Search

Superconductivity (SC) was experimentally observed for the first time in antimony polyhydride. The diamond anvil cell combined with laser heating system was used to synthesize the antimony polyhydride sample at high pressure and high temperature conditions. In-situ high pressure transport measurements as function of temperature with applied magnet are performed to study the SC properties. It was found that the antimony polyhydride samples show superconducting transition with critical temperature Tc 116 K at 184 GPa. The investigation of SC at magnetic field revealed that the superconducting coherent length ~40 angstroms based on Ginzburg Landau (GL) equation. Antimony polyhydride superconductor has the second highest Tc in addition to sulfur hydride among the polyhydrides of elements from main group IIIA to VIIA in periodic table.

Goethite, {\alpha}-FeOOH, is a major component among oxidized iron species, called rust, which formed as a product of metabolism of anoxygenic prokaryotes (1, 2) inhabiting the Earth from about 3.8 billion years (Gy) ago until the Great Oxidation Event (GOE) of about 2.5 Gy ago. The rust was buried on the ocean floor (1, 2) and had to submerge into the Earth mantle with subducting slabs due to the plate tectonics started about 2.8 Gy ago (3). The fate and the geological role of the rust at the lower mantle high-pressure and high-temperature(HPHT) conditions is unknown. We studied the behavior of goethite up to 82(2) GPa and 2300(100) K using in situ synchrotron single-crystal X-ray diffraction. At these conditions, corresponding to the coldest slabs at the depth of about 1000 km, {\alpha}-FeOOH decomposes to various iron oxides (Fe2O3, Fe5O7, Fe7O10, Fe6.32O9) and an oxygen-rich fluid. Our results suggest that recycling of the rust in the Earth mantle could contribute to oxygen release to the atmosphere and explain the sporadic increase of the oxygen level before the GOE linked to the formation of Large Igneous Provinces(4).

Extreme pressures and temperatures are known to drastically affect the chemistry of iron oxides resulting in numerous compounds forming homologous series $n$FeO$\cdot m$Fe$_2$O$_3$ and the appearance of FeO$_2$. Here, based on the results of \emph{in situ} single-crystal X-ray diffraction, M\"ossbauer spectroscopy, X-ray absorption spectroscopy, and DFT+dynamical mean-field theory calculations we demonstrate that iron in high pressure cubic FeO$_2$ and isostructural FeO$_2$H$_{0.5}$ is ferric (Fe$^{3+}$), and oxygen has a formal valence less than two. Reduction of oxygen valence from 2, common for oxides, down to 1.5 can be explained by a formation of a localized hole at oxygen sites.

We investigate the low-energy phase excitations of the quasi-one-dimensional charge density wave (CDW) in $\mathrm{K}_{0.3}\mathrm{Mo}\mathrm{O}_3$, by direct probing of infrared-active CDW-lattice modes (phase-phonons) with ultrafast terahertz spectroscopy. Both the nonequilibrium response and temperature dependence of the bands are reconciled by generalizing the time-dependent Ginzburg-Landau theory, beyond that previously applied to the amplitude-phonons, to include impurity effects, while the photoinduced blue-shifts are attributed to a reduction of the electron-phonon coupling induced by a long-lived free-carrier population.

Synchrotron diffraction as a function of temperature and pressure, specific heat, magnetic susceptibility and small-angle neutron scattering experiments have revealed an anomalous response of MnGe. Similar but less pronounced behavior has also been observed in Mn$_{1-x}$Co$_x$Ge and Mn$_{1-x}$Fe$_x$Ge solid solutions. Spin density fluctuations and Mn spin state instability are discussed as possible candidates for the observed effects., Comment: 7 pages, 9 figures, to be published in Physical Review B: Condensed Matter