Search

Efficient charge injection/extraction from/to contact electrodes is essential to realize organic electronic and optoelectronic devices with optimum characteristics for many applications. Herein, we studied a versatile reductive interlayer based on sodium borohydride (NaBH

Sodium-ion batteries (SiBs) have recently attracted considerable interest due to the plentiful supply of raw materials for their production and their electrochemical behavior, which is similar to that of lithium-ion batteries (LiBs). However, the relatively larger radius of sodium ions than that of lithium ions is not suitable for storage in conventional graphite, which is widely used as the anode. To resolve this issue, in this study, we developed a new harmonized carbon material with a three-dimensional (3D) grapevine-like structure and a sulfur component using an efficient synthesis process. On the basis of these advantages, the harmonized sulfur-carbon material exhibited a highly reversible capacity of 146 mA h g

Solution-processed nonvolatile organic transistor memory devices are fabricated by employing semiconductor blends of p-channel 6,13-bis(triisopropylsilylethynyl)pentacene and n-channel poly{[ N, N'-bis(2-octyldodecyl)-naphthalene-1,4,5,8-bis(dicarboximide)-2,6-diyl]- alt-5,5'-(2,2'-bithiophene)} (P(NDI2OD-2T); N2200) on polystyrene-brush as a polymer electret. Electret-based memory characteristics are significantly changed depending on the frontier molecular orbitals of the active semiconductors because the charge-trapping efficiency is mainly determined by the energy barrier to transfer electrons and holes from the active channel to the electret layer. A semiconductor mixture with an optimized blending ratio results in an efficient programming and erasing process. Thus, we obtained a remarkably high ratio of ON/OFF current (memory ratio) about 107 and a large amount of shifts in the threshold voltage (memory window) between the programmed and erased states of 55 V, while single-component N2200 showed only writing-once-read-many (WORM)-type memory. Especially, the programmed data can be stably retained more than 10 years with a sufficient memory ratio of 103. Furthermore, our semiconductor blend system leads to preferable vertical phase separation, which affords good reliability under a sequential memory operation condition as well as stability in ambient air. It is expected that our memory devices can be applied for versatile data storage in printed and flexible electronic applications.

We report the fabrication of high-performance, printed, n-channel organic field-effect transistors (OFETs) based on an N,N-dialkyl-substituted-(1,71,6)-dicyanoperylene-3,4:9,10-bis(dicarboximide) derivative, PDI-RCN2, optimized by the solvent-vapor annealing (SVA) process. We performed a systematic study on the influence of solubility and the chemical structure of a solvent used for the SVA process on the ordering and orientation of PDI-RCN2 molecules in the thin film. The PDI-RCN2 film showed improved crystallinity under vapor annealing with the aliphatic 1,2-dichloroethane (DCE) as a marginal solvent. The n-type OFETs with DCE-vapor-annealed PDI-RCN2 show highly improved charge-carrier mobility of ~0.5 cm(2) V(-1) s(-1) and higher stability under gate bias stress than the pristine OFETs. This large performance improvement was mainly attributed to increased crystallinity of the semiconductor thin film, enhancing π-π stacking. We also introduced a new method to pattern crystallinity of a certain region in the semiconducting film by selective exposure to the solvent vapor using a shadow mask. The crystal-patterned PDI-RCN2 OFETs exhibit decreased off-currents by ~10× and improved gate bias stability by minimizing crosstalk, reducing leakage current between devices, and reducing the density of charge trap states of the organic semiconductor.

