The application of multiferroics is often limited by low ordering temperatures. Here, the authors show that BaFe2O4 is a room temperature antiferromagnet with improper ferroelectricity, suggesting it as a playground for the study of multiferroicity.

Ionic engineering is exploited to substitute Bi cations in BiFe0.95Mn0.05O3 NPs (BFM) with rare-earth (RE) elements (Nd, Gd, and Dy). The sol-gel synthesized RE-NPs are tested for their magnetic hyperthermia potential. RE-dopants alter the morphology of BFM NPs from elliptical to rectangular to irregular hexagonal for Nd, Gd, and Dy doping, respectively. The RE-BFM NPs are ferroelectric and show larger piezoresponse than the pristine BFO NPs. There is an increase of the maximum magnetization at 300 K of BFM up to 550% by introducing Gd. In hyperthermia tests, 3 mg/ml dispersion of NPs in water and agar could increase the temperature of the dispersion up to ∼39°C under an applied AC magnetic field of 80 mT. Although Gd doping generates the highest increment in magnetization of BFM NPs, the Dy-BFM NPs show the best hyperthermia results. These findings show that RE-doped BFO NPs are promising for hyperthermia and other biomedical applications.

The phase content and sequence, the crystal structure, and the magnetic properties of perovskite solid solutions of the (1−y)BiFeO3–yBiZn0.5Ti0.5O3 series (0.05 ≤ y ≤ 0.90) synthesized under high pressure have been studied. Two perovskite phases, namely the rhombohedral R3c and the tetragonal P4mm, which correspond to the structural types of the end members, BiFeO3 and BiZn0.5Ti0.5O3, respectively, were revealed in the as-synthesized samples. The rhombohedral and the tetragonal phases were found to coexist in the compositional range of 0.30 ≤ y ≤ 0.90. Magnetic properties of the BiFe1−y[Zn0.5Ti0.5]yO3 ceramics with y < 0.30 were measured as a function of temperature. The obtained compositional variations of the normalized unit-cell volume and the Néel temperature of the BiFe1−y[Zn0.5Ti0.5]yO3 perovskites in the range of their rhombohedral phase were compared with the respective dependences for the BiFe1−yB3+yO3 perovskites (where B3+ = Ga, Co, Mn, Cr, and Sc). The role of the high-pressure synthesis in the formation of the antiferromagnetic states different from the modulated cycloidal one characteristic of the parent BiFeO3 is discussed.

Laser fragmentation of colloidal submicron-sized bismuth ferrite particles was performed by irradiating a liquid jet to synthesize bismuth ferrite nanoparticles. This treatment achieved a size reduction from 450 nm to below 10 nm. A circular and an elliptical fluid jet were compared to control the energy distribution within the fluid jet and thereby the product size distribution and educt decomposition. The resulting colloids were analysed via UV-VIS, XRD and TEM. All methods were used to gain information on size distribution, material morphology and composition. It was found that using an elliptical liquid jet during the laser fragmentation leads to a slightly smaller and narrower size distribution of the resulting product compared to the circular jet.