The intercalation of dimethyl sulphoxide (DMSO), pyridine (Py), ethanolamine (Ea), and Nmethyl formamide (NMF) molecules into the kaolinite interlayers led to an appreciable decrease of 3697 cm−1 of the hydroxyl band. The appearance of the peaks at 3662, 3541, and 3504 cm−1proved that the DMSO species are intercalated between the kaolinite layers through forming H-bonds with internal-surface hydroxyl groups. The intensities of the 942 and 796 cm-1bending peaks arising from inner-surface hydroxyls decreased and new vibrational features appeared due to the intercalation of the guest species. The d001 value of pure kaolinite was found at 7.18 A° , and the d001 values were seen at 11.26, 11.62, 10.77, and 10.67 °A for kaolinite-dimethyl sulphoxide (K-DMSO), kaolinite-pyridine (K-Py), kaolinite-ethanolamine (K-EA), and kaolinite-N-methyl formamide (K-NMF) composites, respectively. The endothermic differential thermal analysis (DTA) peaks at a temperature of 108 - 334 ◦C reflected the changes in the physicochemical properties of the intercalated species. The thermal stability increase followed the order of K-Py

A novel N-pyridin-2-ylmethylsuccinamic acid-functionalized smectite nanomaterial was synthesized by immobilizing of N-pyridin-2-ylmethylsuccinamic acid through chemical bonding onto (3-aminopropyl)triethoxysilane modified smectite. The structural, thermal, morphological and surface properties of raw, silane-grafted and the N-pyridin-2-ylmethylsuccinamic acid-functionalized smectites were investigated by various characterization techniques. The thermal analysis data showed the presence of peaks in the temperature range from 200 °C to 600 °C due to the presence of physically adsorbed silanes, intercalated silanes, surface grafted silanes and chemically grafted silane molecules between the smectite layers. The powder x-ray diffraction patterns clearly indicated that the aminopropyl molecules also intercalated into the smectite interlayers as bilayer arrangement whereas N-pyridin-2-ylmethylsuccinamic acid molecules were only attached to 3-aminopropyltriethoxysilane molecules on the external surface and edges of clay and they did not intercalate. Fourier transform infrared spectroscopy confirms N-pyridin-2-ylmethylsuccinamic acid molecules bonding through the amide bond between the amine group of aminopropyltriethoxysilane molecules and a carboxylic acid functional group of N-pyridin-2-ylmethylsuccinamic acid molecules. The guest molecules functionalized onto the smectite caused significant alterations in the textural and morphological parameters of the raw smectite. The anchoring of N-pyridin-2-ylmethylsuccinamic acid molecules led to positive electrophoretic mobility values when compared to starting materials. N-pyridin-2-ylmethylsuccinamic acid-functionalized smectite was employed as an electroactive ingredient in the structure of potentiometric PVC-membrane sensor. The sensor exhibited more selective potentiometric response towards chlorate ions compared to the other common anionic species.