Here we report high-performance polymer OFETs with a low-cost Mo source/drain electrode by efficient charge injection through the formation of a thermally deposited V2O5 thin film interlayer. A thermally deposited V2O5 interlayer is formed between a regioregular poly(3-hexylthiophene) (rr-P3HT) or a p-type polymer semiconductor containing dodecyl-substituted thienylenevinylene (TV) and dodecylthiophene (PC12TV12T) and the Mo source/drain electrode. The P3HT or PC12TV12T OFETs with the bare Mo electrode exhibited lower charge carrier mobility than those with Au owing to a large barrier height for hole injection (0.5-1.0 eV). By forming the V2O5 layer, the P3HT or PC12TV12T OFETs with V2O5 on the Mo electrode exhibited charge carrier mobility comparable to that of a pristine Au electrode. Best P3HT or PC12TV12T OFETs with 5 nm thick V2O5 on Mo electrode show the charge carrier mobility of 0.12 and 0.38 cm(2)/(V s), respectively. Ultraviolet photoelectron spectroscopy results exhibited the work-function of the Mo electrode progressively changed from 4.3 to 4.9 eV with an increase in V2O5 thickness from 0 to 5 nm, respectively. Interestingly, the V2O5-deposited Mo exhibits comparable Rc to Au, which mainly results from the decreased barrier height for hole carrier injection from the low-cost metal electrode to the frontier molecular orbital of the p-type polymer semiconductor after the incorporation of the transition metal oxide hole injection layer, such as V2O5. This enables the development of large-area, low-cost electronics with the Mo electrodes and V2O5 interlayer.

We report here the development of high-performance p- and n-channel organic field-effect transistors (OFETs) and complementary circuits using inkjet-printed semiconducting layers and high-k polymer dielectric blends of poly(vinylidenefluoride-trifluoroethylene) (P(VDF-TrFE)) and poly(methyl methacrylate) (PMMA). Inkjet-printed p-type polymer semiconductors containing alkyl-substituted thienylenevinylene (TV) and dodecylthiophene (PC12TV12T) and n-type poly{[N,N'-bis(2-octyldodecyl)-naphthalene-1,4,5,8-bis(dicarboximide)-2,6-diyl]-alt-5,5'-(2,2'-dithiophene)} (P(NDI2OD-T2)) OFETs typically show high field-effect mobilities (μ(FET)) of 0.2-0.5 cm²/(V s), and their operation voltage is effectively reduced to below 5 V by the use of P(VDF-TrFE):PMMA blends. The main interesting result is that the OFET characteristics could be tuned by controlling the mixing ratio of P(VDF-TrFE) to PMMA in the blended dielectric. The μ(FET) of the PC12TV12T OFETs gradually improves, whereas the P(NDI2OD-T2) OFET properties become slightly worse as the P(VDF-TrFE) content increases. When the mixing ratio is optimized, well-balanced hole and electron mobilities of more than 0.2 cm²/(V s) and threshold voltages below ±3 V are obtained at a 7:3 ratio of P(VDF-TrFE) to PMMA. Low-voltage-operated (∼2 V) printed complementary inverters are successfully demonstrated using the blended dielectric and exhibit an ideal inverting voltage of nearly half of the supplied bias, high voltage gains of greater than 25, and excellent noise margins of more than 75% of the ideal values.

Ambipolar π-conjugated polymers may provide inexpensive large-area manufacturing of complementary integrated circuits (CICs) without requiring micro-patterning of the individual p- and n-channel semiconductors. However, current-generation ambipolar semiconductor-based CICs suffer from higher static power consumption, low operation frequencies, and degraded noise margins compared to complementary logics based on unipolar p- and n-channel organic field-effect transistors (OFETs). Here, we demonstrate a simple methodology to control charge injection and transport in ambipolar OFETs via engineering of the electrical contacts. Solution-processed caesium (Cs) salts, as electron-injection and hole-blocking layers at the interface between semiconductors and charge injection electrodes, significantly decrease the gold (Au) work function (∼4.1 eV) compared to that of a pristine Au electrode (∼4.7 eV). By controlling the electrode surface chemistry, excellent p-channel (hole mobility ∼0.1-0.6 cm(2)/(Vs)) and n-channel (electron mobility ∼0.1-0.3 cm(2)/(Vs)) OFET characteristics with the same semiconductor are demonstrated. Most importantly, in these OFETs the counterpart charge carrier currents are highly suppressed for depletion mode operation (I(off)70 nA when I(on)0.1-0.2 mA). Thus, high-performance, truly complementary inverters (high gain50 and high noise margin75% of ideal value) and ring oscillators (oscillation frequency ∼12 kHz) based on a solution-processed ambipolar polymer are demonstrated.