The present study addressed the change in the microstructure of Al–2.5 wt% Fe binary alloy produced using laser powder bed fusion (L-PBF) technique by thermal exposure at 300 °C, and the associated mechanical and thermal properties were systematically examined as well. Multi-semi-cylindrical patterns corresponding to melt pools in the microstructure were macroscopically observed for the as-manufactured sample. No change in the melt-pool morphology was observed after thermal exposure for 1000 h. Inside the melt pools, a large number of the nanoscale metastable Al6Fe phase particles were uniformly distributed inside columnar grains of the α-Al matrix containing concentrated solute Fe in supersaturation. The sequential formation and coarsening of stable θ-Al13Fe4 phases were observed upon exposure to a 300 °C environment, but a considerable amount of nano-sized metastable Al6Fe phases remained even after 1000 h. Furthermore, the thermal exposure continuously reduced the concentration of solute Fe atoms in the α-Al matrix. No significant grain growth was found in α-Al matrix after 1000 h owing to the pinning effect of the dispersed fine particles on grain boundary migration. These results demonstrate a sluggish change in microstructural morphologies of the Al–2.5 wt% Fe alloy. The quantified microstructural parameters addressed dominant strengthening contributions by the solid solution of Fe element and Orowan strengthening mechanism by fine Al–Fe intermetallics in the L-PBF-produced alloy. The high strength level was sustained even after being exposed to 300 °C for long periods. The superior balance of mechanical properties and thermal conductivity can be achieved in the experimental alloys by taking advantage of the various microstructural parameters related to the Al–Fe intermetallic phases and α-Al matrix. more...

In the present study, microstructural and crystallographic features of an Al-Fe binary alloy with a near eutectic composition (Al-2.5wt%Fe) fabricated by laser powder bed fusion (LPBF) process were examined. The LPBF processing for the Al-Fe alloy powder was conducted at room temperature using a 3D Systems ProX 200 operating at a laser power of 204 W and a laser scan speed of 0.6 m/s and 0.8 m/s to fabricate cube samples with high relative density above 99 %. The fabricated sample exhibited characteristic microstructure consisting of a number of melt pools in which the regions had locally melted and rapidly solidified by laser irradiation during the LPBF process. Numerous fine particles of Al-Fe intermetallics with a mean size below 100 nm were found within the α-Al matrix in the observed melt pools, whereas relatively coarsened particles were localized around melt pool boundaries. Electron backscatter diffraction (EBSD) analyses revealed a number of columnar a-Al grains with a mean size of approximately 10 μm. The LPBF-fabricated Al-Fe alloy exhibits a high hardness of approximately 90 HV, which is more than twice higher than the conventionally casted Al-Fe alloy. more...

The inhomogeneous microstructure and its change by annealing for an AlSi10Mg lattice structure with a body-centered cubic unit cell additively manufactured via laser powder bed fusion (LPBF) were investigated. The as-built lattice structure exhibited a cellular microstructure consisting of a number of primary α-Al phases decorated with α-Al/Si eutectic structure. The developed microstructure varied depending on the locations of the node and strut parts of the lattice structure. At the location near the bottom surface of the node part, the cellular microstructure became coarser and more equiaxed than those at the location near the top surface. At the location near the bottom surface of the strut part, the columnar α-Al phases were often elongated along the direction of the strut part. After the annealing at 300 °C for 2 h, numerous Si particles finely precipitated within the primary α-Al phases and coarsening of the eutectic Si phases occurred. After the annealing at 530 °C for 6 h, the microstructural characteristics changed significantly. A significant coarsening of the Si particles and the formation of Fe-containing intermetallic phase (β-AlFeSi) with a plate-shaped morphology occurred. The microstructures became homogeneous in the whole area of the lattice structure annealed at 530 °C for 6 h. more...

