Search

Background: Poor mechanical properties, undesirable fast dissolution rate, and lack of antibacterial activity limit the application of hydroxyapatite (HA) as an implant coating material. To overcome these limitations, a hybrid coating of Ag + -substituted fluorhydroxyapatite and titania nanotube (TNT) was prepared., Methods: The incorporation of silver into the HA-TiO 2 hybrid coating improves its antimicrobial properties. The addition of F as a second binary element increases the structural stability of the coating. The TNT/F-and-Ag-substituted HA (FAgHA) bilayer coating on the Ti substrate was confirmed by X-ray diffraction, scanning electron microscope, energy-dispersive X-ray spectroscopy (EDS), and X-ray photoelectron spectroscopy (XPS)., Results: The results indicate that the FAgHA/TNT nanocomposite coating has a dense and uniform morphology with a nano-rod-like structure. The solubility measurement result shows that the substitution of F - ions into the AgHA structure has a positive effect on the dissolution resistance of HA. The adhesion strength of FAgHA/TNT has significantly increased because of the interlocking of the roughened surface with nano-rod-like particles that entered into the voids of the TiO 2 nanotubes. Compared with that of the bare Ti, the corrosion current density of FAgHA/TNT-coated Ti substrate decreased from 3.71 to 0.18 μA, and its corrosion resistance increased by almost two orders of magnitude. Moreover, despite pure HA, the FAgHA killed all viable Staphylococcus aureus after 24 hours of incubation. Although the fabricated FAgHA/TNT coating is hydrophobic, it induced deposition of the typical spherical apatite when immersed in a simulated body fluid (SBF); the osteoblasts spread very well on the surface of the coating. In addition, in vitro cell culture tests demonstrated cell viability and alkaline phosphatase (ALP) similar to pure HA, which indicated good cytocompatibility. Interestingly, compared with bare Ti, FAgHA/TNT-coated Ti surface was innocent for cell vitality and even more beneficial for cell osteogenesis in vitro., Conclusion: Enhancing the osseointegration and preventing infection in implants, the FAgHA/TNT-coated Ti makes implants more successful., Competing Interests: Disclosure The authors report no conflicts of interest in this work.

Objectives: Dentin hypersensitivity (DH) is a prevalent problem. This study aimed to formulate a paste using fluorhydroxyapatite (FA) crystals dispersed in different carriers to treat DH. The ability to occlude patent dentinal tubules and to release ions was investigated., Materials and Methods: Twenty percent FA/sodium alginate, 40% FA/poly(hydroxyethyl methacylate(HEMA)), and 40% FA/poly(DMA-co-MEA) were applied to etched dentin samples and examined with scanning electron microscopy (SEM) to determine the degree of tubule occlusion. Fluoride electrode was used to measure F release and spectroscopy to evaluate Ca and PO4 release. The cytotoxicity of the synthesized poly(DMA-co-MEA) gel was tested. Kruskall-Wallis test was used to test the differences in ion release between the groups., Results: FA/poly(DMA-co-MEA) paste obstructed up to 80% of the dentinal tubules, while the coverage was up to 70% for FA/poly(HEMA) and less than 50% for FA/sodium alginate. Fluoride and Ca release was the highest for FA/P(HEMA), 7.2 ± 0.7 and 139.8 ± 32.5 ppm, respectively. The highest concentration of PO4 was 46.2 ± 16.4 ppm for FA/Sodium alginate. No statistical significance was found., Conclusions: FA/Poly(DMA-co-MEA) and FA/poly(HEMA) pastes may offer immediate short-term relief of DH because of their ability to occlude the tubules and adhere to wet dentin surfaces. The release of the F, Ca, and PO4 ions may offer long-term relief by forming a mineral barrier both within the dentinal tubules and on the dentin surface., Clinical Significance: The tested materials may offer a long-term treatment for DH.

Fluorhydroxyapatite/strontium-substituted hydroxyapatite (FHA/SrHA) biphasic coatings with F and Sr elements incorporated simultaneously into one coating layer were prepared on titanium substrate via colloidal sol-gel method. The bioactivity of the as-prepared FHA/SrHA biphasic coatings was evaluated in vitro by immersion in simulated body fluid (SBF). All the biphasic coatings exhibited great ability to induce apatite precipitation on their surfaces. In vitro cell responses were evaluated using osteoblast-like MG63 cells in terms of cell proliferation and differentiation (alkaline phosphatase activity and osteocalcin level). The biphasic coatings show significantly positive effects on the viability and functional activity of osteoblastic cells with clear evidence that an optimum SrHA amount dose exists, indicating that the coexistence of FHA and SrHA had a synergistic stimulatory effect. This finding suggests the potential use of this colloidal sol-gel derived FHA/SrHA biphasic coatings for hard tissue applications., (Copyright © 2013 Wiley Periodicals, Inc.)