Search

Plasma polymers (PPs) can easily modify material surfaces to improve their bio-applicability due to match-made surface-free energy and functionality. However, cell adhesion to PPs typically composed of various functional groups has not yet been fully understood. We explain the origin of strong resistance to trypsin treatment previously noted for nonendothelial cells on amine PPs. It is caused mainly by nonspecific adhesion of negatively charged parts of transmembrane proteins to the positively charged amine PP surface, enabled by thin glycocalyx. However, endothelial cells are bound primarily by their thick, negatively charged glycocalyx and sporadically by integrins in kinetic traps, both cleaved by trypsin. Cell scratching by atomic force microscopy tip confirmed the correlation of trypsin resistance to the strength of cell adhesion.

Excellent adhesion of electrospun nanofiber (NF) to textile support is crucial for a broad range of their bioapplications, e.g., wound dressing development. We compared the effect of several low- and atmospheric pressure plasma modifications on the adhesion between two parts of composite-polycaprolactone (PCL) nanofibrous mat (functional part) and polypropylene (PP) spunbond fabric (support). The support fabrics were modified before electrospinning by low-pressure plasma oxygen treatment or amine plasma polymer thin film or treated by atmospheric pressure plasma slit jet (PSJ) in argon or argon/nitrogen. The adhesion was evaluated by tensile test and loop test adapted for thin NF mat measurement and the trends obtained by both tests largely agreed. Although all modifications improved the adhesion significantly (at least twice for PSJ treatments), low-pressure oxygen treatment showed to be the most effective as it strengthened adhesion by a factor of six. The adhesion improvement was ascribed to the synergic effect of high treatment homogeneity with the right ratio of surface functional groups and sufficient wettability. The low-pressure modified fabric also stayed long-term hydrophilic (ten months), even though surfaces usually return to a non-wettable state (hydrophobic recovery). In contrast to XPS, highly surface-sensitive water contact angle measurement proved suitable for monitoring subtle surface changes.

Plasma polymers (PPs) can easily modify material surfaces to improve their bio-applicability due to match-made surface-free energy and functionality. However, cell adhesion to PPs typically composed of various functional groups has not yet been fully understood. We explain the origin of strong resistance to trypsin treatment previously noted for nonendothelial cells on amine PPs. It is caused mainly by nonspecific adhesion of negatively charged parts of transmembrane proteins to the positively charged amine PP surface, enabled by thin glycocalyx. However, endothelial cells are bound primarily by their thick, negatively charged glycocalyx and sporadically by integrins in kinetic traps, both cleaved by trypsin. Cell scratching by atomic force microscopy tip confirmed the correlation of trypsin resistance to the strength of cell adhesion.

Excellent adhesion of electrospun nanofiber (NF) to textile support is crucial for a broad range of their bioapplications, e.g., wound dressing development. We compared the effect of several low- and atmospheric pressure plasma modifications on the adhesion between two parts of composite-polycaprolactone (PCL) nanofibrous mat (functional part) and polypropylene (PP) spunbond fabric (support). The support fabrics were modified before electrospinning by low-pressure plasma oxygen treatment or amine plasma polymer thin film or treated by atmospheric pressure plasma slit jet (PSJ) in argon or argon/nitrogen. The adhesion was evaluated by tensile test and loop test adapted for thin NF mat measurement and the trends obtained by both tests largely agreed. Although all modifications improved the adhesion significantly (at least twice for PSJ treatments), low-pressure oxygen treatment showed to be the most effective as it strengthened adhesion by a factor of six. The adhesion improvement was ascribed to the synergic effect of high treatment homogeneity with the right ratio of surface functional groups and sufficient wettability. The low-pressure modified fabric also stayed long-term hydrophilic (ten months), even though surfaces usually return to a non-wettable state (hydrophobic recovery). In contrast to XPS, highly surface-sensitive water contact angle measurement proved suitable for monitoring subtle surface changes.

Thin polymer films were deposited on polished stainless-steel samples by PECVD from a cyclopropylamine precursor and characterized by X-ray photoelectron spectroscopy, secondary-ion mass spectrometry and glow discharge optical emission spectroscopy (GDOES) depth profiling. These depth profiles exhibited reasonable agreement. The GDOES involved the erosion of the polymer films in plasma sustained by an asymmetric RF capacitively coupled discharge using both Ar and Ar-O-2 gases. The application of pure Ar caused unwanted effects, such as the broadening of the polymer-film/substrate interface, which were suppressed when using the mixture with oxygen. Another benefit of oxygen was a significant increase in the etching rate by a factor of about 15 as compared to pure argon. The mechanisms involved in the depth profiling using the mixture of gases were elaborated in some detail, taking into account plasma parameters typical for an asymmetric, capacitively coupled RF discharge in a small volume. The main benefit of using the Ar/O-2 GDOES profiling with respect to XPS and SIMS depth profiling is the increased sputtering rate for polymer films. Comparing the GDOES depth profiling with the Ar/O-2 mixture with profiling in pure Ar, the benefits are a higher sputtering rate and better depth resolution at the polymer/substrate interface.