The samples of the Al–15Fe (mass%) binary alloy that were additively manufactured by laser powder bed fusion (L-PBF) were exposed to intermediate temperatures (300 and 500 °C), and the thermally induced variations in their microstructural characteristics were investigated. The L-PBF-manufactured sample was found to have a microstructure comprising a stable θ-Al13Fe4 phase localized around melt-pool boundaries and several spherical metastable Al6Fe-phase particles surrounded by a nanoscale α-Al/Al6Fe cellular structure in the melt pools. The morphology of the θ phase remained almost unchanged even after 1000 h of exposure at 300 °C. Moreover, the nanoscale α-Al/Al6Fe cellular structure dissolved in the α-Al matrix; this was followed by the growth (and nucleation) of the spherical Al6Fe-phase particles and the precipitation of the θ phase. Numerous equiaxed grains were formed in the α-Al matrix during the thermal exposure, which led to the formation of a relatively homogenous microstructure. The variations in these microstructural characteristics were more pronounced at the higher investigated temperature of 500 °C. more...

In order to manage both the strength and ductility of Al–Si alloys additively manufactured by laser powder bed fusion (L-PBF), an attempt was made to introduce nanoscale precipitates within the α-Al (fcc) supersaturated solid solution using the L-PBF manufactured Al–12%Si alloy by artificial aging treatments. The aging treatment at 120°C improved both the tensile strength and ductility (total elongation) of the L-PBF manufactured specimen. The simultaneous strength–ductility enhancement is due to the homogeneously distributed nanoscale Si precipitates that enhanced the strain hardening. These results provide new insights for overcoming the strength-ductility trade-off in the L-PBF manufactured Al alloys. more...

The precipitation of intermetallic phases and the associated hardening by artificial aging treatments at elevated temperatures above 400 °C were systematically investigated in the commercially available AC2B alloy with a nominal composition of Al–6Si–3Cu (mass%). The natural age hardening of the artificially aged samples at various temperatures was also examined. A slight increase in hardness (approximately 5 HV) of the AC2B alloy was observed at an elevated temperature of 480 °C. The hardness change is attributed to the precipitation of metastable phases associated with the α-Al15(Fe, Mn)3Si2 phase containing a large amount of impurity elements (Fe and Mn). At a lower temperature of 400 °C, a slight artificial-age hardening appeared. Subsequently, the hardness decreased moderately. This phenomenon was attributed to the precipitation of stable θ-Al2Cu and Q-Al4Cu2Mg8Si6 phases and their coarsening after a long duration. The precipitation sequence was rationalized by thermodynamic calculations for the Al–Si–Cu–Fe–Mn–Mg system. The natural age-hardening behavior significantly varied depending on the prior artificial aging temperatures ranging from 400 °C to 500 °C. The natural age-hardening was found to strongly depend on the solute contents of Cu and Si in the Al matrix. This study provides fundamental insights into controlling the strength level of commercial Al–Si–Cu cast alloys with impurity elements using the cooling process after solution treatment at elevated temperatures above 400 °C. more...

In this study, an attempt is made to control the WC-Co two-phase microstructures by laser powder-bed fusion (LPBF) process using cemented carbide powders with different compositions of WC-25Co (mass%) and WC-17Co (mass%) and post heat-treatment at 1380 °C. The as-built cemented carbide samples had different microstructures from those of the cemented carbides fabricated by conventional manufacturing methods. The microstructures of the as-fabricated WC-25Co and WC-17Co cemented carbides were characterized by two types of regions. Region 1 consisted of W2C and W3Co3C phases, including numerous pores and defects. Region 2 consisted of WC and Co phases. Post heat-treatment of the LPBF-built WC-25Co sample at 1380 °C led to the formation of a defect-free WC-Co two-phase microstructure. In contrast, the W3Co3C phase remained in the LPBF-built WC-17Co sample even after heat treatment. The addition of carbon to the WC-17Co powder prevented the formation of the W3Co3C phase in the cemented carbide processed by LPBF and subsequent heat treatments. The addition of carbon to the WC-17Co powder had a slight effect on the hardness of as-fabricated samples, but reduced the hardness of heat-treated samples. The reduced hardness was attributed to the increased volume fractions of the WC and W3Co3C phases. more...

