Single and multilayer films of La0.67Sr0.33MnO3 and CoFe2O4 were deposited by spin-coating. The all-alkoxide precursors allowed inorganic gel films of extreme homogeneity to be formed and converted to phase pure complex oxides at low temperatures. La0.67Sr0.33MnO3 films were made with La- and Ca-methoxy-ethoxides and Mn19O12(moe)(14)(moeH)(10) as precursors at 800 degrees C. The CoFe2O4 films were obtained at extremely low 275 degrees C, using a new CoFe2-methoxyethoxide precursor. The decomposition and microstructural development on heating was described by TG, TEM, XRD and IR spectroscopy. XRD showed no spurious phases and the unit-cell dimensions coincided quite well with literature values of the targeted phases. The structural, magnetic and electronic properties of these films established their phase purity and high quality with physical properties comparable to films deposited by physical deposition methods. The magnetic and magneto transport results are presented for single, bi- and tri- layer structures. The magnetically soft La0.67Sr0.33MnO3 layer was exchange coupled to the magnetically hard CoFe2O4 layer, giving rise to interesting switching behaviour in magnetism and magneto-transport properties.

The austenitic stainless steel 316L has been compared to duplex stainless steels to be able to highlight a choice of material for manufacturing of spare tanks used for cooling water at nuclear power stations on the Swedish west coast. In this report 316L and the duplex stainless steels 2205, 2304 and LDX 2404 have been compared according to corrosion resistance, strength, manufacturing aspects and prices. The steels arranged by increasing corrosion resistance: 316L < 2304 < LDX 2404 < 2205. The steels arranged by increasing strength (considering the thickness of the plates needed for construction): 316L < 2304 < LDX 2404 and 2205. The steels arranged by increasing price/tank: 2304 < LDX 2404 < 2205 < 316L. One of the duplex stainless steels is recommended rather than the austenitic stainless steel 316L. In terms of price 2304 is preferable to 2205 and LDX 2404. When it comes to corrosion resistance 2205 is superior to 2304 and can sometimes be considered as unnecessary good and therefore not relevant for this application.