This study investigated the fabrication of porous fluorescent SiC using a constant voltage-controlled anodic oxidation process. The application of a high, constant voltage resulted in a spatial distinction between the porous structures formed inside the fluorescent SiC substrates, due to the different etching rates at the terrace and the large step bunches. Large, dendritic porous structures were formed as the etching process continued and the porous layer thickened. Under the conditions of low hydrofluoric acid (HF) concentration, the uniformity of the dendritic porous structures through the entire porous layer was considerably improved compared with the conditions of high HF concentration. The resulting large uniform structure offered a sizable surface area, and promoted the penetration of atomic layer-deposited (ALD) Al2O3 films (ALD–Al2O3). The emission intensity in the porous fluorescent SiC was confirmed via photoluminescence (PL) measurements to be significantly improved by a factor of 128 after ALD passivation. With surface passivation, there was a clear blueshift in the emission wavelength, owing to the effective suppression of the non-radiative recombination rate in the porous structures. Furthermore, the spatial uniformity of emitted light was examined via PL mapping using three different excitation lasers, which resulted in the observation of uniform and distinctive emissions in the fluorescent SiC bulk and porous areas.

Broadened emission was demonstrated in coaxial GaInN/GaN multiple quantum shell (MQS) nanowires that were monolithically grown by metalorganic chemical vapor deposition. The non-polar GaInN/GaN structures were coaxially grown on n-core nanowires with combinations of three different diameters and pitches. To broaden the emission band in these three nanowire patterns, we varied the triethylgallium (TEG) flow rate and the growth temperature of the quantum barriers and wells, and investigated their effects on the In incorporation rate during MQS growth. At higher TEG flow rates, the growth rate of MQS and the In incorporation rate were promoted, resulting in slightly higher cathodoluminescence (CL) intensity. An enhancement up to 2–3 times of CL intensity was observed by escalating the growth temperature of the quantum barriers to 800 °C. Furthermore, decreasing the growth temperature of the quantum wells redshifted the peak wavelength without reducing the MQS quality. Under the modified growth sequence, monolithically grown nanowires with a broaden emission was achieved. Moreover, it verified that reducing the filling factor (pitch) can further promote the In incorporation probability on the nanowires. Compared with the conventional film-based quantum well LEDs, the demonstrated monolithic coaxial GaInN/GaN nanowires are promising candidates for phosphor-free white and micro light-emitting diodes (LEDs).