Because additively manufactured materials are increasingly being used in load-bearing structures, strength research has become critical. Surprisingly, numerous studies have reported the tensile strength measurements, but only a few studies have presented meaningful results for the shear strength measurements of additively manufactured polymers. Hence, this paper proposes a combined experimental and numerical investigation of a new interlayer shear strength measurement approach, and it targeted the applications of the same polyamide (PA12) specimens made with fused deposition modeling (FDM) and selective laser sintering (SLS). A necking-shaped shear specimen was developed to measure the pure shear strengths with the aid of a three-dimensional (3D) finite element analysis. The results showed that the specimens made with FDM and SLS exhibited totally different shear failure behaviors. The ultimate shear strength of the FDM-PA specimens had more than a 32% increase over that of the SLS-PA specimens. An interface mechanics assumption was employed to explore the different shear failure mechanisms with the support of a fractography analysis.

Nanofibers based on phenanthroimidazole derivatives PCC, PDC, and PSC were fabricated by organogelation processes, and their fluorescence sensory properties towards acid were investigated. It was found that the emission of PCC in the nanofiber-based film could be quenched significantly upon exposure to gaseous TFA due to the formation of protonated PCC, in which ICT (intramolecular charge transfer) would occur. On the other hand, TFA vapor led to the emitting colors of PDC and PSC in the nanofiber-based films to turn to yellow and green from sky blue and blue, respectively. Additionally, we found that the decay times of PCC were 0.1 s and 1.9 s in probing the saturated vapor of TFA in nanofiber-based film and in spin-coated film, respectively. The results suggested that the high surface-to-volume ratio and large interspace in the nanofiber-based networks favored the enhanced adsorption, accumulation, and diffusion of gaseous molecules, resulting in such a high performance., (© 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.)