Search

The heavy metals are used in many industrial processes and when discharged to the environment can cause harmful effects to human, plants and animals. The adsorption technology has been used as an effective methodology to remove metallic ions. The search for new adsorbents motivated the development of this research, accomplished with the purpose of removing Cr (III) from aqueous solutions. Diatomite, chitosan, Filtrol 24TM and active carbon were used as adsorbents. To modify the adsorbent surface was used a bicontinuous microemulsion composed by water (25%), kerosene (25%), saponified coconut oil (10%) and as co-surfactant isoamyl or butyl alcohols (40%). With the objective of developing the best operational conditions the research started with the surfactant synthesis and after that the pseudo-ternary diagrams were plotted. It was decided to use the system composed with isoamyl alcohol as co-surfactant due its smallest solubility in water. The methodology to impregnate the microemulsion on the adsorbents was developed and to prepare each sample was used 10 g of adsorbent and 20 mL of microemulsion. The effect of drying time and temperature was evaluated and the best results were obtained with T = 65 ºC and t = 48 h. After evaluating the efficiency of the tested adsorbents it was decided to use chitosan and diatomite. The influence of the agitation speed, granule size, heavy metal synthetic solution concentration, pH, contact time between adsorbent and metal solution, presence or not of NaCl and others metallic ions in the solution (copper and nickel) were evaluated. The adsorption isotherms were obtained and Freundlich and Langmuir models were tested. The last one correlated better the data. With the purpose to evaluate if using a surfactant solution would supply similar results, the adsorbent surface was modified with this solution. It was verified that the adsorbent impregnated with a microemulsion was more effective than the one with a surfactant solution, showing that the organic phase (kerosene) was important in the heavy metal removal process. It was studied the desorption process and verified that the concentrated minerals acids removed the chromium from the adsorbent surface better than others tested solutions. The treatment showed to be effective, being obtained an increase of approximately 10% in the chitosan s adsorption capacity (132 mg of Cr3+ / g adsorbent), that was already quite efficient, and for diatomite, that was not capable to remove the metal without the microemulsion treatment, it was obtained a capacity of 10 mg of Cr3+ / g adsorbent, checking the applied treatment effectiveness Os metais pesados são utilizados em muitos processos industriais e, quando descartados ao meio ambiente, podem ocasionar efeitos prejudiciais aos seres vivos. O processo de adsorção vem sendo utilizado como metodologia eficaz para a remoção de íons metálicos. A busca por novos adsorventes motivou o desenvolvimento deste trabalho, realizado com o objetivo de remover Cr (III) de soluções aquosas. Utilizou-se como adsorventes: diatomita, quitosana, Filtrol 24TM e carvão ativo. Empregou-se como agente modificador dos adsorventes uma microemulsão bicontínua composta de água (25 %), querosene (25 %), óleo de coco saponificado (10 %) e cotensoativo (álcool isoamílico ou butílico, 40 %). Com o objetivo de obter as melhores condições operacionais partiu-se da obtenção do tensoativo e obteve-se os diagramas pseudoternários. Resolveu-se empregar o sistema contendo o álcool isoamílico devido sua menor solubilidade em água. Desenvolveu-se a técnica de impregnação da microemulsão sobre os adsorventes e, para o preparo de cada amostra, empregou-se 10 g de adsorvente e 20 mL de microemulsão. Avaliou-se o efeito do tempo de secagem e da temperatura, obtendo-se os melhores resultados com T = 65 ºC e t = 48 h. Após avaliar a eficiência dos adsorventes testados resolveu-se utilizar a quitosana e a diatomita e avaliou-se a influência da velocidade de agitação, granulometria, concentração, pH, presença de outros cátions metálicos (cobre e níquel) e NaCl na solução e o tempo de contato do adsorvente com a solução de metal. Obteve-se as isotermas de adsorção e testou-se os modelos de Freundlich e Langmuir, que correlacionou melhor os dados. Com o propósito de verificar se o emprego de uma solução de tensoativo forneceria resultados semelhantes, tratou-se o adsorvente com esta solução e verificou-se que o adsorvente impregnado com a microemulsão foi mais efetivo, comprovando que a fase orgânica (querosene) era importante para o processo. Estudou-se o processo de dessorção e verificou-se que os ácidos minerais concentrados eluiam melhor o cromo. O tratamento mostrou-se eficaz obtendo-se um aumento na capacidade de adsorção de cromo de aproximadamente 10 % para a quitosana (132 mg de Cr3+/ g adsorvente), que já era bastante eficiente, e, para a diatomita, que não era capaz de remover o metal, obteve-se uma capacidade de 10 mg de Cr3+/g adsorvente, comprovando a eficácia do tratamento aplicado