AlGaN/GaN high electron mobility transistors (HEMTs) were demonstrated for structures grown on ZrTi metallic alloy buffer layers, which provided lattice matching of the in-plane lattice parameter ("a-parameter") to hexagonal GaN. The quality of the GaN buffer layer and HEMT structure were confirmed with X-ray 2th and rocking scans as well as cross-section transmission electron microscopy (TEM) images. The X-ray 2th scans showed full widths at half maximum (FWHM) of 0.06deg, 0.05deg and 0.08deg for ZrTi alloy, GaN buffer layer, and the entire HEMT structure, respectively. TEM of the lower section of the HEMT structure containing the GaN buffer layer and the AlN/ZrTi/AlN stack on the Si substrate showed that it was important to grow AlN on the top of ZrTi prior to growing the GaN buffer layer. The estimated threading dislocation (TD) density in the GaN channel layer of the HEMT structure was in the 108 cm[?]2 range.

AlGaN/GaN high electron mobility transistors (HEMTs) were demonstrated for structures grown on ZrTi metallic alloy buffer layers, which provided lattice matching of the in-plane lattice parameter (“a-parameter”) to hexagonal GaN. The quality of the GaN buffer layer and HEMT structure were confirmed with X-ray 2θ and rocking scans as well as cross-section transmission electron microscopy (TEM) images. The X-ray 2θ scans showed full widths at half maximum (FWHM) of 0.06°, 0.05° and 0.08° for ZrTi alloy, GaN buffer layer, and the entire HEMT structure, respectively. TEM of the lower section of the HEMT structure containing the GaN buffer layer and the AlN/ZrTi/AlN stack on the Si substrate showed that it was important to grow AlN on the top of ZrTi prior to growing the GaN buffer layer. The estimated threading dislocation (TD) density in the GaN channel layer of the HEMT structure was in the 108cm−2range.