Search

Bioactive glasses (BGs) are being increasingly considered for numerous biomedical applications. The loading of natural compounds onto BGs to increase the BG biological activity is receiving increasing attention. However, achieving efficient loading of phytotherapeutic compounds onto the surface of bioactive glass is challenging. The present work aimed to prepare novel amino-functionalized mesoporous bioactive glass nanoparticles (MBGNs) loaded with the phytotherapeutic agent Boswellia sacra extract. The prepared amino-functionalized MBGNs showed suitable loading capacity and releasing time. MBGNs (nominal composition: 58 wt% SiO 2 , 37 wt% CaO, 5 wt% P 2 O 5 ) were prepared by sol-gel-modified co-precipitation method and were successfully surface-modified by using 3-aminopropyltriethoxysilane (APTES). In order to evaluate MBGNs loaded with Boswellia sacra , morphological analysis, biological studies, physico-chemical and release studies were performed. The successful functionalization and loading of the natural compound were confirmed with FTIR, zeta-potential measurements and UV-Vis spectroscopy, respectively. Structural and morphological evaluation of MBGNs was done by XRD, SEM and BET analyses, whereas the chemical analysis of the plant extract was done using GC/MS technique. The functionalized MBGNs showed high loading capacity as compared to non-functionalized MBGNs. The release studies revealed that Boswellia sacra molecules were released via controlled diffusion and led to antibacterial effects against S. aureus (Gram-positive) bacteria. Results of cell culture studies using human osteoblastic-like cells (MG-63) indicated better cell viability of the Boswellia sacra -loaded MBGNs as compared to the unloaded MBGNs. Therefore, the strategy of combining the properties of MBGNs with the therapeutic effects of Boswellia sacra represents a novel, convenient step towards the development of phytotherapeutic-loaded antibacterial, inorganic materials to improve tissue healing and regeneration.

As an innovative approach to overcome the rate-limiting staging of conventional aligners, using shape memory polymers (SMPs) as aligners' materials was investigated in this in vitro study. The ability of SMPs to shape recover and consequently move tooth, upon appropriate stimuli, was evaluated on a typodont model before clinical application. The study design was to achieve 1.9 mm correction movement of an upper central incisor by one aligner after multiple steps/activation. A custom-made aligned typodont model with a movable upper central incisor was scanned. Using an orthodontic software and a 3D printer, resin-models were generated. Seven aligners of ClearX sheets (SMPs) were fabricated by thermoforming on the resin aligned model. Each aligner was tested for repositioning of the central incisor in the typodont model. The model was scanned after each step and the corrective movement was measured through the superimposition of scans. Results showed that the total correction efficiency of the SMPs' aligner was ≈93% (1.76 mm). The corrective movement was 0.94 ± 0.04 mm after the reforming step, 0.66 ± 0.07 mm after the first activation step, and 0.15 ± 0.10 mm after the second activation step. It was concluded that aligners made of SMPs could have a promising future-use in orthodontic aesthetic treatment.

Although several natural plants and mixtures have been known and used over the centuries for their antibacterial activity, few have been thoroughly explored in the field of dentistry. Thus, the aim of this study was to enhance the antimicrobial activity of a conventional glass ionomer cement (GIC) with natural plant extracts. The effect of this alteration on the bond strength and film thickness of glass ionomer cement was evaluated and related to an 0.5% chlorohexidine modified GIC. Olive leaves (Olea europaea) , Fig tree ( Ficus carica) , and the leaves and roots of Miswak ( Salvadora persica) were used to prepare an alcoholic extract mixture. The prepared extract mixture after the evaporation of the solvent was used to modify a freeze-dried glass ionomer cement at three different extracts: water mass ratios 1:2, 1:1, and 2:1. An 0.5% chlorhexidine diacetate powder was added to a conventional GIC for the preparation of a positive control group (CHX-GIC) for comparison. The bond strength to dentine was assessed using a material-testing machine at a cross head speed of 0.5 mm/min. Failure mode was analyzed using a stereomicroscope at 12× magnification. The cement film thickness was evaluated in accordance with ISO standard 9917-1. The minimum number of samples in each group was n = 10. Statistical analysis was performed using a Kruskal-Wallis test followed by Dunn's post hoc test for pairwise comparison. There was a statistically insignificant difference between the median shear bond strength ( p = 0.046) of the control group (M = 3.4 MPa), and each of the CHX-GIC (M = 1.7 MPa), and the three plant modified groups of 1:2, 1:1, 2:1 (M = 5.1, 3.2, and 4.3 MPa, respectively). The CHX-GIC group showed statistically significant lower median values compared to the three plant-modified groups. Mixed and cohesive failure modes were predominant among all the tested groups. All the tested groups ( p < 0.001) met the ISO standard of having less than 25 µm film thickness, with the 2:1 group (M = 24 µm) being statistically the highest among all the other groups. The plant extracts did not alter either the shear bond strength or the film thickness of the GIC and thus might represent a promising additive to GICs.

Objective: To evaluate the surface topography and roughness of orthodontic arch wire materials, including low-friction titanium molybdenum alloy (TMA), conventional TMA, and stainless-steel arch wires., Materials and Methods: The surface topography was evaluated using atomic force microscopy (AFM). A total of 24 wire specimens were used for the AFM scans {8 low-friction TMA (TMA-Low), 8 conventional TMA (TMA-C), and 8 stainless steel (SS)} (Ormco, Orange, CA, USA), measuring 0.016 × 0.022 inches. The conventional and low-friction TMA arch wires served as the test groups, while the stainless-steel arch wire served as the control group., Results: Surface roughness evaluation using AFM revealed that the highest mean of all three roughness parameters was found in the TMA-C group followed by the TMA-Low and SS arch wires in descending order. Pairwise comparison of the mean values showed that the mean value of the SS arch wire material is statistically significantly lower than the mean values of the other two arch wire materials (TMA-C and TMA-Low). However, there was no statistically significant difference in the mean values of TMA-C and TMA-Low arch wires., Conclusion: The SS arch wire showed the smoothest surface topography among the alloys and had statistically significantly lower roughness values than the TMA-C and TMA-Low groups. Low-friction TMA arch wire is still considered to be inferior to stainless steel arch wire., Competing Interests: There are no conflicts of interest., (Copyright: © 2021 Journal of Orthodontic Science.)