The humidity influence on the electronic and ionic resistance properties of thin post-treated poly(3,4-ethylene dioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) films is investigated. In particular, the resistance of these PEDOT:PSS films post-treated with three different concentrations (0, 0.05, and 0.35 M) of ethyl-3-methylimidazolium dicyanamide (EMIM DCA) is measured while being exposed to a defined humidity protocol. A resistance increase upon elevated humidity is observed for the 0 M reference sample, while the EMIM DCA post-treated samples demonstrate a reverse behavior. Simultaneously performed in situ grazing-incidence small-angle X-ray scattering (GISAXS) measurements evidence changes in the film morphology upon varying the humidity, namely, an increase in the PEDOT domain distances. This leads to a detriment in the interdomain hole transport, which causes a rise in the resistance, as observed for the 0 M reference sample. Finally, electrochemical impedance spectroscopy (EIS) measurements at different humidities reveal additional contributions of ionic charge carriers in the EMIM DCA post-treated PEDOT:PSS films. Therefrom, a model is proposed, which describes the hole and cation transport in different post-treated PEDOT:PSS films dependent on the ambient humidity.

Mono- and few-layer MoS 2 were studied by three-dimensional electron diffraction (3D ED) showing distinctly different symmetry for crystals consisting of odd and even number of layers. Experimentally obtained intensity distributions along the relrods match qualitatively kinematically simulated data. Our findings allow to differentiate unambiguously between 1-, 2-, 3- 4- and 5-layers MoS 2 crystals., (Copyright © 2021 Elsevier Ltd. All rights reserved.)