With purpose of preparing Bis-GMA free dental resin composites (DRCs) with anti-adhesion effect against Streptococcus mutans (S. mutans), a new fluorinated dimethacrylate (DFMA) was synthesized and used as base resin of DRCs. Two reactive diluents TEGDMA and SR833s were mixed with DFMA separately to prepare resin matrixes. After mixing with inorganic fillers, two DFMA based DRCs were obtained and named as DT (DFMA/TEGDMA) and DS (DFMA/SR833s) according to the resin matrix composition. Bis-GMA based DRC (BT) was used as control. The double bond conversion (DC), bacteria adhesion, mucin adsorption, contact angle, surface free energy, volumetric shrinkage (VS), shrinkage stress (SS), water sorption (WS) and solubility (SL), flexural strength (FS) and modulus (FM) before and after water immersion were investigated, and all the results were statistically analyzed with ANOVA analysis. The results showed that DT and DS had comparable (ρ > 0.05) surface free energy which was lower than that of BT (ρ < 0.05). Compared with BT, with the same surface roughness (ρ > 0.05), less amount of S. mutans was accumulated on the surface of DT and DS (ρ < 0.05). In all DRCs, the DS had the best resistance to mucin adsorption (ρ < 0.05) due to its high hydrophobicity. Compared with BT, both DFMA based DRCs had advantages such as lower VS and SS (ρ < 0.05), lower WS and SL (ρ < 0.05), and better water resistance. The DS, which had antibacterial adhesion effect, mucin adsorption resistance, lowest VS and SL (ρ < 0.05), and the highest FS and FM no matter before or after water immersion (ρ < 0.05) was considered to have the best comprehensive properties in all DRCs. • Bis-GMA free DRC was prepared using fluorinated dimethacrylate as base resin. • Fluorinated dimethacrylate-based DRCs could have antibacterial adhesion effect. • Fluorinated dimethacrylate-based DRCs had lower shrinkage and shrinkage stress. • Fluorinated dimethacrylate-based DRCs had better mechanical properties. • Fluorinated dimethacrylate-based DRCs had better water resistance. [ABSTRACT FROM AUTHOR]