Search

The study of degradation and growth patterns of fungi in modified wood may increase the understanding of their mode of action and may lead to more accurate service-life predictions. The aim of this paper was to study the degradation and growth patterns of brown rot fungi in modified wood and to measure moisture content (MC), structural integrity and the acetyl content by frequent monitoring over 300 days. Mass loss (ML) in the modified wood materials increased slowly up to 3% for 50–100 days after which it flattened out and remained constant during the remainder of the test. Structural integrity and acetyl content were maintained in the modified wood materials and MC was lower compared to untreated wood throughout the decay test. ML results of untreated wood indicate that fungi in solid wood go through distinct phases; the degradation patterns in the modified wood materials were more difficult to interpret.

The study of degradation and growth patterns of fungi in modified wood may increase the understanding of their mode of action and may lead to more accurate service-life predictions. The aim of this paper was to study the degradation and growth patterns of brown rot fungi in modified wood and to measure moisture content (MC), structural integrity and the acetyl content by frequent monitoring over 300 days. Mass loss (ML) in the modified wood materials increased slowly up to 3% for 50–100 days after which it flattened out and remained constant during the remainder of the test. Structural integrity and acetyl content were maintained in the modified wood materials and MC was lower compared to untreated wood throughout the decay test. ML results of untreated wood indicate that fungi in solid wood go through distinct phases; the degradation patterns in the modified wood materials were more difficult to interpret.

The aim of cell wall modification is to keep wood moisture content (MC) below favorable conditions for decay organisms. However, thermally modified, furfurylated, and acetylated woods partly show higher MCs than untreated wood in outdoor exposure. The open question is to which extent decay is influenced by the presence of liquid water in cell lumens. The present paper contributes to this topic and reports on physiological threshold values for wood decay fungi with respect to modified wood. In total, 4200 specimens made from acetylated, furfurylated, and thermally modified beech wood (Fagus sylvatica L.) and Scots pine sapwood (sW) (Pinus sylvestris L.) were exposed to Coniophora puteana and Trametes versicolor. Piles consisting of 50 small specimens were incubated above malt agar in Erlenmeyer flasks for 16 weeks. In general, pile upward mass loss (ML) and MC decreased. Threshold values for fungal growth and decay (ML≥2%) were determined. In summary, the minimum MC for fungal decay was slightly below fiber saturation point of the majority of the untreated and differently modified materials. Surprisingly, T. versicolor was able to degrade untreated beech wood at a minimum of 15% MC, and growth was possible at 13% MC. By contrast, untreated pine sW was not decayed by C. puteana at less than 29% MC. © 2016 by De Gruyter 2016.

Chemically or physically modified wood materials have enhanced resistance to wood decay fungi. In contrast to treatments with traditional wood preservatives, where the resistance is caused mainly by the toxicity of the chemicals added, little is known about the mode of action of nontoxic wood modification methods. This study reviews established theories related to resistance in acetylated, furfurylated, dimethylol dihydroxyethyleneurea- treated, and thermally modified wood. The main conclusion is that only one theory provides a consistent explanation for the initial inhibition of brown rot degradation in modified wood, that is, moisture exclusion via the reduction of cell wall voids. Other proposed mechanisms, such as enzyme nonrecognition, micropore blocking, and reducing the number of free hydroxyl groups, may reduce the degradation rate when cell wall water uptake is no longer impeded. © 2014 Walter de Gruyter GmbH, Berlin/Boston.