1. Dark current analysis of InasSb-based hetero-p-i-n mid-infrared photodiode
- Author
-
Suo, Fei, Tong, Jinchao, Zhang, Dao Hua, and School of Electrical and Electronic Engineering
- Subjects
Electrical and electronic engineering [Engineering] ,Heterostructure ,Dark Current - Abstract
We comprehensively study the characteristics of dark current for a p-i-n heterostructure photodiode. To reduce the dark current, a wide-bandgap layer (AlGaSb) and thin quaternary layers (AlInAsSb) are inserted in the heterostructure for blocking the dark carrier diffusion and limiting type-II transition at interface, respectively. The activation energy derived from measurement results indicates the positive (negative) correlation between the dominant dark current density and voltage bias (temperature). Whatever the voltage bias (temperature), this relationship always exists, indicating the high stability and reliability of our devices. Indeed, the measures taken for reducing dark current are confirmed to be effective as the dark current density for this photodiode is limited to a lower level. For the typical square mesa with 350 μm side length, at the bias of -0.4 V, the dark current density is 1.78 A/cm2 for T=293 K, and reduces to 0.4 A/cm2 for T=77 K, where the room-temperature value is lower than or comparable with that of the state-of-the-art mid-infrared photodetectors. A room-temperature detectivity of 8.3 × 108 cm · Hz1/2/W with a cut-off wavelength of 4 μm is demonstrated. Agency for Science, Technology and Research (A*STAR) Ministry of Education (MOE) This work was supported in part by the A∗ Star under Grant SERC A1883c0002 and Grant 1720700038, in part by the Ministry of Education, Singapore, under Grant 2017-T1-002-117 and Grant RG 177/17, and in part by the Asian Office of Aerospace Research and Development under Grant FA2386-17-1-0039. (Corresponding author: Jinchao Tong.)
- Published
- 2020