Thin polymer films were deposited on polished stainless-steel samples by PECVD from a cyclopropylamine precursor and characterized by X-ray photoelectron spectroscopy, secondary-ion mass spectrometry and glow discharge optical emission spectroscopy (GDOES) depth profiling. These depth profiles exhibited reasonable agreement. The GDOES involved the erosion of the polymer films in plasma sustained by an asymmetric RF capacitively coupled discharge using both Ar and Ar-O-2 gases. The application of pure Ar caused unwanted effects, such as the broadening of the polymer-film/substrate interface, which were suppressed when using the mixture with oxygen. Another benefit of oxygen was a significant increase in the etching rate by a factor of about 15 as compared to pure argon. The mechanisms involved in the depth profiling using the mixture of gases were elaborated in some detail, taking into account plasma parameters typical for an asymmetric, capacitively coupled RF discharge in a small volume. The main benefit of using the Ar/O-2 GDOES profiling with respect to XPS and SIMS depth profiling is the increased sputtering rate for polymer films. Comparing the GDOES depth profiling with the Ar/O-2 mixture with profiling in pure Ar, the benefits are a higher sputtering rate and better depth resolution at the polymer/substrate interface.

The COVID-19 pandemic has raised the problem of efficient, low-cost materials enabling the effective protection of people from viruses transmitted through the air or via surfaces. Nanofibers can be a great candidate for efficient air filtration due to their structure, although they cannot protect from viruses. In this work, we prepared a wide range of nanofibrous biodegradable samples containing Ag (up to 0.6 at.%) and Cu (up to 20.4 at.%) exhibiting various wettability. By adjusting the magnetron current (0.3 A) and implanter voltage (5 kV), the deposition of TiO2 and Ag+ implantation into PCL/PEO nanofibers was optimized in order to achieve implantation of Ag+ without damaging the nanofibrous structure of the PCL/PEO. The optimal conditions to implant silver were achieved for the PCL-Ti0.3-Ag-5kV sample. The coating of PCL nanofibers by a Cu layer was successfully realized by magnetron sputtering. The antiviral activity evaluated by widely used methodology involving the cultivation of VeroE6 cells was the highest for PCL-Cu and PCL-COOH, where the VeroE6 viability was 73.1 and 68.1%, respectively, which is significantly higher compared to SARS-CoV-2 samples without self-sanitizing (42.8%). Interestingly, the samples with implanted silver and TiO2 exhibited no antiviral effect. This difference between Cu and Ag containing nanofibers might be related to the different concentrations of ions released from the samples: 80 mu g/L/day for Cu2+ versus 15 mu g/L/day for Ag+. The high antiviral activity of PCL-Cu opens up an exciting opportunity to prepare low-cost self-sanitizing surfaces for anti-SARS-CoV-2 protection and can be essential for air filtration application and facemasks. The rough cost estimation for the production of a biodegradable nanohybrid PCL-Cu facemask revealed $0.28/piece, and the business case for the production of these facemasks would be highly positive, with an Internal Rate of Return of 34%.

This bachelor work deals with a significant part of American history. It analyzes slavery as it is seen in novels of two African American writers who felt a need to express to the story of their ancestors. First part of this work briefly discusses slavery from a historical point of view including first talented black authors and after that a digest of African American literature ensues. The body of the work consists in the analysis of selected novels that is divided into three following parts – life of slaves, attitude of slave owners and interpersonal relationships. Each chapter covers with feelings and thoughts of people held in bondage and with their psyche weakened by the institution of slavery. Final part concerns a literary style of both authors and the importance of selected works., Bakalářská práce pojednává o významné etapě amerických dějin. Analyzuje otroctví tak, jak je viděno v románech dvou afroamerických spisovatelů, kteří cítili potřebu vyjádřit se k osudu svých předků. První část práce popisuje otroctví z hlediska historického včetně prvních nadaných černošských autorů. Poté následuje stručný přehled afroamerické literatury. Hlavní část práce je založena na analýze zvolených románů, která je rozdělena do tří částí – život otroků, postoj otrokářů a mezilidské vztahy. Každá kapitola se zabývá smýšlením a pocity otroků a také tím, jak byla narušována jejich psychika. Závěr práce je věnován literárnímu stylu obou autorů a významu zvolených děl., Katedra anglistiky a amerikanistiky, Dokončená práce s úspěšnou obhajobou