. The thermal conductivity measurements of the three FLG-based nanofluid series are carried out in the temperature range 283.15–323.15 K by the transient hot-wire method. From a modeling analysis of the nanofluid thermal conductivity behavior, it is finally shown that synergetic effects of FLG nanosheet size and thermal resistance at the FLG interface both have significant impact on the evidenced thermal conductivity enhancement.