This study investigates the potential use of Yellow River sand (YRS) sourced from the lower reaches of the Yellow River in China as a sustainable and cost-effective substitute for quartz sand in engineered cementitious composites (ECCs). This region accumulates around 400 million tons of sand annually. The study evaluates the impact of different YRS replacement percentages (0, 25, 50, 75, and 100%) on mechanical and microstructure properties under freeze-thaw conditions, focusing on assessing the ECC durability during cooling cycles. The results show that YRS exhibits a smaller normal distribution of particle sizes compared to that of quartz sand and a 5.77 times greater specific surface area, affecting the ECC particle size distribution. After 300 cooling cycles, the R25 group maintains 97.5% of the initial mass and 79.4% of flexural strength, indicating superior durability. The R25 group also demonstrates a minimal decrease of 11.5% in equivalent bending strength, reaching a level of 104.4% compared to R0. The R25 group’s porosity is 30.80%, with an average pore size of 20.47 mm, showing 1.3% and 6.7% decreases compared to the R0 group. Additionally, this study establishes a failure progression equation using the Weibull probability distribution model, with calculated values closely aligning with measured values. Overall, this study recommends using YRS as a sustainable ECC material.

This study examines the impact of the recycled brick powder (RBP) replacement rate, especially at elevated temperatures on RBP-ultra-high-performance concrete (UHPC) properties such as the stress–strain curve, Poisson’s ratio, elastic modulus, and axial compressive strength through uniaxial compression experiments. The results show that with the increase of heating temperature, the axial compressive strength of the specimen increases first and then decreases under natural cooling (NC). In contrast, Poisson’s ratio shows opposite values. The peak strain continues to increase, and the initial elastic modulus and peak secant modulus continue to decrease. Compared with NC, the axial compressive strength of the specimens under water cooling has been reduced, the peak strain is generally larger, the initial elastic modulus and the peak secant modulus are smaller, and the incorporation of RBP also has a certain effect on the mechanical properties. Through regression analysis, an equation is established to calculate the axial compressive strength of RBP-UHPC with temperature, accounting for variables such as temperature, RBP replacement rate, and cooling method. Furthermore, based on the results of axial compression experiments, a constitutive equation for axial compression in RBP-UHPC after exposure to high temperatures is proposed. Overall, the theoretical curve closely aligns with the experimental curve, verifying its accuracy.