Search

After acrylic resins have been developed they found a broad area of application. Today they have totally replaced the amalgam and are used in the manufacturing of dental prosthesis, restorative materials, root canal filling materials, bonding materials and glass ionomers. As a consequence, the number of allergic reactions to these materials is increasing. Purpose: The aim of this study was to evaluate the most common intraoral clinical manifestations of allergic reactions to plastic materials used in dentistry. Materials and methods: The study population consisted of 200 interviewed participants divided into two groups: dental patients with methacrylic restorations and occupationally exposed to methacrylates manicurists and dental technicians. All of them had dental treatments with acrylic materials. 154 of them were patch tested with 24 methacrylate allergens compiled from (Meth)Acrylate Series Adhesives, Dental & Other, (Meth)Acrylate Series - Nails Artificial Series (MN- 1000) (Chemotechnique Diagnostics Vellinge, Sweden). 30 patients (19.48%) showed positive reactions to tested substances. Results: Erythema was observed in 8 (26.66 %) patients, edematous changes in oral tissues in 4 (13.33%) patients. In 60% of patients with positive reactions, there were no intraoral findings. Aphthous or lichenoid eruptions which are specific for contact allergy to dental materials were not registered during intraoral inspections. Conclusions: According to results of this study we cannot confirm that there are specific intra or extra oral changes pathognomonic for methacrylate allergy in dental patients.

Made available in DSpace on 2015-09-17T15:25:05Z (GMT). No. of bitstreams: 0 Previous issue date: 2015-02-09. Added 1 bitstream(s) on 2015-09-17T15:49:21Z : No. of bitstreams: 1 000843397.pdf: 1823033 bytes, checksum: c39021817bdac57624d83d1107f2cb19 (MD5) Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) O objetivo no projeto foi avaliar a resistência à fratura de próteses fixas temporárias, com ou sem reforço posicionado em diferentes orientações (horizontal ou vertical), antes e após a termociclagem. Foram confeccionadas 72 próteses fixas temporárias de quatro elementos com resina bis-acrílica, divididas em três grandes grupos: sem reforço, com reforço horizontal e com reforço vertical. Cada grupo foi subdividido em dois, submetidos ou não a ciclagem térmica, totalizando seis subgrupos (n = 12). O reforço consiste em uma malha de nylon revestida por sílica (experimental). Os grupos ciclados receberam 1.000 ciclos térmicos. Todos os espécimes foram submetidos ao ensaio de resistência à fratura em uma máquina de ensaio universal (EMIC), com velocidade de 1,0 mm/min. No segundo experimento foi avaliada a influência do reforço em barras com dimensões de 25 X 10,5 X 3,3mm. As barras foram submetidas à termociclagem como descrito acima e ao ensaio de resistência à flexão 3 pontos, com velocidade de 5mm/min, com celular de carga de 10 KN. A análise estatística foi realizada através dos testes de Kruskal-Wallis Dunn (5%) e demonstrou que a incorporação e a disposição da malha influenciaram a resistência à fratura e a resistência à flexão da resina bis-acrílica foi aprimorada após a adição da malha The aim of this study was to evaluate fracture resistance of temporary bridges as the influence of the addition of a modified nylon mesh in a bis-acrylic resin (Structur 2SC, VOCO, Cuxhaven, Germany). To the first step a temporary fixed prosthesis was made and were analyzed the presence or absence of the fiber and your position (horizontal or vertical). Some groups was subjected to thermal cycling of 1,000 to simulate a temporary fixed prosthesis with extended use period. All specimens were subjected to the test of fracture resistance in a universal testing machine (EMIC DL 1000, EMIC, Brazil), with a speed of 1.0 mm / min. For the second experiment, the test specimens was made in bar shaped (25 x 10.5 x 3.3 mm). The bars were analyzed concerning groups containing or not fibers. Some specimens were subjected to thermal cycling 1,000 cycles. All bars were submitted to the flexural strength by three points bending test in a universal testing machine at constant speed 5 mm/min with load cell of 10 kN. Statistical analysis was performed with Kruskal-Wallis and Dunn tests (5%) and demonstrated that the incorporation and arrangement of the mesh influence the fracture toughness and flexural strength of the bis-acrylic resin was improved afte adding the mesh

Orientador: Celia Marisa Rizzatti Barbosa Tese (doutorado) - Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba Resumo: Este estudo avaliou a influência do material de inclusão (gesso tipo 11 Herodent@ "G", silicone por condensação laboratorial Zetalabor@ "Z"), e da configuração da porção distal da grade metálica (com apoio "C" e sem apoio "s" sobre o modelo), nas alterações horizontais (esquerda "HE" e direita "HD") e verticais (esquerda "VE" e direita "VD") , entre as porções distais de estruturas metálicas de prõteses parciais removíveis (PPR's) e seus respectivos modelos durante o processamento das bases em resina acrílica. Foram utilizados modelos simulando uma arcada inferior parcialmente desdentada classe I de Kennedy. Quarenta amostras padronizadas foram divididas em quatro grupos. As bases foram processadas com uma resina polimerizada por energia de microondas (Onda-Cryl@). Os dados foram submetidos à análise de variância e as médias, ao teste de Tukey (p