To identify the microstructural features of the lattice structures of Al alloys built via the selective laser melting (SLM) process, AlSi10Mg alloy with a body-centered cubic (BCC)-type lattice structure was prepared. Characteristic microstructures comprising melt pools with several columnar α-Al phases with orientations along the elongation direction and surrounded by eutectic Si particles were observed at all portions of the built lattice structure. In the node portions of the lattice structure, a gradient microstructure (continuous change in microstructure) was observed. The columnar α-Al phases were observed near the top surface of the node portion, whereas they became coarser and more equiaxed near the bottom surface, resulting in softening localized near the bottom surface. In the strut portions of the lattice structure, the columnar α-Al phases were elongated along the inclined direction of struts. This trend was more prevalent near the bottom surface. The α-Al phases became coarser and more equiaxed near the bottom surface as well. The aforementioned results were the basis of a discussion of the development of the gradient microstructure in lattice-structured Al alloys during the SLM process in terms of thermal conductivities at the boundaries between the manufactured (locally melted and rapidly solidified) portions and adjacent (unmelted) alloy powder. more...

A porous Fe/TiB2 composite layer was synthesized on an Fe substrate by a powder metallurgy process using combustion reactions among Fe, Ti, and B to achieve Fe/resin joints through interpenetrating phase layers. The effects of Fe particle size and the blending ratio of the raw powder mixture on the porous structure, roughness of the top surface of the porous layer, and adhesiveness between the porous layer and Fe substrate were investigated. The peak temperature measured with a thermocouple increased with increasing Fe particle size and blending ratio of Ti and B. An increase in the peak temperature does not affect the porosity of the porous layer. Higher peak temperatures increase the pore size and change the pore morphology from open to semi-closed (although pores are not completely isolated). The change in pore morphology prevents the exposure of pores on the top surface of the porous layer, resulting in decreasing surface roughness. Moreover, an increase in the maximum temperature promotes bonding between the Fe substrate and porous layer. These results are discussed in view of the thermodynamic assessment using the calculated equilibrium phase diagram. more...

In this study, the effects of laser power and scan speed on the relative density, melt pool depth, and Vickers hardness of selectively laser melted (SLM) maraging steel were systematically investigated. The change in these structural parameters and hardness could not always be clarified by the volumetric energy density, which is widely used in the SLM processes. The deposited energy density, wherein the thermal diffusion length is used as a heat-distributed depth, can express the change in these structural parameters and the hardness with one curve. To clarify the effect of the laser parameters, the deposited energy should be used instead of the volumetric energy density. Thus, this study provides a new insight on the selection of the laser condition for SLM-fabricated materials., ファイル公開：2021-08-01 more...

Porous layer on an aluminum alloy (A5052) sheet for joining with a Polyamide-6 (PA6) sheets was synthesized using combustion reactions among Al, Ti, and C powders. The laser was irradiated on the bedded powder blend of Al, Ti and C to induce the combustion reactions. The porous layer consists of a number of particle-shaped protrusions. Phase identification and microstructural observation of the cross-sectioned porous layer showed that the protrusions consisting of α-Al, TiC and Al3Ti phases, bonded well with the Al sheet. Single lap joints with PA6 and Al sheets via the porous layer were fabricated using a hydraulic hot press; PA6 infiltrated into the gaps among the particle-shaped protrusions. Fractography analysis indicated that the particle-shaped protrusions well interlocked with PA6, which resulted in a high-joint strength along with high reliability., ファイル公開：2021-08-01 more...

In the present study, we characterized the Fe–Al intermetallic phases formed in interstitial-free (IF) steel hot-dipped in a Zn–6Al–3Mg (wt.%) alloy melt at different temperatures (400, 460 and 500 °C) and dipping times (from 2 to 3600 s). Chemical composition analyses indicated Fe dissolution into the Zn alloy melt even after 2 s of dipping. Microstructural characterization revealed the initial formation of a continuous θ-Fe4Al13 phase layer, followed by the local growth of η-Fe2Al5 phase toward both steel and Zn alloy melt sides during the hot-dipping process. After long-term hot-dipping, further growth of the η phase was accompanied by significant dissolution of Fe into the Zn alloy melt, resulting in the loss of thickness of the IF steel sheets. Altogether, we rationalized the formation mechanism of Fe–Al intermetallic phases and their associated growth at the interface between solid Fe and liquid Zn alloy in terms of a Zn–Al–Mg–Fe quaternary phase diagram, calculated according to thermodynamic database available in the literature., ファイル公開：2021-06-01 more...

The low oxygen powder metallurgy technique makes it possible to prepare full-dense ultrafine-grained (UFG) Al compacts with an average grain size of 160 nm by local surface bonding at a substantially lower temperature of 423 K from an Al nanopowder prepared by a low oxygen induction thermal plasma process. By atomic level analysis using transmission electron microscopy, it was found that there was almost no oxide layer at the Al/Al interfaces (grain boundaries) in UFG Al compact. The electrical conductivity of the UFG Al compact reached 3.5 × 107 S/m, which is the same level as that of the cast Al bulk. The Vickers hardness of the UFG Al compact of 1078 MPa, which is 8 times that of the cast Al bulk, could be explained by the Hall–Petch law. In addition, fracture behavior was analyzed by conducting a small punch test. The as-sintered UFG Al compact initially fractured before reaching its ultimate strength due to its large number of grain boundaries with a high misorientation angle. Ultimate strength and elongation were enhanced to 175 MPa and 24%, respectively, by reduction of grain boundaries after annealing, indicating that high compatibility of strength and elongation can be realized by appropriate microstructure control. more...

Centimeter-sized samples of hypereutectic Al–15 mass% Fe alloy were manufactured by a laser powder bed fusion (L-PBF) process while systematically varying laser power (P) and scan speed (v). The effects on relative density and melt pool depth of L-PBF-manufactured samples were investigated. In comparison with other Al alloys, a small laser process window of P = 77–128 W and v = 0.4–0.8 ms–1 was found for manufacturing macroscopically crack-free samples. A higher v and P led to the creation of macroscopic cracks propagating parallel to the powder-bed plane. These cracks preferentially propagated along the melt pool boundaries decorated with brittle θ-Al13Fe4 phase, resulting in low L-PBF processability of Al–15%Fe alloy. The deposited energy density model (using P·v−1/2) would be useful for identifying the optimum L-PBF process conditions towards densification of Al–15%Fe alloy samples, in comparison with the volumetric energy density (using P·v−1), however, the validity of the model was reduced for this alloy in comparison with other alloys with high thermal conductivities. This is likely due to inhomogeneous microstructures having numerous coarsened θ–Al13Fe4 phases localized at melt pool boundaries. These results provide insights into achieving sufficient L-PBF processability for manufacturing dense Al–Fe binary alloy samples. more...

This study provides a novel approach to fabricating Al/C composites using laser powder bed fusion (LPBF) for a wide range of structural applications utilizing Al-matrix composites in additive manufacturing. We investigated the effects of LPBF on the fabrication of aluminum/multiwalled carbon nanotube (Al/MWCNT) composites under 25 different conditions, using varying laser power levels and scan speeds. The microstructures and mechanical properties of the specimens, such as elastic modulus and nanohardness, were analyzed, and trends were identified. We observed favorable sintering behavior under laser conditions with low energy density, which verified the suitability of Al/MWCNT composites for a fabrication process using LPBF. The size and number of pores increased in specimens produced under high energy density conditions, suggesting that they are more influenced by laser power than scan speed. Similarly, the elastic modulus of a specimen was also more affected by laser power than scan speed. In contrast, scan speed had a greater influence on the final nanohardness. Depending on the laser power used, we observed a difference in the crystallographic orientation of the specimens by a laser power during LPBF. When energy density is high, texture development of all samples tended to be more pronounced. more...